A study on the effects of organoclay content and compatibilizer addition on the properties of biodegradable poly(butylene succinate) nanocomposites under natural weathering
Restricted accessResearch articleFirst published online April, 2015
A study on the effects of organoclay content and compatibilizer addition on the properties of biodegradable poly(butylene succinate) nanocomposites under natural weathering
Biodegradable poly(butylene succinate)/organo-montmorillonite nanocomposites were prepared at different organo-montmorillonite loadings, using maleic anhydride-grafted poly(butylene succinate) as compatibilizer. Poly(butylene succinate) nanocomposites were exposed to outdoor natural weathering for 180 days. Weight loss and decrease in mechanical properties after weathering revealed the degradation of poly(butylene succinate). Natural weathering caused photo-oxidation on poly(butylene succinate), leading to the formation of degraded products, as manifested in Fourier transform infrared spectroscopy. Gel permeation chromatography showed a significant reduction in molecular weight after weathering. It was noted that poly(butylene succinate) nanocomposite exhibited lower degradability as compared to neat poly(butylene succinate), due to the enhanced barrier properties after the addition of organo-montmorillonite. However, the incorporation of maleic anhydride-grafted poly(butylene succinate) increased the degradability. Degree of crystallinity of poly(butylene succinate) reduced after weathering, as shown in differential scanning calorimetry. Scanning electron microscopy analysis revealed fungal and bacterial colonization on the sample surface. In addition, the isolation and identification of bacterial strain were also performed.
OkamotoKRaySSOkamotoM. New poly(butylene succinate)/layered silicate nanocomposites. II. Effect of organically modified layered silicates on structure, properties, melt rheology, and biodegradability. J Polym Sci Part B: Polym Phys2003; 41: 3160–3172.
2.
SomeyaYNakazatoTTeramotoN. Thermal and mechanical properties of poly(butylene succinate) nanocomposites with various organo-modified montmorillonites. J Appl Polym Sci2003; 91: 1463–1475.
ShihYFWangTYJengRJ. Biodegradable nanocomposites based on poly(butylene succinate)/organoclay. J Polym Environ2007; 15: 151–158.
5.
ChiengBWIbrahimNAYunusWMZW. Effect of organo-modified montmorillonite on poly(butylene succinate)/poly(butylene adipate-co-terephthalate) nanocomposites. eXPRESS Polym Lett2010; 4: 404–414.
6.
PhuaYJChowWSMohd. IshakZA. Poly(butylene succinate)/organo-montmorillonite nanocomposites: effects of the organoclay content on mechanical, thermal, and moisture absorption properties. J Thermoplast Compos Mater2010; 24: 133–151.
7.
PhuaYJChowWSMohd. IshakZA. Mechanical properties and structure development in poly(butylene succinate)/organo-montmorillonite nanocomposites under uniaxial cold rolling. eXPRESS Polym Lett2011; 5: 93–103.
8.
PhuaYJChowWSMohd. IshakZA. Reactive processing of maleic anhydride-grafted poly(butylene succinate) and the compatibilizing effect on poly(butylene succinate) nanocomposites. eXPRESS Polym Lett2013; 7: 340–354.
9.
NishideHToyotaKKimuraM. Effects of soil temperature and anaerobiosis on degradation of biodegradable plastics in soil and their degrading microorganisms. Soil Sci Plant Nutr1999; 45: 963–972.
10.
TezukaYIshiiNKasuyaK. Degradation of poly(ethylene succinate) by mesophilic bacteria. Polym Degrad Stab2004; 84: 115–121.
11.
KimHYangHKimH. Biodegradability and mechanical properties of agro-flour-filled polybutylene succinate biocomposites. J Appl Polym Sci2005; 97: 1513–1521.
12.
LiuLYuJChengL. Mechanical properties of poly(butylene succinate) (PBS) biocomposites reinforced with surface modified jute fibre. Composites Part A2009; 40: 669–674.
13.
PhuaYJChowWSMohd. IshakZA. The hydrolytic effect of moisture and hygrothermal aging on poly(butylene succinate)/organo-montmorillonite nanocomposites. Polym Degrad Stab2011; 96: 1194–11203.
14.
PhuaYJLauNSSudeshK. Biodegradability studies of poly(butylene succinate)/organo-montmorillonite nanocomposites under controlled compost soil conditions: effects of clay loading and compatibiliser. Polym Degrad Stab2012; 97: 1345–1354.
15.
