Influence of laser process parameters and fiber content on interface properties of GFRPP -aluminum alloy composite by hot press molding

Abstract

Glass fiber-reinforced polypropylene (GFRPP) is widely used in the automotive, aerospace, and other industries due to its advantages of low weight, high strength, corrosion resistance, and low cost. However, insufficient interfacial bonding strength between GFRPP and aluminum alloy limits the performance and reliability of composite structures. In this paper, a grid-like micro-texture was fabricated on the aluminum alloy surface using laser processing, and a mechanical interlocking joint with GFRPP was achieved by hot press molding. The effects of the number of laser scanning passes, grid spacing, and glass fiber content on interfacial bonding performance were systematically investigated. The results showed that joint strength was optimized when the number of laser scanning passes was 10 and the grid spacing was 0.1 mm, while the interfacial performance was optimal when the glass fiber content was 20%. The tensile strength and yield strength of GFRPP increased by up to 97.93% and 126.90%, respectively compared to pure polypropylene. Analysis of the interfacial micromorphology revealed that the laser-textured structure formed effective mechanical interlocking with the GFRPP melt, transforming the interfacial failure mode from brittle interfacial debonding to matrix cohesive failure, thereby enhancing interfacial bonding strength and fracture toughness.

Keywords

GFRPP aluminum alloy laser surface micro-texture hot press molding interfacial bonding strength mechanical interlocking

Get full access to this article

View all access options for this article.

References

Çam

Sofuoğlu

. An investigation on crashworthiness performance of adhesive bonding in automobile hybrid front bumper system subjected to high-speed impact. Int J Impact Eng 2023; 173: 104478. https://doi.org/10.1016/j.ijimpeng.2022.104478

Roszak

Bula

Sagradov

, et al. Experimental and numerical investigation of metal-polymer riveted joints. Mater Res Express 2022; 9(1): 015303. https://doi.org/10.1088/2053-1591/ac49bb

Zou

Jiao

, et al. Effects of laser hybrid interfacial pretreatment on enhancing the carbon fiber reinforced thermosetting composites and TC4 alloy heterogeneous joint. Mater Today Commun 2022; 30: 103142. https://doi.org/10.1016/j.mtcomm.2022.103142

Yin

Xie

, et al. Polymer-metal hybrid material with an ultra-high interface strength based on mechanical interlocking via nanopores produced by electrochemistry. Ind Eng Chem Res 2020; 59(27): 12409–12420. https://doi.org/10.1021/acs.iecr.0c01304

Matta

Sedlacek

Kadleckova

, et al. The effect of surface substrate treatments on the bonding strength of aluminum inserts with glass-reinforced poly(phenylene) sulphide. Materials 2022; 15(5): 1929. https://doi.org/10.3390/ma15051929

Wang

, et al. Effect of different preparation methods on mechanical behaviors of carbon fiber-reinforced PEEK-titanium hybrid laminates. Polym Test 2020; 85: 106462. https://doi.org/10.1016/j.polymertesting.2020.106462

Zou

Feng

Qiu

. Excellent heat transfer enhancement of CNT-metal interface by loading carbyne and metal nanowire into CNT. Int J Heat Mass Tran 2022; 186: 122533. https://doi.org/10.1016/j.ijheatmasstransfer.2022.122533

Shao

Marriam

, et al. Quasi-static and dynamic interfacial evaluations of plasma functionalized carbon nanotube fiber. Appl Surf Sci 2019; 465: 795–801. https://doi.org/10.1016/j.apsusc.2018.09.258

Tan

, et al. Durability of adhesively bonded CFRP-aluminum alloy joints subjected to coupled temperature and alternating load. Int J Adhesion Adhes 2020; 99: 102583. https://doi.org/10.1016/j.ijadhadh.2020.102583

10.

Jiao

Zou

, et al. Carbon fiber reinforced thermoplastic composites and TC4 alloy laser assisted joining with the metal surface laser plastic-covered method. Compos Part B-Eng 2021; 202(3): 108738. https://doi.org/10.1016/j.compositesb.2021.108738

11.

Balle

Huxhold

Emrich

, et al. Influence of heat treatments on the mechanical properties of ultrasonic welded AA 2024/CF-PA66-Joints. Adv Eng Mater 2013; 15(9): 837–845. https://doi.org/10.1002/adem.201200301

12.

Kimura

Kadoya

Kajihara

. Effects of molding conditions on injection molded direct joining under various surface fine-structuring. Int J Adv Manuf Technol 2018; 101(9-12): 2703–2712. https://doi.org/10.1007/s00170-018-3154-8

13.

Pan

Wang

, et al. Enhanced adhesive performance of Ti–6Al–4V/PEEK interface by loading SPEEK on Ti–6Al–4V plates. Int J Adhesion Adhes 2022; 114: 103116. https://doi.org/10.1016/j.ijadhadh.2022.103116

14.

Gonzalez-Canche

Flores-Johnson

Cortes

, et al. Evaluation of surface treatments on 5052-H32 aluminum alloy for enhancing the interfacial adhesion of thermoplastic-based fiber metal laminates. Int J Adhesion Adhes 2018; 82: 90–99. https://doi.org/10.1016/j.ijadhadh.2018.01.003

15.

Liu

Fan

, et al. Enhancement of the adhesion strength at the metal-plastic interface via the structures formed by laser scanning. Opt Laser Technol 2019; 111: 635–643. https://doi.org/10.1016/j.optlastec.2018.10.026

16.

Mourya

Nanda

Parashar

, et al. An explanatory study on defects in plastic molding parts caused by machine parameters in injection molding process. Mater Today Proc 2023; 78: 656–661. https://doi.org/10.1016/j.matpr.2022.12.070

17.

Khatami

Nabavi

Farshidianfar

. A comprehensive review of laser marking: an in-depth exploration of processes, methods, parameters, materials, and applications. Weld World 2025; 69(11): 3415–3442. https://doi.org/10.1007/s40194-025-02129-9

18.

. Effect of fiber factor on the workability and mechanical properties of polyethylene fiber-reinforced high toughness geopolymers. Ceram Int 2022; 48(8): 10458–10471. https://doi.org/10.1016/j.ceramint.2021.12.254

19.

Monticeli

dos Reis

Neves

, et al. Statistical analysis of creep behavior in thermoset and thermoplastic composites reinforced with carbon and glass fibers. J Strain Anal Eng 2021; 56(7): 452–461. https://doi.org/10.1177/0309324720976637

20.

Erartsın

van Drongelen

Govaert

. Identification of plasticity-controlled creep and fatigue failure mechanisms in transversely loaded unidirectional thermoplastic composites. J Compos Mater 2021; 55(14): 1947–1965. https://doi.org/10.1177/0021998320964252

21.

Tseng

Chang

Hsu

. Comparison of recent fiber orientation models in injection molding simulation of fiber-reinforced composites. J Thermoplast Compos 2020; 33(1): 35–52. https://doi.org/10.1177/0892705718804599

22.

Sun

, et al. Nature of steady-state fast flow in entangled polymer melts: chain stretching, shear thinning, and viscosity scaling. Macromolecules 2022; 55(23): 10737–10750. https://doi.org/10.1021/acs.macromol.2c01345

23.

Gurel

Giuntoli

. Shear thinning from bond orientation in model unentangled bottlebrush polymer melts. Macromolecules 2023; 56(15): 5708–5717. https://doi.org/10.1021/acs.macromol.3c01061

24.

Kim

. Collective viscosity model for shear thinning polymeric materials. Rheol Acta 2020; 59(1): 63–72. https://doi.org/10.1007/s00397-019-01180-w