Thermoplastic interleaving is a promising technique to improve delamination resistance of laminated composites. In this study, plain-weave carbon fiber/epoxy composites were interleaved with nylon 6,6 nonwoven fabrics with an areal weight density of 17 gsm. The carbon fiber/epoxy composite laminates with/without nylon 6,6 nonwoven fabric interlayers were manufactured by VARTM technique. Double cantilever beam fracture toughness tests were carried out on the prepared composite test specimens in accordance with ASTM 5528 standard. The experimental test data were statistically analyzed by two-parameter Weibull distribution. The results showed that the initiation and propagation fracture toughness Mode-I fracture toughness of carbon fiber/epoxy composites could be improved by about 34 and 156% (corresponding to a reliability level of 0.50) with the incorporation of nylon 6,6 interlayers in the interlaminar region, respectively. The results also revealed that the percent increase in the propagation fracture toughness value was 67 and 41% at reliability levels of 0.90 and 0.95, respectively.
GreenhalghESRogersCRobinsonP. Fractographic observations on delamination growth and the subsequent migration through the laminate. Compos Sci Technol2009; 69: 2345–2351.
2.
Greenhalgh ES. Failure analysis and fractography of polymer composites. Woodhead Publishing Series in Composites Science and Engineering, CRC Press, 2009, 164–165.
3.
HojoMAndoTTanakaM, et al.Modes I and II interlaminar fracture toughness and fatigue delamination of CF/epoxy laminates with self-same epoxy interleaf. Int J Fatigue2006; 28: 1154–1165.
4.
NakaiYHiwaC. Effects of loading frequency and environment on delamination fatigue crack growth of CFRP. Int J Fatigue2002; 24: 161–70.
5.
SelaNIshaiO. Interlaminar fracture toughness and toughening of laminated composite materials: A review. Compos1989; 20: 423–435.
6.
YasaeeMBondIPTraskRS, et al.Mode I interfacial toughening through discontinuous interleaves for damage suppression and control. Compos A Appl S2012; 43: 198–207.
7.
Saz-OrozcoBDRayDStanleyWF. Effect of thermoplastic veils on interlaminar fracture Toughness of a Glass Fiber/Vinyl Ester Composite. Poly Comp2017; 38: 2501–2508.
8.
NashNHYoungTMStanleyWF. The reversibility of Mode-I and -II interlaminar fracture toughness after hydrothermal aging of carbon/benzoxazine composites with a thermoplastic toughening interlayer. Compos Struct2016; 152: 558–567.
9.
O’DonovanKRayKDMcCarthyMA. Toughening effects of interleaved nylon veils on glass fabric/low-styrene-emission unsaturated polyester resin composites. J Appl Polym Sci2014; 132: 41462–41462.
10.
FitzmauriceKRayDMcCarthyMA. PET interleaving veils for improved fracture toughness of glass fibre/low-styrene-emission unsaturated polyester resin composites. J Appl Polym Sci2016; 133: 42877–42877.
11.
Kuwata M. Mechanisms of interlaminar fracture toughness using non-woven veils as interleaf materials. PhD Thesis, University of London, UK, 2010.
12.
Miller SG, Roberts G, Kohlman L, et al. Impact behavior of composite fan blade leading edge subcomponent with thermoplastic polyurethane interleave. In: Proceedings of 20th international conference on composite materials, Denmark, 19–24 July 2015, pp.1–12.
13.
NiNWenYHeD, et al.High damping and high stiffness CFRP composites with aramid non-woven fabric interlayers. Compos Sci and Technol2015; 117: 92–99.
14.
RamirezVAHoggPJSampsonWW. The influence of the nonwoven veil architectures on interlaminar fracture toughness of interleaved composites. Compos Sci and Technol2015; 110: 103–110.
15.
LeeS-HNoguchiHKimY-B, et al.Effect of interleaved non-woven carbon tissue on interlaminar fracture toughness of laminated composites: Part II – Mode I. J Compos Mater2002; 36: 2169–2181.
16.
HallinanAJ. A review of the Weibull distribution. J Qual Technol1993; 25: 85–93.
17.
OnoK. A Simple estimation method of Weibull modulus and verification with strength data. Appl Sci2019; 9: 1575–1575.
18.
NareshaKShankarKVelmuruganR. Reliability analysis of tensile strengths using Weibull distribution in glass/epoxy and carbon/epoxy composites. Compos B Eng2018; 133: 129–144.
19.
DirikoluMHAktasABirgorenB. Statistical analysis of fracture strength of composite materials using Weibull distribution. Turk J Eng Env Sci2002; 26: 45–48.
20.
ZhouYPervinFLewisL, et al.Fabrication and characterization of carbon/epoxy composites mixed with multi-walled carbon nanotubes. Mater Sci Eng A2008; 475: 157–165.
21.
LiYZhouM. Prediction of fracture toughness scatter of composite materials. Comp Mater Sci2016; 116: 44–51.
22.
ASTM D5528-13. Standard test method for mode I interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites. Annual book of ASTM standards, West Conshohocken, PA, 2013.
PokludaJŠanderaP. Micromechanisms of fracture and fatigue: In a multi-scale context, 1st ed. London: Springer, 2010.
25.
BeylergilBTanoğluMAktaşE. Effect of polyamide-6, 6 (PA 66) nonwoven veils on the mechanical performance of carbon fiber/epoxy composites. Compos Struct2018; 194: 21–35.
26.
QuanDMischoCBinsfeldL, et al.Fracture behaviour of carbon fibre/epoxy composites interleaved by MWCNT- and graphene nanoplatelet-doped thermoplastic veils. Compos Struct2020; 235: 105642–105642.
27.
BeckermannGPickeringK. Mode I and Mode II interlaminar fracture toughness of composite laminates interleaved with electrospun nanofibre veils. Compos A Appl S2015; 72: 11–21.
28.
BeylergilBTanoğluMAktaşE. Enhancement of interlaminar fracture toughness of carbon-fiber epoxy composites using polyamide-6,6 electrospun nanofibers. J Appl Polym Sci2017; 134: 45244–45244.
29.
BeylergilBTanoğluMAktaşE. Mode-I fracture toughness of carbon fiber/epoxy composites interleaved by aramid nonwoven veils. Steel Compos Struct2019; 31: 113–123.
30.
QuanDBolognaFScarselliG, et al.Interlaminar fracture toughness of aerospace-grade carbon fibre reinforced plastics interleaved with thermoplastic veils. Compos A Appl S2020; 128: 105642–105642.
31.
García-RodríguezSMCostaJRankinKE, et al.Interleaving light veils to minimise the trade-off between mode-I interlaminar fracture toughness and in-plane properties. Compos A Appl S2020; 128: 105659–105659.
32.
MolnarKKostakovaEMeszarosL. The effect of needleless nanofibrous interleaves on mechanical properties of carbon fabrics/epoxy laminates. Express Polym Lett2014; 8: 62–72.