Fiber-Matrix Adhesion and Its Effect on Composite Mechanical Properties: IV. Mode I and Mode II Fracture Toughness of Graphite/Epoxy Composites

Abstract

To optimize the level of fiber-matrix adhesion an understanding of the relationship between fiber-matrix interfacial bond strength and the mechanical and frac ture behavior of composites is essential. This study establishes the relationship between fiber-matrix interfacial shear strength (ISS) and interlaminar fracture toughness (both Mode I and Mode II) and failure modes for graphite/epoxy composites. A well defined and characterized graphite fiber/epoxy system was chosen in which the level of adhesion be tween fiber and matrix was changed by using the same graphite fibers with different sur face treatments. These surface treatments changed the level of adhesion between the fiber and matrix thus resulting in an increase of the fiber-matrix ISS by over a factor of two while the fiber and matrix properties remained unchanged. The Mode I and Mode II tests were conducted by the double cantilever beam (DCB) and end-notch flexure (ENF) tests methods, respectively. The Mode I fracture toughness (G_IC ) of composites having low fiber-matrix ISS could not be determined from the DCB test because of extensive fiber bridging and crack meandering. For the composites having higher values of the ISS, the G_IC increased with the ISS. The experimental results demonstrated that there is a strong dependency of Mode II fracture toughness (G_IIC ) on fiber-matrix adhesion. Increased fiber-matrix adhesion in one group of composites significantly improved the G_IIC , but the presence of brittle interphase around graphite fibers in another group of composites tended to cancel part of the improvement resulting from increased adhesion. Based on the major failure modes occurring during the Mode I and Mode II loading conditions, a causal link age between fiber-matrix adhesion and interlaminar fracture behavior of graphite/epoxy composites is established.

Get full access to this article

View all access options for this article.

References

Herakovich, C.T. 1981. "On the Relationship between Engineering Properties and Delamination of Composite Materials," J. Composite Materials, 15:336-348.

Sela, N. and O. Ishai. 1989. "Interlaminar Fracture Toughness and Toughening of Laminated Composite Materials: A Review," Composites, 20:423-435.

Pipes, R.B. and N.J. Pagano. 1970. "Interlaminar Stresses in Composite Laminates under Uniform Axial Tension," J. Composite Materials, 4:538-548.

Wang, A.S.D. and F.W. Crossman. 1978. "Calculation of Edge Stresses in Multi-Layer Laminates by Sub-Structuring," J. Composite Materials, 12:538-548.

Wang, S.S. 1983. "Fracture Mechanics of Delamination Problems in Composite Materials," J. Composite Materials, 17:210-223.

Wang, S.S. 1979. "Delamination Crack Growth in Unidirectional Fiber-Reinforced Composites under Static and Cyclic Loading," in Composite Materials Testing and Design. (5th Conference), ASTM STP 674, American Society for Testing and Materials, p. 642

O'Brien, T.K. 1982. "Characterization of Delamination Onset and Growth in a Composite Laminate," in Damage in Composite Materials, ASTM STP 775, Philadelphia : American Society for Testing and Matenals, p. 140.

Poe, C.C., Jr. and W. Illg. 1989. "Strength of a Thick Graphite/Epoxy Rocket Motor Case after Impact by a Blunt Object," in Test Methods for Design Allowables for Fibrous Composites: 2nd Volume, ASTM STP 1003, C. C. Chamis, ed. , Philadelphia: American Society for Testing and Materials, pp. 150-179.

Williams, J.G. and M.D. Rhodes. 1982. "Effect of Resin on Impact Damage Tolerance of Graphite/Epoxy Laminates," in Composite Materials: Testing and Design (Sixth Conference), ASTM STP 787, I. M. Damel, ed., American Society for Testing and Materials, pp. 450-480.

10.

Cantwell, W.J. , P.T. Curtis and J. Morton. 1986. "An Assessment of the Impact Performance of CFRP Reinforced with High-Strain Carbon Fibers," Composite Science and Technology , 25:133-148.

11.

Levin, K. 1986. "Effect of Low-Velocity Impact on Compression Strength of Quasi-Isotropic Laminates," Proceedings of American Society for Composites, First Technical Conference, Dayton, OH , pp. 313-325.

12.

Caprino, G. , J.C. Halpin and L. Nicolais. 1980. "Fracture Toughness of Graphite/Epoxy Laminates" (research report), Composites , pp. 105-107.

13.

Harris, B. , S.E. Dorey and R.G. Cooke. 1988. "Strength and Toughness of Fiber Composites," Composite Science and Technology, 31:121-141.

14.

