The Influence of Loading Rate on the Mode II Interlaminar Fracture Toughness of Composite Materials

Abstract

The effect of varying loading rate on the mode II interlaminar fracture toughness of a range of composite materials has been investigated. A screw-driven universal testing machine and a fully instrumented drop-weight carriage have been used to obtain crosshead speeds in the range 0.01 mm/min to 3 m/s. The results have shown that the value of G_IIc for many composites is rate-sensitive, tending to increase with increasing loading rate. Damage development in the crack tip region has been investigated by examining the polished edges of a number of test specimens in a scanning electron microscope. It has also been shown that offsetting the center plies by a few degrees in order to reduce fiber bridging results in a greater degree of rate-sensitivity in G_IIc . It is believed that the presence of fiber-bridging in standard unidirectional fracture-mechanics samples conceals much of the intrinsic viscoelastic response of the polymeric matrix. Failure mechanisms at the crack tip have been investigated using the Double Edge Notch Flexure specimen. A scanning electron microscope study of this region has shown that the size and nature of this zone is dependent upon the crosshead displacement rate.

Get full access to this article

View all access options for this article.

References

1. Russell, A. J. and K. N. Street . 1985. "Moisture and Temperature Effects on the Mixed-Mode Delamination Fracture of Unidirectional Graphite/Epoxy." In Delamination and Debonding of Materials, W. S. Johnson , ed., ASTM STP 876, p. 349.

2. Davies, P. and F. X. de Charentenay . 1987. "The Effect of Temperature on the Interlaminar Fracture of Tough Composites," Proc. ICCM6/ECCM2, F. L. Matthews , N. C. R. Buskell and J. M. Hodgkinson , eds., p. 3.284.

3. Hine, P. J. , B. Brew , R. A. Duckett and I. M. Ward . 1989. "Failure Mechanisms in Continuous Carbon Fibre Reinforced PEEK Composites," Comp. Sci. and Tech., 35:31.

4. Davies, P. , W. Cantwell and H. H. Kausch . 1989. "Measurement of Initiation Values of GI, in IM6/PEEK Composites," Comp. Sci. and Tech., 35:301.

5. Beguelin, P. and H. H. Kausch . 1994. "The Effect of the Loading Rate on the Fracture Toughness of Poly(methyl methacrylate), Polyacetal, Polyetheretherketone and Modified PVC," J. Mats. Sci., 29:91.

6. Smiley, A. J. and R. B. Pipes . 1987. "Rate Effects on Mode I Interlaminar Fracture Toughness in Composite Materials," J. Comp. Mats., 21:670.

7. Friedrich, K. , R. Walter , L. A. Carlsson , A. J. Smiley and J. W. Gillespie . 1989. "Mechanisms for Rate Effects on Interlaminar Fracture Toughnesses of Carbon/Epoxy and Carbon/PEEK Composites," J. Mats. Sci., 24:3387.

8. Gillespie, J. W., Jr. , L. A. Carlsson and A. J. Smiley . 1987. "Rate-Dependent Mode I Interlaminar Crack Growth Mechanisms in Graphite/Epoxy and Graphite/PEEK," Comp. Sci. and Tech., 28:1.

9. Mall, S. , G. E. Law and M. Katouzian . 1987. "Loading Rate Effects on Interlaminar Fracture Toughness of a Thermoplastic Composite;," J. Comp. Mats., 21:569.

10.

10. Beguelin, P. , M. Barbezat and H. H. Kausch . 1991. "Mechanical Characterization of Polymers and Composites with a Servohydraulic High-Speed Tensile Tester," J. Phys. III, (1):1867.

11.

11. Aliyu, A. A. and I. M. Daniel . 1985. "Effects of Strain Rate on Delamination Fracture Toughness of Graphite/Epoxy." In Delamination and Debonding of Materials, W. S. Johnson , ed., ASTM STP 876, p. 336.

12.

12. Daniel, I. M. , I. Shareef and A. A. Aliyu . 1987. "Rate Effects on Delamination Fracture Toughness of a Toughened Graphite/Epoxy." In Toughened Composites, N. J. Johnston , ed., ASTM STP 937

13.

13. Masters, J. E. 1987. "Correlation of Impact and Delamination Resistance in Interleafed Laminates," Proc. ICCM6/ECCM2, F. L. Matthews , N. C. R. Buskell and J. M. Hodgkinson , eds., p. 3.96.

14.

14. Chapman, T. J. , A. J. Smiley and R. B. Pipes . 1987. "Rate and Temperature Effects on Mode II Interlaminar Fracture Toughness in Composite Materials," Proc. ICCM6/ECCM2, F. L. Matthews , N. C. R. Buskell and J. M. Hodgkinson , eds., p. 3.295.

15.

15. Maikuma, H. , J. W. Gillespie, Jr. , and D. J. Wilkins . 1990. "Mode II Interlaminar Fracture of the Center Notch Flexural Specimen under Impact Loading," J. Comp. Mats., 24:124.

16.

16. European Structural Integrity Society . 1993. "Protocol for Mode II Testing of Composite Materials," ESIS.

17.

17. Johnson, W. S. and P. D. Mangalgiri . 1986. "Investigation of Fiber Bridging in Double Cantilever Beam Specimens," NASA TM 87776.

18.

18. Harding, J. and L. M. Welsh . 1983. "A Tensile Testing Technique for Fibre-Reinforcing Composites at Impact Rates of Strain," J. Mats. Sci., 18:1810.

19.

19. ICI data sheets on APC2.

20.

20. Davies, P. , W. Cantwell , H. Richard , C. Moulin and H. H. Kausch . 1989. "Interlaminar Fracture Testing of Carbon Fibre/PEEK Composites, Validity and Applications" Proc. ECCM3, A. R. Bunsell , P. Lamicq and A. Massiah , eds., p. 747.

21.

21. Hunston, D. L. , A. J. Kinloch , S. J. Shaw and S. S. Wang . 1988. "Characterization of the Fracture Behavior of Adhesive Joints." In Adhesive Joints, K. L. Mittal , ed.. Plenum Press, p. 789.

22.

22. Fischer, C. and F. J. Arendts . "The Temperature Dependence of the Interlaminar Fracture Toughness and the Correlation with the Temperature Dependent Impact Behaviour of Composite Structures," Proc. ICCM9, Vol. 5, A. Miravete , ed., Woodhead Pub. Ltd., p. 350.

23.

23. Cantwell, W. J. 1996. "Low Temperature Fracture of Epoxy Resins and Their Composites," Proc. Instn. Mech. Engrs., Vol. 210, pp. 1-7.

24.

24. Davies, P. , W. J. Cantwell and H. H. Kausch . 1990. "Delamination from Thin Starter Films in Carbon Fibre/PEEK Composites," J. Mass. Sci. Letters, 9:1349.

25.

25. Cantwell, W. J. and H. H. Kausch . 1992. "An Evaluation of the Interlaminar Fracture Toughness of a Thermoplastic Composite with Offset Centre Plies," Mechanics of Composite Materials, 4:476.

26.

26. Davies, P. , W. J. Cantwell and H. H. Kausch . 1989. "A Study of the Delamination Resistance of IM6/PEEK Composites," Comp. Sci. and Tech., 36:153.

27.

27. Sue, H. J. 1992. "Craze-Like Damage in a Core-Shell Rubber-Modified Epoxy Ststem," J. Mats. Sci., 27:3098.