Mechanical properties of graphene nanoplatelet/epoxy composites

Abstract

Due to their high specific stiffness, carbon-filled epoxy composites can be used in structural components in aircraft. Graphene nanoplatelets are short stacks of individual layers of graphite that are a newly developed, lower cost material that often increases the composite tensile modulus. In this work, researchers fabricated neat aerospace epoxy (EPON 862 with Curing Agent W) and 1 to 6 wt% of two different types of graphene nanoplatelets (XG Sciences xGnP®-M-5 and xGnP®-C-300) in epoxy composites. These materials were tested for tensile properties using typical macroscopic measurements. In addition, nanoindentation was used to determine modulus and creep compliance. The macroscopic measurements showed that the tensile modulus increased from 2.72 GPa for the neat epoxy to 3.35 GPa for 6 wt% (3.7 vol%) xGnP®-M-5/epoxy composite and 3.10 GPa for 6 wt% (3.7 vol%) xGnP®-C-300/epoxy composite. The modulus results from nanoindentation followed this same trend. xGnP®-C-300/epoxy composites had higher tensile strength and ductility compared to similar loading levels of xGnP®-M-5/epoxy composites. The creep compliance for the neat epoxy, 1 to 6 wt% xGnP®-M-5/epoxy composites, and 1 to 6 wt% xGnP®-C-300/epoxy composites were similar. The two dimensional randomly oriented filler Halpin-Tsai model adjusted for platelet filler shape predicts the tensile modulus well for the xGnP®-M-5/epoxy composites and the three-dimensional randomly oriented filler Halpin-Tsai model works well for the xGnP®-C-300/epoxy composites. Per the authors’ knowledge, mechanical properties and modeling for xGnP®-M-5 and xGnP®-C-300 in this epoxy system has never been reported in the open literature.

Keywords

Epoxy nanocomposites graphene nanoplatelets tensile properties nanoindentation

Get full access to this article

View all access options for this article.

References

XG Sciences Inc. xGnP® Brand Graphene Nanoplatelets Product Information. 3101 Grand Oak Drive, Lansing, MI, 2010.

Kalaitzidou

Fukushima

Drzal

. Mechanical properties and morphological characterization of exfoliated graphite-polypropylene nanocomposites. Compos A Appl Sci Manuf 2007; 38: 1675–1682.

Fukushima

Drzal

Rook

. Thermal conductivity of exfoliated graphite nanocomposites. J Thermal Anal Calorimetry 2006; 85: 235–238.

Kalaitzidou

Fukushima

Miyagawa

. Flexural and tensile moduli of polypropylene nanocomposites and comparison of experimental data to Halpin_Tsai and Tandon-Weng models. Polym Engg Sci 2007; 47: 1796–1803.

Kalaitzidou

Fukushima

Drzal

. A new compounding method for exfoliated graphite-polypropylene nanocomposites with enhanced flexural properties and lower percolation threshold. Compos Sci Technol 2007; 67: 2045–2051.

Halpin

Kardos

. The Halpin-Tsai equations: a review. Polym Engg Sci 1976; 16: 344–352.

Agarwal

Broutman

. Analysis and performance of fiber composites, New York, NY: Wiley, 1980.

Mallick

. Composites engineering handbook, New York, NY: Marcel Dekker, Inc., 1997.

Halpin

. Stiffness and expansion estimates for oriented short fiber composites. J Compos Mater 1969; 3: 732–734.

10.

Momentive Specialty Chemicals, Inc. EPON 862/EPIKURE Curing Agent W System Product Literature, 180 E. Broad Street, Columbus, OH, 2011.

11.

Tack

Ford

. Thermodynamic and mechanical properties of epoxy resin DGEBF crosslinked with DETDA by molecular dynamics. J Molecular Graphics Model 2008; 26: 1269–1275.

12.

Zhou

Pervin

Lewis

. Fabrication and characterization of carbon/epoxy composites mixed with multi-walled carbon nanotubes. Mater Sci Engg A 2008; 475: 157–165.

13.

Chen

Curliss

. Processing and morphological development of montmorillonite epoxy composites. Nanotechnology 2003; 14: 643–648.

14.

Standard test method for tensile properties of plastics. ASTM D638. American Society for Testing and Materials. Philadelphia, PA, 2008.

15.

Oliver

Pharr

. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 1992; 7: 1564–1583.

16.

Tehrani

Safdari

Al-Halik

. Nanocharacterization of creep behavior of multiwall carbon nanotubes/epoxy nanocomposite. Int J Plast 2011; 27: 887–901.

17.

Tack JL. Thermodynamic and mechanical properties of EPON 862 with curing agent DETDA by molecular simulation. MS Thesis. Texas A&M University, College Station, TX, 2006.

18.

King

Klimek

Miskioglu

. Mechanical properties of graphene nanoplatelet/ epoxy composites. J Appl Polym Sci 2013; 128: 4217–42231.

19.

Fukushima H. Graphite nanoreinforcement in polymer nanocomposites. PhD Dissertation, Michigan State University, East Lansing, MI, 2003.

20.

Hadden

Jensen

Bandyopadhyay

. Molecular modeling of EPON-862/graphite composites: interfacial characteristics for multiple crosslink densities. Compos Sci Technol 2013; 76: 92–99.

21.

Tranchida

Piccarolo

Loos

. Mechanical characterization of polymers on a nanoscale through nanoindentation. A study pile-up and viscoeleasticiy. Macromoledues 2007; 40: 1259–1267.

22.

Lagoudas

Thakre

Benzerga

. Nanoindenation of CNT reinforced epoxy nanocomposites. Fract Nano Engr Mater Struct 2006; 1: 649–650.

23.

Tranchida

Piccarolo

Loos

. Accurately evaluation Young’s modulus of polymers through nanoindentations: A phenomenological correction factor to the Oliver and Pharr procedure. Appl Phys Lett 2006; 89: 171905–171905.

24.

Dowling

. Mechanical behavior of materials, 3rd ed. Upper Saddle River, NJ: Pearson Prentice Hall, 2007.

25.

Zandiastashbar

Ricu

Koratkar

. Control of epoxy creep using graphene. Small 2012; 8: 1676–1682.

26.

Marsh H and Rodriguez-Reinoso F. Sciences of carbon materials. Universidad de Alicante, San Vicente del Raspeig Alicante, Spain, 2001.

27.

Van Es M. Polymer-clay nanocomposite: the importance of particle dimensions. PhD dissertation. Delft University of Technology, Delft, Netherlands, 2001.