Carlsson, L.A. and R.B. Pipes. 1987. Experimental Characterization of Composite Materials. Englewood Cliffs, NJ: Prentice-Hall, Inc.

15.

Chai, H. 1984. "The Characterization of Mode I Delamination Failure m Non-Woven, Multidirectional Laminates," Composites , 15:277-290.

16.

Drake, R. and A. Siebert. 1975. "Elastomer-Modified Epoxy Resin for Structural Applications," The SAMPE Quarterly , pp. 11-21.

17.

Scott, J.M. and D.C. Phillips. 1975. "Carbon Fiber Composites with Rubber Toughened Matrices," J. Materials Science , 10:551-562.

18.

Bascom, W.D. , J.L. Bitner , R.J. Moulton and A.R. Siebert. 1980. "The Interlaminar Fracture of Organic-Matrix Woven Reinforcement Composites," Composites, pp 9-18.

19.

Hunston, D.L. , R.J. Moulton , N.J. Johnston and W.D. Bascom. 1987 " Matrix Resin Effects in Composite Delamination. Mode I Fracture Aspects," in Toughened Composites, ASTM STP 937 , N. J. Johnston, ed., Philadelphia : American Society for Testing and Materials, pp. 74-94.

20.

Jordan, W.M. and W.L. Bradley 1987. "Micromechanics of Fracture in Toughened GraphiteEpoxy Laminates," in Toughened Composites, ASTM STP 937 , N. J. Johnston, ed., Philadelphia : American Society for Testing and Materials, pp. 95-114.

21.

Hibbs, M.F. , M.K. Tse and W.L. Bradley. 1987. "Interlaminar Fracture Toughness and Real-Time Fracture Mechamsm of Some Toughened Graphite/Epoxy Composites," in Toughened Composites, ASTM STP 937, N. J. Johnston, ed., Philadelphia : American Society for Testing and Materials, pp. 115-130.

22.

Russell, A.J. and K.N. Street. 1987. "The Effect of Matrix Toughness on Delamination: Static and Fatigue Fracture under Mode II Shear Loading of Graphite Fiber Composites," in Toughened Composites, ASTM STP 937 , N. J. Johnston, ed. , Philadelphia: American Society for Testing and Materials, pp. 275-294.

23.

Johnson, W.S. and P.D. Mangalgiri. 1987. "Influence of the Resin on Interlaminar Mixed-Mode Fracture," in Toughened Composites, ASTM STP 937 , N. J. Johnston, ed., Philadelphia: American Society for Testing and Materials, pp. 295-315.

24.

Bascom, W.D. , R.L. Cottington , R.L. Jones and P. Peyser. 1975. J. Applied Polymer Science, 19:2545.

25.

Tsai, S.W. and H.T. Hahn. 1980. "Role of Interface in the Strength of Composite Materials," Adhesion and Adsorption of Polymers , Part 8. New York, NY: Plenum Publishing Corp.

26.

Ying, L. 1983. "Role of Fiber/Matrix Interphase in Carbon Fiber-Epoxy Composite Impact Toughness," SAMPE Quarterly , pp. 26-33.

27.

Drzal, L.T. and M.J. Rich. 1985. "Effect of Graphite/Epoxy Matrix Adhesion on Composite Fracture Behavior," in Research Advances in Composites in United States and Japan, ASTM STP 846, J. R. Vinson and M. Taya, eds., Philadelphia : American Society for Testing and Materials, pp. 16-26.

28.

Schwartz, A.S. and J.T. Hartness. 1987. "Effect of Fiber Coatings on Interlaminar Fracture Toughness of Composites," in Toughened Composites, ASTM STP 937 , N. J Johnston, ed., Philadelphia : American Society for Testing and Materials, pp. 150-178.

29.

Banerjee, A. , D.D. Edie and A.A. Ogale. 1987. "Interfacial Characteristics of Carbon-Epoxy Composites," Proceedings of American Society for Composites, 2nd Technical Conference, Newark, DE, pp. 259-263.

30.

Drzal, L.T. , M.J. Rich and P.F. Lloyd. 1982. "Adhesion of Graphite Fibers to Epoxy Matrices: I. The Role of Fiber Surface Treatment," J. Adhesion, 16:1-30.

31.

Drzal, L.T. , M.J. Rich , M.F. Koenig and P.F. Lloyd. 1982. 'Adhesion of Graphite Fibers to Epoxy Matrices: II. The Effect of Fiber Finish," J.Adhesion, 16:133-152.

32.

