Seawater ageing effect on the mechanical properties of composites with different fiber and matrix types

Abstract

The use of fiber-reinforced composites in marine applications such as components of tidal turbines and wave energy converters is becoming attractive because of their reduced weight and improved corrosion resistance. However, when these polymer matrix composite structures are exposed to seawater environment, degradation of material properties is produced affecting reliability. A deep understating of seawater ageing effect on composite structures is essential to ensure long-term performance and durability. A systematic investigation was conducted in this work to evaluate the effect of seawater ageing on mechanical properties of five different composites manufactured with two types of fiber fabrics (unidirectional glass and carbon) and three types of resin systems (epoxy, vinylester and polyester). The behavior of samples with and without accelerated seawater ageing and subjected to tensile, compressive, flexural and shear loading was evaluated. A significant strength reduction due to seawater ageing was observed on composites with epoxy and polyester matrices. Low strength and stiffness values of composites with vinylester matrix are in general observed; however, seawater ageing makes these properties increase slightly. Fracture surface examination by scanning electron microscopy revealed delamination, fiber debonding and resin crumbling due to seawater effect.

Keywords

Seawater ageing fiber-reinforced composites

Get full access to this article

View all access options for this article.

References

Davies

Rajapakse

YDS

. Durability of composites in a marine environment, Springer: New York, 2014.

Garcia-Espinel

Castro-Fresno

Parbole Gayo

, et al. Effects of sea water environment on glass fiber reinforced plastic materials used for marine civil engineering constructions. Mater Des 2015; 66: 46–50.

Shen

C-H

Springer

. Effects of moisture and temperature on the tensile strength of composite materials. J Compos Mater 1977; 11: 2–16.

Tual

Carrere

Davies

, et al. Characterization of sea water ageing effects on mechanical properties of carbon/epoxy composites for tidal turbine blades. Compos Part A 2015; 78: 380–389.

Yang

. Hygrothermal effects in composites. In: Hashmi

MSJ

(ed.) Reference module in materials science and materials engineering, Amsterdam: Elsevier, 2017, pp. 502–519.

Asp

. The effects of moisture and temperature on the interlaminar delamination toughness of a carbon/epoxy composite. Compos Sci Technol 1998; 58: 967–977.

Colin

Verdu

Humid ageing of organic matrix composites. In: Davies

Rajapakse

YDS

(eds). Durability of composites in a marine environment, Netherlands: Springer, 2014, pp. 47–114.

Weitsman

. Fluid effects in polymers and polymeric composites, Boston: Springer Science & Business Media, 2012.

Bazli

Ashrafi

Oskouei

. Effect of harsh environments on mechanical properties of GFRP pultruded profiles. Compos Part B 2016; 99: 203e215.

10.

Visco

Campo

Cianciafara

. Comparison of seawater absorption properties of thermoset resins based composites. Compos Part A 2011; 42: 123–130.

11.

Gellert

Turley

. Seawater immersion ageing of glass-fibre reinforced polymer laminates for marine applications. Compos Part A 1999; 30: 1259–1265.

12.

Pal

Narasimha Murthy

Sreejith

, et al. Effect of laminate thickness on moisture diffusion of polymer matrix composites in artificial seawater ageing. Front Mater Sci 2012; 6: 225–235.

13.

Mungamurugu

Marru

Sardar

, et al. Long term performance study of glass reinforced composites with different resins under marine environment. Fibers Polym 2017; 18: 122–130.

14.

Grant

Bradley

. In-situ observations in SEM of degradation of graphite/epoxy composite materials due to seawater immersion. J Compos Mater 1995; 29: 852–867.

15.

. Behaviours of glass fibre/unsaturated polyester composites under seawater environment. Mater Des 2009; 30: 1337–1340.

16.

Barbosa

APC

Fulco

APP

Guerra

ESS

, et al. Accelerated aging effects on carbon fiber/epoxy composites. Compos Part B 2017; 110: 298e306.

17.

Afshar

Alkhader

Korach

, et al. Effect of long-term exposure to marine environments on the flexural properties of carbon fiber vinylester composites. Compos Struct 2015; 126: 72–77.

18.

Bian

Xiao

Zeng

, et al. Effects of seawater immersion on water absorption and mechanical properties of GFRP composites. J Compos Mater 2012; 46: 3151–3162.

19.

Aldajah

Alawsi

Rahmaan

. Impact of sea and tap water exposure on the durability of GFRP laminates. Mater Des 2009; 30: 1835–1840.

20.

Jiang

Yang

. Long-term moisture effects on the interfacial shear strength between surface treated carbon fiber and epoxy matrix. Compos Part A 2015; 78: 311–317.

21.

Kafodya

Xian

. Durability study of pultruded CFRP plates immersed in water and seawater under sustained bending: water uptake and effects on the mechanical properties. Compos Part B 2015; 70: 138–148.

22.

Hammami

Al-Ghuilani

. Durability and environmental degradation of glass-vinylester composites. Polym Compos 2004; 25: 609–616.

23.

Arun

Basavarajappa

Sherigara

. Damage characterisation of glass/textile fabric polymer hybrid composites in sea water environment. Mater Des 2010; 31: 930–939.

24.

Siriruk

Penumadu

. Degradation in fatigue behavior of carbon fiber–vinyl ester based composites due to sea environment. Compos Part B 2014; 61: 94–98.

25.

Carra

Carvelli

. Long-term bending performance and service life prediction of pultruded glass fibre reinforced polymer composites. Compos Struct 2015; 127: 308–315.

26.

Shen

C-H

Springer

. Effects of moisture and temperature on the tensile strength of composite materials. J Compos Mater 1977; 11: 2–16.

27.

ASTM D3039: Standard test method for tensile properties of polymer matrix composite materials.

28.

ASTM D6641: Standard test method for compressive properties of polymer matrix composite Materials using a combined loading compression (CLC) test fixture.

29.

ASTM D5379: Standard test method for shear properties of composite materials by the V-notched beam method.

30.

ASTM D7264: Standard test method for flexural properties of polymer matrix composite materials.

31.

ASTM D2344: Standard test method for short-beam strength of polymer matrix composite materials and their laminates.