A graphene/graphite-based conductive polyamide 12 interlayer for increasing the fracture toughness and conductivity of carbon-fiber composites

Abstract

A conductive thermoplastic material was developed to increase the interlaminar fracture toughness and through-the-thickness conductivity of carbon-fiber-reinforced plastics materials. A polyamide 12 nonwoven fabric was coated with graphene/graphite particles in a solution of hexane, water, and graphite particles. The graphite powders were exfoliated in the sonication bath and the resulting layers of graphene resided at the interface of the immiscible solvents, where the graphene layers/graphite simultaneously infused into the polyamide 12. The sonication time and graphite content were optimized to maximize the surface conductivity of conductive polyamide 12 fabric. The presence of pristine graphene flakes and graphite on the polyamide 12 fabric was confirmed by X-ray diffraction and scanning electron microscopy. The dry fabric preform was interleaved with the conductive polyamide 12 and the composite laminates were manufactured by a vacuum-assisted resin transfer molding process. The resulting composite laminate resulted in a significant increase in Mode I and Mode II fracture toughness up to 42% and 141%, respectively, and a decrease in the volume resistivity from 100 MΩm to 402 Ωm.

Keywords

Fracture toughness electrical conductivity graphene/graphite

Get full access to this article

View all access options for this article.

References

Cantwell

Morton

. The impact resistance of composite materials—a review. Composites 1991; 22: 347–362.

Rahman

Hosur

Hsiao

et al.

Low-velocity impact properties of carbon nanofibers integrated carbon fiber/epoxy hybrid composites manufactured by OOA–VBO process. Compos Struct 2015; 120: 32–40.

Tsotsis TK. Interlayer toughening of composite materials. Polym Composite 2009; 30: 70.

Hodgkin

Simon

Varley

. Thermoplastic toughening of epoxy resins: a critical review. Polym Adv Technol 1998; 9: 3–10.

Kinloch

Yuen

Jenkins

. Thermoplastic-toughened epoxy polymers. J Mater Sci 1994; 29: 3781–3790.

Kuwata

Hogg

. Interlaminar toughness of interleaved CFRP using non-woven veils: Part 2. Mode-II testing. Compos A: Appl Sci Manuf 2011; 42: 1560–1570.

Sela

Ishai

. Interlaminar fracture toughness and toughening of laminated composite materials: a review. Composites 1989; 20: 423–435.

Barnstorff K. NASA Lightning Research. NASA, 7 June 2013. NASA Web.

AGATE. Integrated design and manufacturing: Lightning strike direct effects. Pittsfield: NASA Industry FAA, 2002.

10.

Kawakami H and Feraboli P. Lightning strike damage resistance and tolerance of scarf-repaired mesh-protected carbon fiber composites. Compos Part A Appl Sci Manuf 2011; 42: 1247–1262.

11.

Rakov

Uman

. Lightning: physics and effects, Cambridge: Cambridge University Press, 2006.

12.

Kawakami H. Lightning strike induced damage mechanisms of carbon fiber composites. University of Washington, 2011.

13.

Feraboli

Miller

. Damage resistance and tolerance of carbon/epoxy composite coupons subjected to simulated lightning strike. Compos A 2009; 40: 954–967.

14.

Guo

Liu

et al.

Simultaneously increasing the electrical conductivity and fracture toughness of carbon–fiber composites by using silver nanowires-loaded interleaves. Compos Sci Technol 2014; 97: 27–33.

15.

Arnold M, Henne M, Bender K, et al. Polyamide 12 modified with nanoparticles: Effect on impact behaviour and on the electrical conductivity of carbon fibre-reinforced epoxy composites. J Compos Mater 2016; 50: 159–171.

16.

Kim

Hahn

. Graphite fiber composites interlayered with single-walled carbon nanotubes. J Compos Mater 2011; 45: 1109–1120.

17.

Latko P and Boczkowska A. Fabrication of carbon nanotubes-doped veils. In: Smart Intelligent Aircraft Structures (SARISTU), 2016, pp.815–824. Springer International Publishing.

18.

Latko P, Rumiński W and Boczkowska A. Carbon nanotubes-doped veils. Compos Struct 2015; 134: 52–59.

19.

Xie

X-L

Mai

Y-W

Zhou

X-P

. Dispersion and alignment of carbon nanotubes in polymer matrix: a review. Master Sci Eng 2005; 49: 89–112.

