The Extension of Crack Tip Damage Zones in Fiber Reinforced Plastic Laminates

Abstract

The size and character of the damage zone at the tip of sharp notches in fiber reinforced plastic laminates have been investigated. The variables studied were the stress intensity factor, specimen size, laminate thickness, ply thickness, ply orientation, and fiber properties. The damage zone consists of subcracks parallel to the fibers of each ply, in some cases accompanied by delamination between plies. The damage zone is found to increase in extent approximately in proportion to K² _I up to fracture for notch-sensitive laminates. For notch-insensitive laminates, a point is reached where the zone spreads rapidly across the entire specimen prior to fracture. A strong dependence of damage zone size and fracture toughness on ply thickness, fiber orientation, and fiber properties is demonstrated and discussed.

Get full access to this article

View all access options for this article.

References

E. Orowan , and D.K. Felbeck , "Experiments on Brittle Fracture of Steel Plates," Welding J. Suppl. Nov. (1955).

F.J. McGarry , and J.F. Mandell , "Fracture Toughness of Fibrous Glass Reinforced Plastic Composites ," Proc. 27th Reinforced Plastic/Composites Div , SPI, Section 9A (1972).

F.J. McGarry and J.F. Mandell , "Fracture Toughness Studies of Fiber Reinforced Plastic Laminates," Proc. Special Discussion of Solid-Solid Interfaces, Faraday Division of the Chemical Society, Nottingham, England (1972).

J.F. Mandell , F.J. McGarry , J. Im , and U. Meier , "Fiber Orientation, Crack Velocity, and Cyclic Loading Effects on the Mode of Crack Extension in Fiber Reinforced Plastics," Failure Modes in Composites II, TMS/AIME (1974).

S.S. Wang , J.F. Mandell , and F.J. McGarry ," Three-Dimensional Solution for a Through-Thickness Crack with Crack Tip Damage in a Crossplied Laminate," presented at ASTM Symposium on Fracture Mechanics of Composites, Gaithersburg, Md. (Sept. 1974).

S.S. Wang , J.F. Mandell , and F.J. McGarry , "Three-Dimensional Solution for a Through-Thickness Crack in a Crossplied Laminate," presented at ASTM Symposium on Fracture Mechanics of Composites, Gaithersburg, Md. (September 1974).

W.F. Brown, Jr. , and J.E. Srawley , "Plane Strain Crack Toughness Testing of High Strength Metallic Materials ," ASTM STP 410 (1966).

D.L. Bowie , "Rectangular Tensile Sheet with Symmetric Edge Cracks," Paper 64-APM-3, American Society of Mechanical Engineers (1964).

J.F. Mandell , F.J. McGarry , S.S. Wang , and J. Im , "Stress Intensity Factors for Anisotropic Fracture Test Specimens of Several Geometries," J. Composite Materials , Vol. 8 ( 1974), p. 106.

10.

J. Cook , and J.E. Gordon , "A Mechanism for the Control of Crack Propagation in All Brittle Systems ," Proc. Roy. Soc., Vol. A282 (1964), p 508.

11.

J.F. Mandell , F.J. McGarry , R. Kashihara , and W.O. Bishop , "Engineering Aspects of Fracture Toughness: Fiber Reinforced Laminates," Proc. 29th Reinf. Plas./Comp. Div, SPI ( 1974) Section 17D.

12.

J. Rice , "Mechanics of Crack Tip Deformation and Extension by Fatigue," Fatigue Crack Prapagation, ASTM STP 415, (1967), p. 247-311.

13.

F.A. McClintock , and G.R. Irwin , "Plasticity Aspects of Fracture Mechanics," ASTM STP 381, ( 1965), p. 84.

14.

A.A. Wells , "Application of Fracture Mechanics and Beyond General Yielding," British Welding Research Association, Report M13/63, British Welding Journal Nov. (1963), p. 563.

15.

E.M. Wu , "Application of Fracture Mechanics to Orthotropic Plates," T & M Report No. 248, University of Illinois (1963).

16.

D.B. Hiatt , "Fracture of Prenotched Unidirectional Glass Fiber Reinforced Plastics," M.S. Thesis, Dept. of Mechanical Engineering, MIT (1969).