Drzal, L.T. , M.J. Rich and W. Ragland. 1987. "Adhesion between Fiber and Matrix-Its Effect on Composite Test Results," 42nd Annual Conference, Composite Institute, The Society of the Plastics Industry, pp. 1-4.

33.

Madhukar, M.S. and L.T. Drzal 1991. "Fiber-Matrix Adhesion and Its Effect on Composite Mechanical Properties. I. Inplane and Interlaminar Shear Behavior of Graphite/Epoxy Composites," J. Composite Materials, 25(8):932-957

34.

Madhukar, M.S. and L.T. Drzal. 1991 "Fiber-Matrix Adhesion and Its Effect on Composite Mechanical Properties: II Longitudinal (0°) and Transverse (90°) Tensile and Flexure Properties of Graphite/Epoxy Composites," J. Composite Materials, 25(8).958-991

35.

Madhukar, M.S. and L.T. Drzal.

"Fiber-Matrix Adhesion and Its Effect on Composite Mechanical Properties: III Longitudinal (0°) Compressive Properties of Graphite/Epoxy Composites,"

J. Composite Materials (in press).

36.

Waterbury, M.C. and L.T. Drzal. 1989. "Determination of Fiber Volume Fraction by Optical Numeric Volume Fraction Analysis," J. Reinforced Plastics and Composites, 8:627-636.

37.

Gupta, V.B. , L.T. Drzal , Y-C. Lee and M.J. Rich. 1985. "The Temperature-Dependence of Some Mechanical Properties of a Cured Epoxy Resin System," Polymer Engineering and Science , 25:812-823

38.

Wilkins, D.J. , J.R. Eisenmann , R.A. Camm , W.S. Margolis and R.A. Benson. 1980. "Characterizing Delamination Growth in Graphite/Epoxy," in Damage in Composite Materials, ASTM STP 775, Philadelphia: American Society for Testing and Materials , p. 168.

39.

Daniel, I.M. , I. Shareef and A.A. Aliyu. 1987. "Rate Effects on Delamination Fracture Toughness of a Toughened Graphite/Epoxy," in Toughened Composites, ASTM STP 937 , N. J. Johnston, ed., Philadelphia: American Society for Testing and Materials, pp. 260-274.

40.

Whitney, J.M. , C.E. Browning and W. Hoogsteden. 1982. "A Double Cantilever Beam Test for Characterizing Mode I Delamination of Composite Materials," J. Reinforced Plastics and Composites , 1:297-313.

41.

Yeung, P. and L.J. Broutman. 1978. "The Effect of Glass-Resin Interface Strength on the Impact Strength of Fiber Reinforced Plastics," Polymer Engineering and Science, 18:62-72.

42.

Bascom, W.D. , D.J. Boll , D.L. Hunston , B. Fuller and P.J. Phillips. 1987. "Fractographic Analysis of Interlaminar Fracture," in Toughened Composites , ASTM STP 937, N. J. Johnston, ed., Philadelphia : American Society for Testing and Matenals, pp. 131-149.

43.

Bradley, W.L. and R.N. Cohen. 1985 "Matrix Deformation and Fracture in Graphite-Reinforced Epoxies," in Delamination and Debondmg of Materials, ASTM STP 876 , W S. Johnson, ed., Philadelphia: American Society for Testing and Materials, pp. 389-410.

44.

Chai, H. 1986. "On the Correlation between the Mode I Failure of Adhesive Joints and Laminated Composites," Engineering Fracture Mechanics, 24:413-431.

45.

Russell, A.J. and K.N. Street. 1985. "Moisture and Temperature Effects on the Mixed Mode Delamination Fracture of Graphite/Epoxy," in Delamination and Debonding of Materials, ASTM STP 876, W. S. Johnson, ed., Philadelphia : American Society for Testing and Materials , pp. 349-370.

46.

Smiley, A.J. and R.B. Pipes. 1986. "Rate Sensitivity of Interlaminar Fracture Toughness in Composite Materials," Proceedings of the American Society for Composites, First Technical Conference, Dayton, OH, pp. 434-449.

47.

Chai, H. 1989. "Interlaminar Shear Fracture of Laminated Composites," Proceedings of American Society for Composites, Fourth Technical Conference, Blacksburg, VA, pp. 815-825.

48.

Jordan, W.M. 1988. "The Toughness of Damaged or Imperfect Laminates," Proceedings of the American Society for Composites, Third Technical Conference, Seattle, WA, pp. 495-504.

49.

Carlsson, L.A. , J.W. Gillespie and R.B. Pipes. 1986. "On the Analysis and Design of the End-Notched Flexure (ENF) Specimen for Mode II Testing," J. Composite Materials , 20:594-604.