Stresses and Deformations Induced during Manufacturing. Part II: A Study of the Spring-in Phenomenon

Abstract

It has been observed that residual stresses always build up during the fabrication of composite components. Such stresses can change the shape of a component when it is removed from the mould. This paper examines the spring-in induced during fabrication of composite angle components by such residual stresses. The sample composite components were fabricated from unidirectional carbon/epoxy pre-preg tape and plain-weave carbon/epoxy pre-preg fabric, as well as from dry carbon fabric and resin using the resin transfer moulding (RTM) technique. The effects of lay-up, orientations, part thickness, tool angle, tool material, etc. were investigated. The results show that (1) the tool material has an insignificant effect on the degree of spring-in, (2) spring-in is insensitive to the lay-up sequence for symmetric lay-ups, (3) spring-in does not depend on ply orientation angles in the case of fabric laminates, (4) spring-in remains constant for almost all radius/thickness ratios and (5) spring-in decreases with an increase in the tool angle. Comparison with the theoretical model developed by Jain and Mai [1] is provided and good agreement is found.

Get full access to this article

View all access options for this article.

References

1. Jain, L. K. and Y.-W. Mai . 1995. "Stresses and Deformations Induced during Manufacturing. Part I: Theoretical Analysis of Composite Cylinders and Shells," Journal of Composite Materials, 31(7): 672-695.

2. Nairn, J. A. and P. Zoller . 1985. "Matrix Solidification and the Resulting Residual Thermal Stresses in Composites," Journal of Materials Science, 20:355-367.

3. Hyer, M. W. , D. E. Cooper and D. Cohen . 1986. "Stresses and Deformations in Cross-Ply Composite Tubes Subjected to a Uniform Temperature Change," Journal of Thermal Stresses, 9:97-117.

4. Tzeng, J. T. 1995. "Predictions and Experimental Verification of Residual Stresses in Thermoplastic Composite Cylinders," Journal of Thermoplastic Composite Materials, 8:163-179.

5. Wüthrich, C. 1992. "Thick-Walled Composite Tubes under Mechanical and Hygrothermal Loading," Composites, 3:407-413.

6. Tzeng, J. T. and L. S. Chien . 1994. "A Thermal/Mechanical Model of Axially Loaded Thick-Walled Composite Cylinders," Composites Engineering, 4:219-232.

7. Zahlan, N. and J. M. O'Neill . 1989. "Design and Fabrication of Composite Components; the Spring Forward Phenomenon," Composites, 20:77-81.

8. O'Neill, J. M. , T. G. Rogers and A. J. M. Spencer . 1988. "Thermally Induced Distortions in the Moulding of Laminated Channel Sections," Mathematical Engineering in Industry, 2:65-72.

9. Kollár, L. P. 1994. "Approximate Analysis of the Temperature Induced Stresses and Deformations of Composite Shells," Journal of Composite Materials, 28:392-414.

10.

10. Nelson, R. H. 1989. "Prediction of Dimensional Changes in Composite Laminates during Cure," Proceedings of 34th International SAMPE Symposium, pp. 2397-2410.

11.

11. Radford, D. W. and R. J. Diefendorf . 1990. "Shape Instabilities in Composites Resulting from Laminate Anisotropy," Japan US Conference, Maui, HI, pp. 439-448.

12.

12. Roy, A. K. 1991. "Response of Thick Laminated Composite Rings to Thermal Stresses," Composite Structures, 18:125-138.

13.

13. Lutton, B. G. 1991. Analysis of Flange Springback in Constant Section Carbon/Epoxy Composite Angled Parts, B.E. Thesis, University of Technology, Sydney, Australia.