Monotonic tensile tests are conducted on seven different Glare grades of fiber metal laminates. In-situ stress–strain curves of glass/epoxy laminate interleaved in Glare 2(3/2) are exposed with the application of metal volume fraction method using the stress–strain curves of Glare 2(3/2) and Aluminum 2024-T3 in unidirectional and transverse directions. The strain–stress curves of cross-ply Glares are predicted by the modification of this method with an empirical parameter and a second parameter considering the relative glass/epoxy laminate thickness ratios of Glare grades. Modified metal volume fraction method presented in this study can be used as a preliminary estimation of stress–strain curves of multiple possible fiber metal laminate configurations without testing.
Vlot A and Gunnink JW. Fiber metal laminates, an introduction. Dordrecht, The Netherlands: Kluwer Academic Publishers, 2001.
2.
VoselesangLBVlotA. Development of fibre metal laminates for advanced aerospace structures. J Mater Process Tech2000; 103: 1–5.
3.
SinmazcelikTAvcuEBoraMOet al.A review: Fibre metal laminates; background, bonding types and applied methods. Mater Des2011; 32: 3671–3685.
4.
SinkeJ. Development of fibre metal laminates: concurrent multi-scale modeling and testing. J Mater Sci2006; 41: 6777–6788.
5.
AsundiAChoiAYN. Fiber metal laminates: An advanced material for future aircraft. J Mater Process Tech1997; 63: 384–394.
6.
LawcockGYeLMaiYW. Novel fiber reinforced metal laminates for aerospace applications – A review. Part I – Background and general mechanical properties. SAMPE J1995; 31: 23–31.
7.
WuHFWuLLSlagterWJet al.Use of rule of mixtures and metal volume fraction for mechanical property predictions of fiber-reinforced aluminum laminates. J Mater Sci1994; 29: 4583–4591.
8.
ChenJLSunCT. Modeling of orthotropic elastic-plastic properties of Arall laminates. Compos Sci Technol1989; 36: 321–337.
9.
KawaiMMorishitaMTomuraSet al.Inelastic behavior and strength of fiber metal hybrid composite: Glare. Int J Mech Sci1998; 40: 183–198.
10.
SoltaniPKeikhosravyMOskoueiRHet al.Studying the tensile behaviour of GLARE laminates: a finite element modelling approach. Appl Compos Mater2011; 18: 271–282.
11.
Seyed YaghoubiALiuYLiawB. Stacking sequence and geometrical effects on low-velocity impact behaviors of GLARE 5 (3/2) fiber-metal laminates. J Thermoplast Compos Mat2012; 25: 223e47–223e47.
12.
ASTM-D3039/D3039M-08. Standard test method for tensile properties of polymer matrix composite materials. West Conshohocken, PA: ASTM International, 2008.
13.
DanielIM. Experimentation and modeling of composite materials. Exp Mech1999; 39: 1–19.
14.
WuHFWuLL. A study of tension test specimens of laminated hybrid composites. 1. Methods of approach. Compos Part A-Appl S1996; 27: 647–654.
15.
JonesRM. Mechanics of composite materials, 2nd ed. New York: Taylor & Francis, 1999.
16.
ASTM-E8/E8M-13a. Standard test methods for tension testing of metallic materials. West Conshohocken, PA: ASTM International, 2013.
17.
Hagenbeek M. Characterisation of fiber metal laminates under thermo-mechanical loadings. PhD Thesis, Aerospace Engineering, Delft University of Technology, 2005.
18.
DanielIMAnastassopoulosG. Failure mechanisms and damage evolution in crossply ceramic-matrix composites. Int J Solids Struct1995; 32: 341–355.
19.
Selvadurai APS, Transverse loading of unidirectionally reinforced composites: the role of matrix damage and matrix fracture. In: JuJWAllenDH (eds). American society of mechanical engineering symposium on damage mechanisms in composites, Chicago: ASME, 1994, pp. 117–127.
20.
AbrateS. Matrix cracking in laminated composites: A review. Compos Eng1991; 1: 337–353.
21.
SunCTJenKC. On the effect of matrix cracks on laminate strength. J Reinf Plast Comp1987; 6: 208–222.
22.
GrovesSEHarrisCEHighsmithALet al.An experimental and analytical treatment of matrix cracking in cross-ply laminates. Exp Mech1987; 27: 73–79.
23.
TalrejaR. Transverse cracking and stiffness reduction in composite laminates. J Compos Mater1985; 19: 355–375.
Tsai CL, Daniel IM and Lee JW. Progressive matrix cracking of cross ply composite laminates under biaxial loading. Microcracking-induced damage in composites. In: Dvorak GJ and Lagoudas DC (eds) Proceedings of ASME 1990 Winter Annual Meeting. New York: American Society of Mechanical Engineers, 1990, pp.9–18.