LeeSRParkHMLimH. Microstructure, tensile properties, and biodegradability of aliphatic polyester/clay nanocomposites. Polymer2002; 43: 2495–2500.
ThirmizirMZAMohd. IshakZATaibRM. Natural weathering of kenaf bast fibre-filled poly(butylene succinate) composites: effect of fibre loading and compatibiliser addition. J Polym Environ2011; 19: 263–273.
22.
American Society for Testing and Materials. ASTM D1435: 2003. Standard Practice for Outdoor Weathering of Plastics, USA: ASTM, 2003.
23.
American Society for Testing and Materials. ASTM D638: 2003. Standard Test Method for Tensile Properties of Plastics, USA: ASTM, 2003.
24.
Kessler M. Thermal analysis of composites using DSC. In: Advanced topics in characterization of composites. Bloomington, USA: Trafford Publishing, pp. 22–23.
25.
FoulcMPBergeretAFerryL. Study of hygrothermal ageing of glass fibre reinforced PET composites. Polym Degrad Stab2005; 89: 461–470.
26.
WilmotteAAuweraGVDWachterRD. Structure of the 16 S ribosomal RNA of the thermophilic cyanobacterium chlorogloeopsis HTF (‘Mastigocladus laminosus HTF’) strain PCC7518, and phylogenetic analysis. FEBS Lett1993; 317(1–2): 96–100.
27.
JangWYShinBYLeeTJ. Thermal properties and morphology of biodegradable PLA/starch compatibilized blends. J Ind Eng Chem2007; 13: 457–464.
28.
El-RehimHAAHegazyESAAliAM. Synergistic effect of combining UV-sunlight-soil burial treatment on the degradation rate of LDPE/starch blends. J Photochem Photobiol A: Chem2004; 163: 547–556.
29.
Al-SulaimanFKhanZMerahN. Effects of weathering on failure pressure of filament-wound GFRP thermoset pipes. J Compos Mater2011; 45: 645–655.
30.
El-AwadyMM. Natural weathering artificial photo-oxidation, and thermal aging of low density polyethylene: grafting of acrylic acid onto aged polyethylene films. J Appl Polym Sci2003; 87: 2365–2371.
31.
Mohd. IshakZABerryJP. Hygrothermal aging studies of short carbon fiber reinforced nylon 6.6. J Appl Polym Sci1994; 51: 2145–2155.
32.
VlasveldDPNGroenewoldJBerseeHEN. Moisture absorption in polyamide-6 silicate nanocomposites and its influence on the mechanical properties. Polymer2005; 46: 12567–12576.
33.
AthijayamaniAThiruchitrambalamMNatarajanU. Effect of moisture absorption on the mechanical properties of randomly oriented natural fibers/polyester hybrid composite. Mater Sci Eng2009; 517(1–2): 344–353.
34.
RabelloMSWhiteJR. Crystallization and melting behavior of photodegraded polypropylene. II. Recrystallization of degraded molecules. Polymer1997; 38: 6389–6399.
KijchavengkulTAurasRRubinoM. Atmospheric and soil degradation of aliphatic-aromatic polyester films. Polym Degrad Stab2010; 95: 99–107.
37.
Freile-PelegrínYMadera-SantanaTRobledoD. Degradation of agar films in a humid tropical climate: thermal, mechanical, morphological and structural changes. Polym Degrad Stab2007; 92: 244–252.
38.
TomitaKKurokiYHayashiN. Isolation of a thermophile degrading poly(butylene succinate-co-butylene adipate). J Biosci Bioeng2000; 90: 350–352.
39.
HayaseNYanoHKudohE. Isolation and characterization of poly(butylene succinate-cobutylene adipate)-degrading microorganism. J Biosci Bioeng2004; 97: 131–133.
40.
AmirulAAYahyaARMSudeshK. Biosynthesis of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) copolymer by Cupriavidus sp. USMAA1020 Isolated from Lake Kulim, Malaysia. Bioresour Technol2008; 99: 4903–4909.
41.
PoonguzhaliSMadhaiyanMYimWJ. Colonization pattern of plant root and leaf surfaces visualized by use of green-fluorescent-marked strain of Methylobacterium suomiense and its persistence in rhizosphere. Appl Microbiol Biotechnol2008; 78: 1033–1043.
42.
CookDMHenriksenEDUpchurchR. Isolation of polymer-degrading bacteria and characterization of the hindgut bacterial community from the detritus-feeding larvae of tipula abdominalis (Diptera: Tipulidae). Appl Environ Microbiol2007; 73: 5683–5686.