Moisture and Temperature Effects of the Compressive Failure of CFRP Unidirectional Laminates

Abstract

Problems in measuring the compressive strength properties of continuous fibre composites are still encountered at present day even though ISO and ASTM standards exist, and the strength prediction remains an unresolved topic. The objective of the present work is to evaluate the compressive response of the T800/924C carbon fibre-epoxy composite system (currently available for aerospace structural applications) in hot-wet environments using a modified Celanese test rig. The weight gains, maximum moisture contents and through-thickness diffusion coefficients of unidirectional laminates immersed in boiling water (accelerated ageing) are reported. Data are also presented on the effects of moisture and temperature on the compressive strength and failure mode of these laminates. It is observed that failure of specimens tested in hot-wet conditions always occurs as a result of out-of-plane fibre microbuckling. This is attributed to the reduction in matrix strength arising from elevated temperatures and environmental conditioning. In addition, two recent microbuckling models are employed to predict the compressive stress-strain response and failure load of the composite; agreement between theory and experiment is acceptable.

Keywords

carbon fibre-epoxy system water absorption accelerated ageing Fickian diffusion compression testing Celanese test method untabbed specimen shear strength fibre microbuckling compressive strength prediction

Get full access to this article

View all access options for this article.

References

1. Potter, R. T. and D. Purslow . 1983. "The Environmental Degradation of Notched CFRP in Compression," Composites, 14(3):206-225.

2. Barker, A. J. and V. Balasundaram . 1987. "Compression Testing of Carbon Fibre-Reinforced Plastics Exposed to Humid Environments," Composites, 18(3):217-226.

3. Browning, C. E. , C. E. Husman and J. M. Whitney . 1977. "Moisture Effects in Epoxy Matrix Composites," AFML-TR-77-41.

4. Copley, S. M. 1982. "A Computer Program to Model Moisture Diffusion and its Application to Accelerated Ageing of Composites," Royal Aircraft Establishment (RAE), TR-82010.

5. Curtis, P. A. 1985. "CRAG Test Methods for the Measurement of the Engineering Properties of Fibre-Reinforced Plastics," RAE. TR-85099.

6. Soutis, C. and D. Turkmen . 1993. "High Temperature Effects on the Compressive Strength of Glass Fibre-Reinforced Composites," Proceedings of the Ninth International Conference on Composite Materials (ICCM/9), Madrid; July 12-16, pp. 581-588.

7. Soutis, C. , D. Turkmen and C. J. Morrison . 1994. "Compressive Failure of Unidirectional Composites at Elevated Temperature Using Untabbed Specimens," ECCM CTS2, pp. 167-177.

8. Lee, S. and M. Munro . 1990. "Evaluation of Testing Techniques for the Iosipescu Shear Test for Advanced Composites Materials," J. Comp. Mat., 24:419-440.

9. De Wilde, W. P. and P. Frolkovic . 1994. "The Modelling of Moisture Absorption in Epoxies: Effects at Boundaries," Composites, 25(2):119-127.

10.

10. Shen, C. and G. S. Springer . 1976. "Moisture Absorption and Desorption of Composite Materials," J. Comp. Mater., 10:2-20.

11.

11. Soutis, C. 1991. "Measurement of the Static Compressive Strength of Carbon Fibre/Epoxy Laminates," Composites Science & Technology, 42:373-392.

12.

12. Ewins, P. T. and R. T. Potter . 1980. "Some Observations on the Nature of Fibre Reinforced Plastics and the Implications for Structural Design," Phil. Trans. R. Soc, Lond., A294:507-517.

13.

13. Shuart, M. J. 1985. "Short Wavelength Buckling and Shear Failures for Compression Loaded Laminates," NASA TM-87640.

14.

14. Hahn, H. T. 1986. "Compression Failure Mechanisms in Composite Structures," NASA CR-3988.

15.

15. Haeberle, J. G. and F. L. Matthews . 1989. "Compression Test Methods for Composites and Theories Predicting the Compressive Strength of Unidirectional CFRP," Applied Solid Mechanics, 3:66-79.

16.

16. Budiansky, B. and N. A. Fleck . 1994. "Compressive Kinking of Fibre Composites: A Topical Review," Applied Mechanics Reviews, Part 2, 47(6):246-270.

17.

17. Schultheisz, C. R. and A. M. Waas . 1996. "Compressive Failure of Composites," 1,11, Prog. Aerospace Sci., 32:1-78.

18.

18. Rosen, B. W. 1965. "Mechanics of Composite Strengthening," Fibre Composite Materials, American Society of Metals, pp. 37-75.

19.

19. Budiansky, B. 1983. "Micromechanics," Computer & Struct., 16(1-4):3-12.

20.

20. Batdorf, S. B. and R. W. C. Ko . 1987. "Stress-Strain Behaviour and Failure of Uniaxial Composites in Combined Compression and Shear, Parts I and II." Internal Report, School of Engineering and Applied Science, Univ. of California, June.

21.

21. Lager, J. B. and R. R. June . 1969. "Compressive Strength of Boron/Epoxy Composites," J. Composite Materials, 3(1):48-56.

22.

22. Ewins, P. D. 1971. "Tensile and Compressive Test Specimens for Unidirectional Carbon Fibre-Reinforced Plastics," RAE Technical Report 71217, England.

23.

23. Steif, P. S. 1990. "A Model for Kinking in Fibre Composites-I, II," Int. J. Solid Structures, 26:549-569.

24.

24. Argon, A. S. 1972. "Fracture of Composites," Treatise on Materials Science & Technology, 1, New York: Academic Press, pp. 79-114.

25.

25. Budiansky, B. and N. A. Fleck . 1993. "Compressive Failure of Fibre Composites," J. Mech. Phys. Solids, 41:183-211.

26.

26. Fleck, N. A. , L. Deng and B. Budiansky . 1993. "Prediction of Microbuckle Width in Fibre Composites," Harvard University Report MECH-203.

27.

27. Slaughter, W. S. , N. A. Fleck and B. Budiansky . 1993. "Microbuckling of Fibre Composites: The Roles of Multi-Axial Loading and Creep," J. Engng. Mats. and Technology, 115(3):308-313.

28.

28. Slaughter, W. S. and N. A. Fleck . 1995. "Microbuckling of Fibre Composites with Random Initial Fibre Waviness." Submitted to J. Mech. Phys. Solids.

29.

29. Haberle, J. G. and F. L. Matthews . 1994. "A Micromechanics Model for Compressive Failure of Unidirectional Fibre-Reinforced Plastics," J. Comp. Materials, 28(17):1618-1639.

30.

30. Saunders, D. E. J. and C. Soutis . 1995. "The Shear and Compressive Behaviour of Low Temperature Cured CFRP Laminates," 3rd Int. Conf. on Deformation and Fracture of Composites, The Institute of Materials, Guildord, UK, March 27-29, pp. 26-35.