Static Compression Failure of Carbon Fibre T800/924C Composite Plate with a Single Hole

Abstract

This paper describes an experimental and theoretical study of the compres sive failure of carbon/epoxy, T800/924C, composite laminates.

Static tests were carried out to investigate the mechanics of uniaxial compressive failure in multidirectional unnotched [(±45/0₂)₃] _s plates. Fibre microbuckling in the 0° plies is the critical damage mode which causes fracture of the composite plate.

A series of experiments was also carried out to determine the failure in compressively loaded [(±45/0₂)₃] _s laminates with circular holes. X-ray radiography and scanning elec tron microscopy were used to observe damage initiation and propagation. Failure is initi ated as matrix cracking. With increasing load fibre microbuckling, surrounded by delami nation, occurs at the edges of the hole at locations of high in-plane compressive stress. When damage reached a critical state the laminate failed catastrophically.

Finally, a theoretical model is presented for predicting the static strength of notched laminates. Theoretical predictions are compared with experimental data for specimens containing circular holes of different sizes. Agreement of theory with test data is ac ceptable.

Get full access to this article

View all access options for this article.

References

Starnes, J.H. , M.D. Rhodes and J.G. Williams. "Effect of Impact and Holes on the Compressive Strength of a Graphite/Epoxy Laminate ," ASTM STP 696, pp. 145-171 (1979).

Garbo, S.P. "Compression Strength of Laminates with Unloaded Fastener Holes," MCAIR-80-005 (May 1980).

Potter, R.T. "The Environmental Degradation of Notched CFRP in Compression," Composites, 14(3) (July 1983).

Curtis, P.T. "CRAG Test Methods for the Measurement of the Engineering Properties of CFRP," RAE TR-85099 (1985).

Guynn, E.G. and W.L. Bradley. "Micromechanics of Compression Failures in Open Hole Composite Laminates," ASTM STP 1012, P. A. Lagace , ed. (1989).

Green, A.E. Proceedings of the Royal Society of London, 180A:173 (1942).

Mikulas, M.M. "Failure Prediction Techniques for Compression Loaded Composite Laminates with Holes," NASA CP 2142 (Aug. 1980).

Scott, I.G. and C.M. Scala. "A Review of Non-destructive Testing of Composite Materials ," NDT International (April 1982).

Freeman, S.M. "Characterization of Lamina and Interlaminar Damage in Graphite/Epoxy by the Deply Technique," ASTM STP 787, pp. 50-62 (1982).

10.

Paris, P.C. and G.C. Sih. "Stress Analysis of Cracks. Fracture Toughness Testing and Its Applications," ASTM STP 381, pp. 30-83 (1965).

11.

Isida, M. "Analysis of SIF for the Tension of a Centrally Cracked Strip with Stiffened End," Eng. Fracture Mech. (1973).

12.

Koiter, W.T. "Note on the SIF for Sheet Strips with Cracks under Tensile Load," Univ. of Technology, Lab. of Engineering Mechanics, Report No. 314, Delft, Netherland (1965).

13.

Parks, D.A. "Fracture Behaviour of Thick, Laminated Technique for Determination of Elastic Crack Tip SIF," Int. J. Fracture , 10(4):487-502 (1974).

14.

Harris, C.E. and D.H. Morris. "Fracture Behaviour of Thick, Laminated Graphite/Epoxy Composites," NASA Contractor Report 3784 (1984).

15.

Waddoups, M.E. , J.R. Eisenman and B.E. Kaminski. "Macroscopic Fracture Mechanics of Advanced Composite Materials," J. Comp. Materials, 5:446-454 (1971).

16.

Bowie's, O.L. "Analysis of an Infinite Plate Containing Radial Cracks Originating from the Boundary of an Internal Circular Hole," J. Math and Physics, 35:60-71 (1956).

17.

Whitney, J.M. and R.J. Nuismer. "Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations," J. Comp. Mater. , 8:253-265 (1974).

18.

Mikulas, M.M. , M.D. Rhodes and P.E. McGowan. "Effects of Orthotropy and Width on the Compression Strength of Graphite/Epoxy Panels with Holes," AIAA Journal, 22(9):1283-1292 (1984).

19.

Nuismer, R.J. and J.D. Labor. "Applications of the Average Stress Failure Criterion: Part II— Compression," J. Composite Materials , 13:49-60 (1979).

20.

Smith, P.A. "Behaviour of Bolted Joints in (0/90)ns Laminates," CUED/C-Mat/TR121, Cambridge University, England (1985).