20.

Sandlera

Pegela

Cadekc

et al.

A comparative study of melt spun polyamide-12 fibres reinforced with carbon nanotubes and nanofibres. Polymer 2004; 45: 2001–2015.

21.

Liu

Phang

Shen

et al.

Morphology and mechanical properties of multiwalled carbon nanotubes reinforced nylon-6 composites. Macromolecules 2004; 37: 7214–7222.

22.

Clingerman ML, Weber EH, King JA, Schulz KH. Synergistic effect of carbon fillers in electrically conductive nylon 6, 6 and polycarbonate based resins. Polym Compos 2002; 23: 911–924.

23.

Vankayala

Lai

W-JP

Cheng

K-C

et al.

Enhanced electrical conductivity of nylon 6 composite using polyaniline-coated multi-walled carbon nanotubes as additives. Polymer 2011; 52: 3337–3343.

24.

Gou J, Tang Y, Liang F, et al. Carbon nanofiber paper for lightning strike protection of composite materials. Composites Part B 2010; 41: 192–198.

25.

Woltornist

et al.

Conductive thin films of pristine graphene by solvent interface trapping. ACS Nano 2013; 7: 7062–7066.

26.

Woltornist

Alamer

McDannald

et al.

Preparation of conductive graphene/graphite infused fabrics using an interface trapping method. Carbon 2015; 8I: 38–42.

27.

Yi M, Shen Z, Zhang X, et al. Achieving concentrated graphene dispersions in water/acetone mixtures by the strategy of tailoring Hansen solubility parameters. J Phys D Appl Phys 2012; 46: 025301.

28.

Saini

Sharma

Akodia

. Graphene oxide and reduced graphene oxide coated polyamide fabrics for antistatic and electrostatic charge dissipation. World J Text Eng Technol 2016; 2: 1–5.

29.

Latko

Kozera

Salinier

et al.

Non-woven veils manufactured from polyamides doped with carbon nanotubes. Fibers Textile East Europe 2013; 21: 45–49.

30.

Latko

Ski

Boczkowska

. Carbon nanotubes-doped veils. Compos Struct 2015; 134: 52–59.

31.

Vankayala

Petrick

Cheng

et al.

Enhanced electrical conductivity of nylon 6 composite using polyaniline-coated multi-walled carbon nanotubes as additives. Polymer 2011; 52: 3337–3343.

32.

Kim

et al.

Mechanical properties of woven laminates and felt composites using carbon fibers. Part 1: in-plane properties. Compos Sci Technol 2004; 64: 2221–2229.

33.

Beckermann

Pickering

. Mode I and Mode II interlaminar fracture toughness of composite laminates interleaved with electrospun nanofibre veils. Compos A: Appl Sci Manuf 2015; 72: 11–21.

34.

Czabaj

Ratcliffe

. Comparison of intralaminar and interlaminar mode I fracture toughnesses of a unidirectional IM7/8552 carbon/epoxy composite. Compos Sci Technol 2013; 89: 15–23.

35.

Nash

et al.

The influence of hydrothermal conditioning on the Mode-I, thermal and flexural properties of Carbon/Benzoxazine composites with a thermoplastic toughening interlayer. Compos A: Appl Sci Manuf 2015; 76: 135–144.

36.

Kuwata M. Mechanisms of interlaminar fracture toughness using non-woven veils as interleaf materials. Dissertation, Queen Mary, University of London, UK, 2010.

37.

Nash

Young

Stanley

. The influence of a thermoplastic toughening interlayer and hydrothermal conditioning on the Mode-II interlaminar fracture toughness of Carbon/Benzoxazine composites. Compos A: Appl Sci Manuf 2016; 81: 111–120.

38.

Campbell FC Jr (ed.) Manufacturing processes for advanced composites. Elsevier, 2003, pp.56–61.

39.

Woods JA, Modin AE, Hawkins RD, et al. U.S. Patent No. 7,334,782. U.S. Patent and Trademark Office, Washington, DC, 2008.

40.

Shinoda T, Odani H, Wadahara E, et al. A-VARTM technology application for Japan’s new regional jet aircraft. Fuel 2007; 10: 20–29.

Supplementary Material

Please find the following supplemental material available below.

For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.

For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.

0.00 MB

0.17 MB