Increased Fracture Toughness of Graphite-Epoxy Composites through Intermittent Interlaminar Bonding

Abstract

The objective of this study has been to increase the fracture toughness of multi-layer continuous-filament graphite-epoxy composites. The method used is intermittent interlaminar bonding, which can lead to a large in crease in the fracture surface area. In this study we achieved intermittent bonding through introduction of thin perforated Mylar between the layers of the composite. For the best optimum condition included in this study, fracture toughness was increased from about 100 kJ/m² for untreated specimens to an average of about 500 kJ/m², while tensile strength dropped from 500 MPa to 400 MPa, and elastic modulus remained the same at about 75 GPa. An approximate analysis is presented to explain the observed improvement in toughness.

Get full access to this article

View all access options for this article.

References

W.T. Freeman and G.C. Kuebeler , "Mechanical and Physical Properties of Advanced Composites", ASTM STP 546 (1974 ), pp. 435-456.

T.U. Marston , A.G. Atkins and D.K. Felbeck , "Interfacial Fracture Energy and the Toughness of Composites", Journal of Materials Science , 9, (1974), pp. 447-455.

A.G. Atkins , "Interlaminar Bonding for High Toughness/High Strength Composites", Journal of Materials Science , 10, (1975), pp. 819-832

. K. Kendall , "Interfacial Cracking of Composite, Part 1 Interlaminar Shear and Tension" , Journal of Materials Science , 11, (1976), pp. 638-644

. J. Cook and J.E. Gordon , "A Mechanism for the Control of Crack Propagation in All-Brittle Systems" , Proc. of the Royal Society, A, 282, (1964), p. 508

. C. Gurney and J. Hunt , "Quasi-Static Crack Propagation", Proc. of the Royal Society, A, 297/8, (1967), p. 508

. L.-C. Jea , "Fracture Toughness of Graphite/Epoxy Composite Laminates Enhanced by the Intermittent-Interlaminar-Bonding Strength". Ph. D. dissertation, University of Michigan, (1979), pp. 62-89, 185-187.

L.-C. Jea and D.K. Felbeck , "Measurement of Fracture Toughness of Thin Graphite-Epoxy Composites in the Range 100 to 800 kJ/m2", in preparation.

M.R. Piggott , "The Effect of Aspect Ratio on Toughness in Composite", Journal of Materials Science , 9, (1974), pp. 494-502.