Investigations on the effectiveness of cyanoacrylate adhesive for repair of fibre-reinforced polymer laminates under different environmental conditions

Abstract

This article presents the results of an experimental study on the long-term durability of delaminated glass fibre-reinforced polyester composites that have been repaired using a rubber toughened cyanoacrylate adhesive. While several studies have investigated cyanoacrylate for glass fibre-reinforced polyester repair applications, none has addressed the impact of environmental conditions on bond durability. Glass fibre-reinforced polyester was fabricated in the laboratory and structural damage was induced before application of cyanoacrylate adhesive. Environmental chambers were used to expose the repaired specimens to the following three standard conditions for a duration of 1000 h: dry/wet cycles of salt mist (5% salt), dry/wet non-saline water mist condition (0% salt) and a cold chamber at −20℃. A fourth set were maintained at ambient temperature and pressure and served as the control. Double cantilever beam tests were used to determine the initial peak load for pre- and post-repair specimens. No degradation in the adhesive performance was observed for the specimens exposed to the salt mist and non-saline mist. A decrease in the peak load was observed for those specimens exposed to the cold environment, indicating some reduction in bond strength.

Keywords

Delamination double cantilever beam tests glass fibre-reinforced polyester cyanoacrylate environmental tests

Get full access to this article

View all access options for this article.

References

Richardson

MOW

Wisheart

. Review of low-velocity impact properties of composites materials. Compos Part A: Appl Sci Manufac 27(12): 1123–1131.

Monti

Natali

Petrucci

. Impact damage sensing in glass fiber reinforced composites based on carbon nanotubes by electrical resistance measurements. J Appl Polym Sci 2011; 122: 2829–2836.

Pang

WCJ

Bond

. A hollow fibre reinforced polymer composite encompassing self-healing and enhanced damage visibility. Compos Sci Technol 2005; 65(11–12): 1791–1799.

Trask

Bond

. Biomimetic self-healing of advanced composite structures using hollow glass fibres. Smart Mater Struct 2006; 15: 704–710.

Bleay

Loader

Hawyes

. A smart repair system for polymer matrix composites. Compos Part A: Appl Sci Manufac 2001; 32(12): 1767–1776.

Karihaloo

Stang

. Buckling-driven delamination growth in composite laminates: guidelines for assessing the threat posed by interlaminar matrix delamination. Compos Part B: Eng 2008; 39: 386–395.

Jang

Chen

Hwang

. The response of fibrous composite to impact loading. Polym Compos 1990; 11(3): 144–157.

Morton

Godwin

. Impact response of tough carbon fibre composites. Compos Struct 1989; 13: 1–19.

Maimi

Camanho

Mayugo

. Matrix cracking and delamination in laminated composites. Part 1: ply constitutive law, first ply failure and onset of delamination. Mech Mater 2011; 43: 169–185.

10.

Mandell

Cairns

Samborsky

. Prediction of delamination in wind turbine blade structural details. J Solar Energy Eng 2003; 125: 522–530.

11.

Mikulik

Kelly

Prusty

. Prediction of flange debonding in composite stiffened panels using an analytical crack tip element-based methodology. Compos Struct 2008; 85: 233–244.

12.

Sohn

. Impact and high strain rate delamination characteristics of carbon fibre epoxy composites. Theor Appl Fract Mech 1996; 25: 17–29.

13.

Lekou DJ and van Wingerde AM. Repair techniques for composite materials applicable to wind turbine blades. In: Proceedings of the 27th Riso international symposium on materials science, Roskilde, Denmark, 4–7 September 2006, pp. 205–212.

14.

Lekou DJ and Vionis P. Report on repair techniques for composite parts of wind turbine blades, Technical document, Optimat Blades, 2002. The Netherlands: WMC.

15.

Callus

Herszberg

. Through-thickness reinforcement repair of delaminated carbon-epoxy panels. Compos Struct 2006; 75: 539–544.

16.

Ghasemnejad

Soroush

Mason

. To improve impact damage response of single and multi-delaminated FRP composites using natural flax yarn. Mater Des 2012; 36: 865–873.

17.

Kari

. Recycling wind turbine blades. Renew Energy Focus 2009; 9(7): 70–73.

18.

Zhao M, Jiang D and Li S. Research on fault mechanism of icing of wind turbine blades. In: World non-grid-connected wind power and energy conference, WNWEC 2009, Nanjing, China, 24–26 September 2009, pp. 1–4.

19.

Dry

. Procedures developed for self-repair of polymer matrix composite materials. Compos Struct 1996; 35: 263–269.

20.

Bader

Hamerton

Hay

. Double cantilever beam testing of repaired carbon fibre composites. Compos Part A: Appl Sci Manufac 2000; 31: 603–608.

21.

Ferreira

JAM

Reis

Costa

JDM

. Fatigue behaviour of composite adhesive lap joints. Compos Sci Technol 2002; 62(10–11): 1373–1379.

22.

Petrie

. Handbook of adhesives and sealants, New York: McGraw-Hill, 2006.

23.

Kister

Winter

Badcock

. Structural health monitoring of a composite bridge using Bragg grating sensors. Part 1: evaluation of adhesives and protection systems for the optical sensors. Eng Struct 2007; 29(3): 440–448.

24.

BS ISO 15024:2001. Fibre-reinforced plastic composites: determination of mode I interlaminar fracture toughness, G_ic, for unidirectionally reinforced materials.

25.

Griffin

Ashwill

. Alternative composite materials for megawatt-scale wind turbine blades: design considerations and recommended testing. J Solar Energy Eng 2003; 125(4): 515–521.

26.

Kessler

White

. Self-activated healing of delamination damage in woven composites. Compos Part A: Appl Sci Manufac 2001; 32: 683–699.

27.

Gude

Prolonho

Gomez-del Rio

. Mode-I adhesive fracture energy of carbon fibre composite joints with nanoreinforced epoxy adhesives. Int J Adhes Adhes 2011; 31: 695–703.

28.

Bardis J and Kedward K. Effects of surface preparation on long-term durability of composite adhesive bonds. Final report. Report no. DOT/FAA/AR-01/8, April 2001. Washington, DC 20591: Office of Aviation Research.

29.

Norris

Bond

Trask

. Interactions between propagating cracks and bioinspired self-healing vascules embedded in glass fibre reinforced composites. Compos Sci Technol 2011; 71: 847–853.

30.

Brunner

Blackman

BRK

Williams

. Calculating a damage parameter and bridging stress from Gic delamination tests on fibre composites. Compos Sci Technol 2006; 66: 785–795.