A 3D finite element model has been developed for predicting manufacturing distortions of fibre-reinforced thermosetting composite parts. The total curing process is divided into three steps that correspond to the states that resin passes through during curing: viscous, rubbery, and glassy. Tool–part interaction properties were calibrated by modelling the distortion of a single ply part. For comparison, composite parts of various geometries (L-section and U-section), stacking sequences, thicknesses, and bagging conditions were manufactured. The full field thickness profile and full field distortion pattern were obtained using a 3D laser scanner, which reveals higher and lower resin bleeding and corner thickening locations. The effect of stacking sequence is also examined with the full field distortion pattern. It was found that the parts manufactured under the bleeding condition give higher spring-in and warpage values. The spring-in predictions were well matched to measurements of the manufactured parts.
WisnomMRGigliottiMErsoyN. Mechanisms generating residual stresses and distortion during manufacture of polymer-matrix composite structures. Compos A2006; 37: 522–529.
2.
WhiteSRHahnHT. Process modelling of composite materials: residual stress development during cure. Part I. Model formulation. J Compos Mater1992; 26: 2423–2453.
3.
WhiteSRHahnHT. Process modelling of composite materials: residual stress development during cure. Part II. Experimental validation. J Compos Mater1992; 26: 2423–2453.
4.
Bogetti TA and Gillipse JW. Processing-induced stress and deformation in thick section thermosetting composite laminates. CCM Report 89-21, University of Delaware, Newark, DE, August 1989.
5.
BogettiTAGillespieJWJr. Process-induced stress and deformation in thick-section thermoset composite laminates. J Compos Mater1992; 26: 626–660.
ArafathARAVaziriRPoursartipA. Closed-from solution for process-induced stresses and deformation of a composite part cured on a solid tool: Part I – flat geometries. Compos A2008; 39: 1106–1117.
8.
ArafathARAVaziriRPoursartipA. Closed-from solution for process-induced stresses and deformation of a composite part cured on a solid tool: Part II – curved geometries. Compos A2009; 40: 1545–1557.
9.
JohnstonAVaziriRPoursartipA. A plane strain model for process-induced deformation of laminated composite structures. J Compos Mater2001; 35: 1435–1469.
10.
SvanbergJMHolmbergJA. An experimental investigation on mechanisms for manufacturing induced shape distortions in homogeneous and balanced laminates. Compos A2001; 32: 827–838.
11.
SvanbergJMAltkvistCNymanT. Prediction of shape distortions for a curved composite C-spar. J Reinf Plast Compos2005; 24: 323–339.
12.
SvanbergJMHolmbergJA. Prediction of shape distortions. Part II. Experimental validation and analysis of boundary conditions. Compos A2004; 35: 723–734.
13.
ErsoyNGarstkaTPotterK. Modelling of the spring-in phenomenon in curved parts made of a thermosetting composite. Compos A2010; 41: 410–418.
14.
ÇınarKÖztürkUEErsoyN. Modelling manufacturing deformations in corner sections made of composite materials. J Compos Mater2014; 48: 799–813.
15.
ÇınarKErsoyN. Effect of fibre wrinkling to the spring-in behaviour of L-shaped composite materials. Compos A2015; 69: 105–114.
16.
ZhuQGeubellePHLiM. Dimensional accuracy of thermoset composites: simulation of process-induced residual stresses. J Compos Mater2001; 35: 2171–2205.
17.
CliffordSJanssonNYuW. Thermoviscoelastic anisotropic analysis of process induced residual stresses and dimensional stability in real polymer matrix composite components. Compos A2006; 37: 538–545.
18.
TavakolBRoozbehjavanPAhmedA. Prediction of residual stresses and distortion in carbon fiber-epoxy composite parts due to curing process using finite element analysis. J Appl Polym Sci2013; 128: 941–950. DOI: 10.1002/app.38075.
19.
WucherBLaniFPardoenT. Tooling geometry optimization for compensation of cure-induced distortions of a curved carbon/epoxy C-spar. Compos A2014; 56: 27–35.
20.
DongC. Modeling the process-induced dimensional variations of general curved composite components and assemblies. Compos A2009; 40: 1210–1216.
21.
KappelEStefaniakDSprowitzT. A semi-analytical simulation strategy and its application to warpage of autoclave-processed CFRP parts. Compos A2011; 42: 1985–1994.
22.
FerlundGRahmanNCourdjiR. Experimental and numerical study of the effect of cure cycle, tool surface, geometry, and lay-up on the dimensional fidelity of autoclave-processed composite parts. Compos A2002; 33: 341–351.
23.
TwiggGPoursartipAFerlundG. Tool-part interaction in composite processing. Part II: numerical modelling. Compos A2004; 35: 135–141.
24.
Garstka T. Separation of process induced distortions in curved composite laminates. PhD Thesis, University of Bristol, Bristol, 2005.
25.
Flanagan R. The dimensional stability of composite laminates and structures. PhD Thesis, Queen’s University of Belfast, Belfast, 1997.
26.
ABAQUS 6.12 Online Documentation, Dassault Systèmes, Providence, RI, USA, 2012.
27.
ErsoyNGarstkaTPotterK. Development of the properties of a carbon fibre reinforced thermosetting composite through cure. Compos A2010; 41: 401–409.
28.
GarstkaTErsoyNPotterKD. In situ measurements of through-the-thickness strains during processing of AS4/8552 composite. Compos A2007; 38: 2517–2526.
29.
HubertPPoursartipA. Aspects of the compaction of composite angle laminates: an experimental investigation. J Compos Mater2001; 35: 2–26.
30.
DarrowDAJrSmithLV. Isolating components of processing induced warpage in laminated composites. J Compos Mater2001; 36: 2407–2418.