Graphite/Epoxy [ ± 45]s Tubes. Their Static Axial and Shear Properties and Their Fatigue Behavior under Completely Reversed Load Controlled Loading

Abstract

Fixtures are described which are appropriate for static and fatigue testing of thin-walled composite tubes of 25.4 mm outer diameter and for use in an MTS servohydraulic tension-torsion system. The room temperature static ax ial and shear properties of tubes consisting of four layers of [ ± 45]s graphite epoxy were determined using axial and axial/shear clip-on extensometers where appropriate. Elastic moduli are equal in tension/compression (tor sion/reversed torsion). Ultimate tensile and compressive strengths are nearly equal. The torsional strength depends strongly on the direction of twist. Beyond the relatively small elastic range time-dependent deformation is observed which is also felt as a frequency effect on fatigue life under com pletely reversed axial load controlled loading. The room temperature axial fatigue strength amplitude at 10⁵ cycles is approximately thirty percent of the ultimate strength.

Get full access to this article

View all access options for this article.

References

P.H. Francis , et al., "Biaxial Fatigue Loading of Notched Composites," NASA-CR-145198, June 1977.

P.H. Francis , D.E. Walrath , D.F. Sims and D.N. Weed , "Biaxial Fatigue Loading of Notched Composites ," J. of Composite Materials , 11 (Oct. 1977), pp. 488-501.

P.H. Francis , D.E. Walrath , and D.N. Weed , "First Ply Fatigue of G/E Laminates under Biaxial Loadings," Fibre Science and Technology, 12 (1979), pp. 97-110.

R.R. Fujczak , "Torsional Fatigue Behavior of Graphite-Epoxy Cylinders," Proceedings of 1978 International Conference on Composite Materials (Toronto), American Inst. of Mining, Metallurgical and Petroleum Engineers Corp., pp. 635-647.

M.J. Owen and J.R. Griffiths , "Evaluation of Biaxial Stress Fatigue Surfaces for a Glass Fabric Reinforced Polyester Resin under Static and Fatigue Loading," J. of Material Science, 13, (1978), pp. 1521-1537.

D.E. Marlowe , G.F. Sushinsky and H.B. Dexter , "Elastic Torsional Buckling of Thin-Walled Composite Cylinders," Composite Materials: Testing and Design (Third Conference, ASTM STP 546, 1974, pp. 84-108.

S. Winckler, test performed in the Advanced Composites Laboratory of Rensselaer Polytechnic Institute, April 1981.

S.W. Tsai and H.T. Hahn , Introduction to Composite Materials, Technomic Publishing Co., Inc., 1980.

D. Kujawski , V. Kallianpur and E. Krempl , "An Experimental Study of Uniaxial Creep, Cyclic Creep and Relaxation of AISI Type 304 Stainless Steel at Room Temperature ," J. Mech. Phys. Solids, 28, (1980), pp. 129-148.

10.

W. Flugge , Viscoelasticity, Blaisdell Publishing Co., Waltham, Mass., 1967.

11.

A. Rotem and Z. Hashin , "Fatigue Failure of Angle Ply Laminates," AIAA Journal , 14, No. 7 (1976), pp. 868-872.

12.

J.B. Sturgeon , "Creep, Repeated Loading, Fatigue and Crack Growth in +45/—45 Oriented Carbon Fibre Reinforced Plastics," J. Materials Science, 13, ( 1978 ), pp. 1490-1498.

13.

W.W. Stinchcomb , K.L. Reifsnider and R.S. Williams , "Critical Factors for Frequency-Dependent Fatigue Processes in Composite Materials," Experimental Mechanics, 16, (Sept. 1976), pp. 343-348.

14.

K.L. Reifsnider and A. Talug , "Analysis of Fatigue Damage in Composite Laminates," Int. J. Fatigue, 2, No. 1, (Jan. 1980), pp. 3-11.

15.

N.Q. Nguyen and J.L. Kardos , "Fatigue of Composite Laminates ," AFML-TR-79-4035, 1979 .