Fracture Behavior of Unidirectional Commingled-Yarn-Based Carbon Fiber/Polyamide 6 Composite under Three-Point Bending

Abstract

Flexure-response and fracture behavior of unidirectional commingled-yarn-based carbon fiber (CF)/polyamide (PA) 6 composite were investigated using three-point edgewise and flatwise bend tests. Difference of the experimental flexure data from that expected was attributed to poorly bonded fiber/matrix interfaces and deviated fiber bundle orientations. For the fracture test, four kinds of notch direction were adopted: edgewise notches parallel (L) and transverse (T) to the major direction of fiber bundles, and flatwise notches parallel (ZT) and perpendicular (ZT) to this direction. Strength and absorbed fracture energy for L and ZL specimens exhibited high sensitivity to notching. ZL specimens exhibited the lowest values of the critical stress intensity factor, K _c which were slightly superior to those of unfilled PA6 matrix. T specimens showed the largest values of the strain energy release rate G_c which were mostly occupied by the plastic fracture energy: the large plastic energy coincided with generation of the crushing-mode failure on the compression side. Enlargement of the compression area was analyzed by means of the rigidity reduction resulting from the fracture progression.

Keywords

commingled-yarn composite flexure test notch direction fracture mechanisms strain energy release rate

Get full access to this article

View all access options for this article.

References

1. O'bradáigh, C. M. and P. J. Mallon . 1989. "Effect of Forming Temperature on the Properties of Polymeric Diaphragm Formed Thermoplastic Composites," Comp. Sci. Tech., 35:235-255.

2. Mallon, P. J. , C. M. O'bradáigh and R. B. Pipes . 1989. "Polymeric Diaphragm Forming of Complex-Curvature Thermoplastic Composite Parts," Composites, 20:48-56.

3. Eveno, E. , J. W. Gillespie , J. M. Schultz and J. R. Vinson . 1987. "Welding of Thermoplastic Composites: Numerical and Experimental Investigation," Proc. 2nd Tech. Conf. American Soc. for Composites, Newark, DE, poster presentation.

4. Woolstencroft, D. H. and P. J. Hogg . 1991. "Cost Effective Manufacturing of Thermoplastic Composites," Proc. 2nd Japan Int. SAMPE Symp., Chiba, Japan, pp. 653-662.

5. Miyasaka, Y. , T. Nakakura , H. Sakai , T. Koba and S. Kishi . 1991. "Thermoplastic Composites for Automobile," ibid., pp. 645-652.

6. Davies, P. and M. L. Benzeggagh . 1989. "Interlaminar Mode-I Fracture Testing," Application of Fracture Mechanics to Composite Materials, K. Friedrich, ed., Amsterdam: Elsevier Sci. Pub., pp. 81-112.

7. Johnston, N. J. , T. W. Towell and P. M. Hergenrother . 1991. "Physical and Mechanical Properties of High-Performance Thermoplastic Polymers and Their Composites," Thermoplastic Composite Materials, L. A. Carlsson, ed., Amsterdam: Elsevier Sci. Pub., pp. 27-71.

8. Bradley, W. L. 1989. "Relationship of Matrix Toughness to Interlaminar Fracture Toughness," Application of Fracture Mechanics to Composite Materials, K. Friedrich, ed., Amsterdam: Elsevier Sci. Pub., pp. 159-187.

9. Coldicott, R. J. , T. Longdon , S. Green and P. J. Ives . 1989. "Heltra—A New System for Blending Fibers and Matrix for Thermoplastic-Based High Performance Composites," Proc. 34th Int. SAMPE Symp., Reno, NV, pp. 2206-2216.

10.

10. Yoon, H. and K. Takahashi . 1993. "Mode I Interlaminar Fracture Toughness of Commingled Carbon Fiber/PEEK Composites," J. Mater Sci., 28:1849-1855.

11.

11. Ye, L. and K. Friedrich . 1993. "Mode I Interlaminar Fracture of Co-Mingled Yarn Based Glass Fiber/Polypropylene Composites," Comp. Sci. Tech., 46:187-198.

12.

12. Ye, L. and K. Friedrich . 1993. "Interlaminar Fracture of Commingled-Fabric-Based GF/PET Composites," Composites, 24:557-654.

13.

13. Matsuo, T. , H. Hamada , Z. Maekawa , N. Ikegawa and M. Yamane . 1993. "Effect of Processing Condition on Bending Properties of Thermoplastic Composites with Commingled Spun Yarn," J. Soc. Mater Sci. Japan, 42:311-316 (in Japanese).

14.

14. Djumaev, A. and K. Takahashi . 1994. "Effect of Moisture Absorption on Damping Performance and Dynamic Stiffness of NY-6/CF Commingled Yarn Composite," J. Mater Sci., 29:4736-4741.

15.

15. Carlsson, L. A. and R. B. Pipes . 1987. Experimental Characterization of Advanced Composite Materials. Englewood Cliffs, NJ: Prentice Hall, pp. 83-93.

16.

16. Kimpara, I., H. C. Kim , I. Ohsawa and M. Takehana , 1979. "Fractography of Fracture Surface of Unidirectional CFRP under Three-Point Bending," J. Soc. Mater Sci. Japan, 28:1160-1166 (in Japanese).

17.

17. Whitney, J. M. 1989. "Experimental Characterization of Delamination Fracture," Interlaminar Response of Composite Materials, N. J. Pagano, ed., Amsterdam: Elsevier Sci. Pub., pp. 161-250.

18.

18. Hashemi, S. and J. G. Williams . 1984. "Size and Loading Mode Effects in Fracture Toughness Testing of Polymers," J. Mater. Sci., 19:3746-3759.

19.

19. ASTM E399-78.

20.

20. Williams, J. G. 1987. Fracture Mechanics of Polymers. Chichester, England: Ellis Horwood, pp. 61-74.

21.

21. Friedrich, K. , T. Gogeva and S. Fakirov . 1988. "Thermoplastic Impregnated Fiber Bundles: Manufacturing of Laminates and Fracture Mechanics Characterization," Comp. Sci. Tech., 33:97-120.

22.

22. Ward, I. M. and D. W. Hadley . 1993. An Introduction to the Mechanical Properties of Solid Polymers. Chichester, England: John Wiley & Sons, pp. 143-171.

23.

23. Karger-Kocsis, J. 1989. "Microstructure and Fracture Mechanical Performance of Short-Fiber Reinforced Thermoplastics," Application of Fracture Mechanics to Composite Materials, K. Friedrich, ed., Amsterdam: Elsevier Sci. Pub., pp. 189-247.