The aim of this study was to significantly reduce the curing time for glass fibre epoxy composites in industrial relevant dimensions without worsening of the mechanical properties. With the combination of microwave heating and resin transfer moulding (RTM), the time between filling the mould and demoulding the samples was reduced to only 1 h and 15 min compared to at least 6 h for conventional curing of the same material. Based on the different dielectric losses of cured and uncured resin a pulsed microwave process was developed. In this way homogenously cured samples were obtained. Tensile strength, flexural strength, flexural modulus of elasticity and Charpy impact strength of microwave cured samples were compared to conventionally cured samples. No statistically significant differences were found. Thus, microwave curing shows a high potential to improve the efficiency of fibre composite production while maintaining the mechanical properties.
ClarkDEFolzDCWestJK. Processing materials with microwave energy. Mater Sci Eng A Struct2000; 287: 153–158.
2.
ThostensonETChouTW. Microwave processing: fundamentals and applications. Compos Part A Appl Sci Manuf1999; 30: 1055–1071.
3.
DasSMukhopadhyayAKDattaS. Prospects of microwave processing: an overview. Bull Mater Sci2009; 32: 1–13.
4.
LeonelliCMasonTJ. Microwave and ultrasonic processing: now a realistic option for industry. Chem Eng Process2010; 49: 885–900.
5.
PapargyrisDDayRNesbittA. Comparison of the mechanical and physical properties of a carbon fibre epoxy composite manufactured by resin transfer moulding using conventional and microwave heating. Compos Sci Technol2008; 68: 1854–1861.
6.
WallaceMAttwoodDDayRJ. Investigation of the microwave curing of the PR500 epoxy resin system. J Mater Sci2006; 41: 5862–5869.
7.
AlazardPPalumboMGourdenneA. Curing under continuous microwaves (2450 MHz) of thermosetting epoxy prepolymers: final statement. Macromol Symp2003; 199: 59–72.
8.
BogdalDGorczykJ. Microwave assisted synthesis and determination of chain branching in solid epoxy resins using 1H NMR spectrometry. Polymer2003; 44: 7795–7800.
9.
MooteriPSSridharaBRaoS. Studies on mechanical behavior of microwave and thermally cured glass fiber reinforced polymer composites. J Reinf Plast Compos2006; 25: 503–512.
10.
YueCLooiH. Influence of thermal and microwave processing on the mechanical and interfacial properties of a glass/epoxy composite. Composites1995; 26: 767–773.
11.
ChaowasakooTSombatsompopN. Mechanical and morphological properties of fly ash/epoxy composites using conventional thermal and microwave curing methods. Compos Sci Technol2007; 67: 2282–2291.
12.
TanrattanakulVJaroendeeD. Comparison between microwave and thermal curing of glass fiber–epoxy composites: effect of microwave-heating cycle on mechanical properties. J Appl Polym Sci2006; 102: 1059–1070.
QiuYHawleyM. Uniform processing of V-shaped and tri-planar composite parts using microwaves. J Compos Mater2001; 35: 1062–1078.
15.
Joshi SC and Bhudolia SK. Microwave-thermal technique for energy and time efficient curing of carbon fiber reinforced polymer prepreg composites. J Compos Mater. 2014; 48(24): 3035–3048.
16.
RaoRMVGKRaoSSridharaB. Studies on tensile and interlaminar shear strength properties of thermally cured and microwave cured glass-epoxy composites. J Reinf Plast Compos2006; 25: 783–795.
17.
ThostensonETChouT. Microwave and conventional curing of thick-section thermoset composite laminates: experiment and simulation. Polym Compos2001; 22: 197–212.
18.
NightingaleCDayR. Flexural and interlaminar shear strength properties of carbon fibre/epoxy composites cured thermally and with microwave radiation. Compos Part A Appl Sci Manuf2002; 33: 1021–1030.
19.
BaiSDjafariV. Interfacial properties of microwave cured composites. Composites1995; 26: 645–651.
20.
HookKJAgrawalRKDrzalLT. Effects of microwave processing on fiber-matrix adhesion. II. Enhanced chemical bonding of epoxy to carbon fibers. J Adhesion1990; 32: 157–170.
21.
AgrawalRKDrzalLT. Effects of microwave processing on fiber-matrix adhesion in composites. J Adhesion1989; 29: 63–79.
22.
LiNLiYHangX. Analysis and optimization of temperature distribution in carbon fiber reinforced composite materials during microwave curing process. J Mater Process Technol2014; 214: 544–550.
23.
Lässig R, Eisenhut M, Mathias A, et al. Series production of high-strength composites – perspectives for the German engineering industry. Report, Roland Berger Strategy Consultants, Germany, September 2012.
24.
JohnsonMSRuddCDHillDJ. The effect of microwave resin preheating on the quality of laminates produced by resin transfer molding. Polym Compos1997; 18: 185–197.
25.
JohnsonMSRuddCDHillDJ. Microwave assisted resin transfer moulding. Compos Part A Appl Sci Manuf1998; 29: 71–86.
26.
DegamberBFernandoG. Process monitoring of a thermosetting resin using optical-fiber sensors in a microwave environment. IEEE Sens J2004; 4: 713–721.
27.
DIN EN ISO 2818. 1996. Plastics – preparation of test specimens by machining.
28.
DIN EN ISO 527-1. 1996. Plastics – determination of tensile properties – part 1: general principles.
29.
DIN EN ISO 527-4. 1997. Plastics – determination of tensile properties – part 4: test conditions for isotropic and orthotropic fibre-reinforced composites.
30.
DIN EN ISO 14125. 1998. Fibre-reinforced plastic composites – determination of flexural properties.
31.
DIN EN ISO 179-1. 2008. Plastics – determination of Charpy impact strength – part 1: non-instrumented impact test.
32.
Saccone G, Amendola E and Acierno D. Conventional and microwave curing process of epoxy systems: kinetic analysis and characterization. Microw Opt Technol Lett 2009; 51: 2777–2783.
33.
FeherLThummM. Microwave innovation for industrial composite fabrication – the HEPHAISTOS technology. IEEE Trans Plasma Sci2004; 32: 73–79.
34.
DrzalLTMadhukarM. Fibre-matrix adhesion and its relationship to composite mechanical properties. J Mater Sci1993; 28: 569–610.
35.
DengSYeL. Influence of fibre-matrix adhesion on mechanical properties of graphite/epoxy composites: I. Tensile, flexural, and fatigue properties. J Reinf Plast Compos1999; 18: 1021–1040.
36.
AbrahamDMatthewsSMcIlhaggerR. A comparison of physical properties of glass fibre epoxy composites produced by wet lay-up with autoclave consolidation and resin transfer moulding. Compos Part A Appl Sci Manuf1998; 29: 795–801.