Tension–tension fatigue tests in a combustion environment were performed on double-edge notched oxide/oxide ceramic matrix composite specimens. The composite, designated as N720/A, constituted woven 0°/90° Nextel™720 fibers in alumina matrix. Monotonic tensile and cyclic loads at a frequency of 1 Hz and a stress ratio of 0.05 were applied on the specimens in a combustion environment. The maximum specimen temperature due to combustion flame impingement in the notch region was 1250 ± 50℃. A stiffness reduction of less than 10% evaluated for the run-out specimens showed the harsh combustion environment had a minimal effect on specimen degradation. The residual strength was evaluated to be ∼75%–85% the strength of non-fatigued (virgin) double-edge notch specimens in room temperature. The monotonic tensile strength and the fatigue limit for 90,000 cycles (run-out) were found to be ∼40 MPa less in the combustion environment when compared to published results for 1200℃ laboratory air environment. The damage mechanisms were also the same in the two environments. Finite element analyses showed that the reduction in strength and fatigue limit in the combustion environment (as compared to the laboratory air environment) was due to the presence of thermal gradient stresses because of non-uniform specimen temperature distribution.
AnsonDRichersonDWThe benefits and challenges of the use of ceramics in gas turbines. In: vanRoodeFerberMRichersonMKDW (eds). Ceramic gas turbine component development and characterization, New York: ASME Press, 2002.
2.
SchafrikRSpragueR. Saga of gas turbine materials: Part III. Adv Mater Proc2004; 162: 27–30.
3.
LangeFFTuWCEvansAG. Processing of damage-tolerant, oxidation-resistant ceramic matrix composites by a precursor infiltration and pyrolysis method. Mater Sci Eng A1995; A195: 145–50.
4.
LunderbergREckerbomLDesign and processing of all-oxide composites. In: EvansAGNaslainRG (eds). High temperature ceramic matrix composites II: Manufacturing and materials development, Westerville, OH: The American Ceramic Society, 1995, pp. 95–104.
MorganPEDMarshallDB. Ceramic composites of monazite and alumina. J Am Cera Soc1995; 78: 1553–1563.
7.
HaslamJJLangeFF. Processing and properties of an all-oxide composite with a porous matrix. J Eur Cera Soc2000; 20: 607–618.
8.
StaehlerJMZawadaLP. Performances of four ceramic–matrix composite divergent flap inserts following ground testing on an F110 turbofan engine. J Am Cera Soc2000; 83: 1727–1738.
9.
ZawadaLPHayRSLeeSSet al.Characterization and high temperature mechanical behavior of an oxide/oxide composite. J Am Cera Soc2003; 86: 981–990.
10.
SteelSGZawadaLPMallS. Fatigue behavior of a Nextel 720/alumina (N720/A) composite at room and elevated temperature. Cera Eng Sci Proc2001; 22: 695–702.
11.
ZawadaLPHayRSLeeSSet al.Characterization and high temperature mechanical behavior of an oxide/oxide composite. J Am Cera Soc2003; 86: 981–990.
12.
Ruggles-WrennMBMallSEberCAet al.Effects of steam environment on high-temperature mechanical behavior of Nextel™720/Alumina (N720/A) continuous fiber ceramic matrix composite. Compos Part A2006; 37: 2029–2040.
13.
MallSBoyerBH. Cyclic and sustained loading behaviors of oxide/oxide Nextel™720/alumina composite with double edge sharp notch. Compos Part A2012; 43: 1153–1159.
14.
MallSSullivanM. Creep rupture and fatigue behavior of a notched oxide/oxide ceramic matrix composite at an elevated temperature. Int J Appl Cera Technol2010; 8: 251–260.
15.
AskarinejadSRahbarNSabelkinVet al.Mechanical behavior of a notched oxide/oxide ceramic matrix composite in combustion environment: experiments and simulations. Compos Struct2015; 127: 77–86.
16.
MallSNyeARJeffersonG. Tension-tension fatigue behavior of Nextel™720/Alumina under combustion environment. Int J Appl Cera Technol2012; 9: 159–171.
17.
SabelkinVZawadaLMallS. Effects of combustion and salt-fog exposure on fatigue behavior of two ceramic matrix composites and a superalloy. J Mater Sci2015; 50: 5204–5213.
18.
KimTTMallSZawadaLPJeffersonG. Simultaneous fatigue and combustion exposure of a SiC/SiC ceramic matrix composite. J Compos Mater2010; 44: 2991–3016.
19.
SabelkinVJoshiGMallSet al.Monotonic tension and creep behavior of single crystal CMSX-486 under combustion environment. Mater Sci Eng A2013; 569: 106–116.
20.
SabelkinVMallSCookTSet al.Fatigue and creep behaviors of a SiC/SiC composite under combustion and laboratory environments. J Compos Mater2016; 50(16): 2145–2153.
21.
LuthraKL. Simulation of gas turbine environments in small burner rigs. High Temp Technol1989; 7: 187–192.
22.
RichardsonGLeiCSSinghRN. Mechanical properties of ceramic matrix composites exposed to rig tests. Cera Eng Sci Proc2004; 25: 153–159.
23.
CormanGSDeanAJBrabetzSet al.Rig and engine testing of melt infiltrated ceramic composites for combustor and shroud applications. J Eng Gas Turbines Power2002; 124: 459–464.
HaqueAAhmedLRamasettyA. Stress concentrations and notch sensitivity in woven ceramic matrix composites containing a circular hole – an experimental, analytical, and finite element study. J Am Cera Soc2005; 88: 2195–2201.
26.
KanuryAM. Introduction to combustion phenomena, New York, USA: Gordonand Breach, 1995.
27.
MontgomeryCJCannonSMMawidMASekarB. Reduced chemical kinetic mechanisms for JP-8 combustion. In: Proceedings of the 40th AIAA aerospace science meeting and exhibit, Reno, NV: American Institute of Aeronautics and Astronautics, 14–17 January 2002.
28.
JachimowskiCJ. Chemical kinetic reaction mechanism for the combustion of propane. Combus Flame1984; 55: 213–224.
29.
MawidMAParkTWSekarBet al.Application of pulse detonation combustion to turbofan engines. J Eng Gas Turb Power2003; 125: 270–283.
30.
GlassmanI. Combustion, New York: Academic Press, 1996.
31.
Smith VK III, Albro JR and More M. New aeropropulsion ground test tools for accelerated engine life assessment. In: 37th AIAA/ASME/SAE/ASEE joint propulsion conference and exhibit, Salt Lake City, UT, 8–11 July 2001.
BergmanTLLavineASIncroperaFPet al.Fundamentals of heat and mass transfer, 7th edition. Hoboken, NJ: John Wiley & Sons, Inc, 2011.
36.
Sullivan MA. Creep-rupture and fatigue behaviors of notched oxide/oxide ceramic matrix composite at elevated temperature. MS Thesis, Air Force Institute of Technology, 2006.
37.
PetersonRE. Stress concentration factors: Charts and relations useful in making strength calculations for machine parts and structural elements, Hoboken, NJ: John Wiley & Sons Inc, 1974.