Thermally-Induced Shapes of Unsymmetric Laminates

Abstract

Models to describe the shapes of unsymmetric laminates produced with a flat mould have been already developed by several researchers. These models are reviewed and on some points theory is extended.

The experimental work done so far to confirm the developed theoretical models is rather limited. This especially applies for angle-ply laminates, on which no experimental work has been reported yet. This paper presents new experimental work that has been conducted both on cross-ply and angle-ply laminates over a wide range of laminate dimensions. The experiments show that the influence of the side length on the curvature is very well predicted both for cross-ply and angle-ply laminates, also the bifurcation point behaviour is clearly observed. Possible causes of differences between theory and experiment are outlined. The theoretical predictions are especially sensitive to the transverse thermal expansion coefficient of the individual layers.

Get full access to this article

View all access options for this article.

References

1. Hyer, M. W. 1981. "Some Observations on the Cured Shape of Thin Unsymmetric Laminates," J. of Comp. Materials, 15:175-194.

2. Hyer, M. W. 1981. "Calculation of the Room-Temperature Shapes of Unsymmetric Laminates," J. of Comp. Materials, 15:296-310.

3. Hyer, M. W. 1982. "The Room-Temperature Shapes of Four-Layer Unsymmetric Cross-Ply Laminates," J. of Comp. Materials, 16:318-340.

4. Jun, W. J. and C. S. Hong . 1990. "Effect of Residual Shear Strain on the Cured Shape of Unsymmetric Cross-Ply Thin Laminates," Comp. Science & Technology, 38:55-67.

5. Jun, W. J. and C. S. Hong . 1992. "Cured Shape of Unsymmetric Laminates with Arbitrary Lay-Up Angles," J. of Reinforced Plastics and Comp., II:1352-1366.

6. Hahn, H. T. and D. G. Hwang . 1981. "Residual Stresses and their Effect in Composite Laminates," Proc. of NCKU/AAS nt. Symposium on Eng. Sciences and Mechanics, Taiwan.

7. Hahn, H. T. 1981. "Warping of Unsymmetric Cross-Ply Graphite/Epoxy Laminates," Composite Review, 3:114-117.

8. White, S. R. and H. T. Hahn . 1992. "Process Modeling of Composite Materials: Residual Stress Development During Cure. Part I. Model Formulations," J. of Comp. Materials, 26:2402-2422.

9. White, S. R. and H. T. Hahn . 1992. "Process Modeling of Composite Materials: Residual Stress Development During Cure. Part II. Experimental Validation," J. of Comp. Materials, 26:2423-2454.

10.

10. White, S. R. and H. T. Hahn . 1993. "Cure Cycle Optimization for the Reduction of Processing-Induced Residual Stresses in Composite Materials," J. of Comp. Materials. 27:1352-1378.

11.

11. Kim, K-S , H. T. Hahn and R. B. Croman . 1989. "The Effect of Cooling Rate on Residual Stress in a Thermoplastic Composite," J. of Comp. Technology & Research, 11(2):47-52.

12.

12. Wang, H-B. , S-J Li and T-Y Yu . 1993. "On the Thermal Behavior and Mechanism of Residual Microstress Build-Up at the Matrix Interface in Filled Epoxy Resins," Polymer Engineering and Science, 33(8):474-479.

13.

13. Mrse, A. and M. R. Piggott . 1990. "Relation Between Fibre Divagation and Compressive Properties of Fibre Composites," Proc. of 35th Int. SAMPE Symposium.

14.

14. Warnet, L. 1992. "Cured Shapes of Thin Laminated Plates," University of Twente, MSc thesis.

15.

15. Powell, P. C. 1994. "Engineering with Fibre/Polymer Composites," Chapman & Hall.

16.

16. Tsai, S. W. and H. T. Hahn. 1980. "Introduction to Composite Materials," Lancaster, PA: Technomic Publishing Co.

17.

17. Timoshenko, S. P. and S. Woinowsky-Krieger . 1964. "Theory of Plates & Shells," McGraw-Hill.

18.

18. Fung, Y. C. 1965. "Foundations of Solid Mechanics," Prentice-Hall.

19.

19. Measurements Group, Inc. 1986. "Measurement of Thermal Expansion Coefficient Using Strain Gages," Tech. Note TN-513.