An energy method based on beam theory is proposed to determine the strain energy release rate of an existing crack in composite laminates. The developed analytical method was implemented in isotropic materials, and the obtained strain energy release rate of a crack was validated by reference results and finite element solutions. The general behavior of crack growth on the left or right crack tip was evaluated, and basic trends leading to crack propagation to one side of the crack were established. A correction factor was introduced to improve the accuracy of the strain energy release rate for small cracks. The singularity at the crack tip caused by dissimilar materials was investigated and was found that the inclusion of the singularity effect could increase the accuracy for small cracks. The calculated strain energy release rate of a crack in a composite beam has been verified by comparing with a finite element model.
ZhengWKassapoglouC. Prediction of delamination onset and growth for AP-PLY composite laminates using the finite element method. Compos Part A – Appl S2017; 101: 381–393.
HamedMNosierAFarrahiG. Separation of delamination modes in composite beams with symmetric delaminations. Mater Design2006; 27: 900–910.
7.
Gordnian K, Hadavinia H, Simpson G, et al. Calculation of energy release rate in mode I delamination of angle ply laminated composites. In: ICCES international conference on computational & experimental engineering and sciences, Miami, USA, 3–8 Jan 2007, volume 5. Icces. pp. 1793–1797.
8.
YaoLAlderliestenRCZhaoMet al.Discussion on the use of the strain energy release rate for fatigue delamination characterization. Compos Part A – Appl S2014; 66: 65–72.
9.
YaoLCuiHAlderliestenRCSunYet al.Thickness effects on fibre-bridged fatigue delamination growth in composites. Compos Part A – Appl S2018; 110: 21–28.
10.
CarlssonLGillespieJPipesR. On the analysis and design of the end notched flexure (ENF) specimen for mode II testing. J Compos Mater1986; 20: 594–604.
11.
SunCZhengS. Delamination characteristics of double-cantilever beam and end-notched flexure composite specimens. Compos Sci Technol1996; 56: 451–459.
12.
DavidsonBKrügerRKönigM. Effect of stacking sequence on energy release rate distributions in multidirectional DCB and ENF specimens. Eng Fract Mech1996; 55: 557–569.
BenzeggaghMKenaneM. Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus. Compos Sci Technol1996; 56: 439–449.
15.
CamanhoPDavilaCDe MouraM. Numerical simulation of mixed-mode progressive delamination in composite materials. J Compos Mater2003; 37: 1415–1438.
16.
KanninenM. An augmented double cantilever beam model for studying crack propagation and arrest. Int J Fract1973; 9: 83–92.
17.
KanninenM. A dynamic analysis of unstable crack propagation and arrest in the DCB test specimen. Int J Fracture1974; 10: 415–430.
18.
AndrewsMMassabòRCoxB. Elastic interaction of multiple delaminations in plates subject to cylindrical bending. Int J Solids Struct2006; 43: 855–886.
19.
SunCPandeyR. Improved method for calculating strain energy release rate based on beam theory. AIAA J1994; 32: 184–189.
20.
O’Brien TK. Characterization of delamination onset and growth in a composite laminate. In: Damage in composite materials basic mechanisms, accumulation, tolerance, and characterization. ASTM STP 775, 1982, pp. 140–57.
21.
RajuICrewsJAminpourM. Convergence of strain energy release rate components for edge-delaminated composite laminates. Eng Fract Mech1988; 30: 383–396.
22.
SchaperyRDavidsonB. Prediction of energy release rate for mixed-mode delamination using classical plate theory. Appl Mech Rev1990; 43: S281–S287.
23.
HuHWuC. Analysis of energy release rate for cracked laminates. Appl Math Mech1995; 16: 565–581.
24.
ZouZReidSSodenPet al.Mode separation of energy release rate for delamination in composite laminates using sublaminates. Int J Solids Struct2001; 38: 2597–2613.
25.
ZhengSSunC. A double-plate finite-element model for the impact-induced delamination problem. Compos Sci Technol1995; 53: 111–118.
26.
SunCManoharanM. Growth of delamination cracks due to bending in a laminate. Compos Sci Technol1989; 34: 365–377.
27.
WangS. Fracture mechanics for delamination problems in composite materials. J Compos Mater1983; 17: 210–223.
28.
SuoZHutchinsonJ. Steady-state cracking in brittle substrates beneath adherent films. Int J Solids Struct1989; 25: 1337–1353.
29.
SuoZHutchinsonJ. Interface crack between two elastic layers. Int J Fract1990; 43: 1–18.
30.
BarberoEReddyJ. Modeling of delamination in composite laminates using a layer-wise plate theory. Int J Solids Struct1991; 28: 373–388.
31.
LeguillonD. A method based on singularity theory to predict edge delamination of laminates. Int J Fract1999; 100: 105–120.
32.
ChoMKimJ. Higher-order zig-zag theory for laminated composites with multiple delaminations. J Appl Mech2001; 68: 869–877.
33.
WilliamsJ. On the calculation of energy release rates for cracked laminates. Int J Fract1988; 36: 101–119.
34.
NairnJ. On the calculation of energy release rates for cracked laminates with residual stresses. Int J Fract2006; 139: 267–293.
35.
WangSChoiI. Boundary-layer effects in composite laminates part 2: free-edge stress solutions and basic characteristics. J Appl Mech1982; 49: 549–560.