Effect of Isothermal Aging on Ultimate Strength of High-Temperature Composite Materials for SST Structures

Abstract

The objective of this experimental study was to evaluate the effect of iso-thermal aging on the ultimate strength of three kinds of carbon/high-temperature composite materials, i.e., G40-800/5260 and MR50K/MR2000N bismaleimide composites and T800H/PI-SP amorphous thermoplastic polyimide composite. These materials are current candidate structural materials for a supersonic transport of the next-generation. The hole-notched and unnotched panels, before being machined to specimens, were isothermally aged at 120°C and 180°C for up to 15,000 hours. Static tests at room and elevated temperatures before and after thermal aging provided the open-hole tensile, open-hole compressive, and short beam shear strengths. Moreover, the effects of five oxidation resistant treatments on open-hole compressive strength at 180°C were investigated after isothermal aging of 5,000 hours at 180°C. The test results clarified the effects of isothermal aging on ultimate strengths and oxidation resistant treatments on open-hole compressive strength. Moreover, the possibility of developing an accelerated aging test method is discussed using a modified Larson-Miller type equation.

Keywords

bismaleimide composites thermoplastic polyimide composite super-sonic transport open-hole strengths short beam shear strength isothermal aging oxidation resistant treatments accelerated test methodology.

Get full access to this article

View all access options for this article.

References

1. Rogalski, M.E. , "Aging of Polymeric Materials for Use on HSCT," SAE Technical Paper Series 942162, SAE International, 1994.

2. Poole, E.L. and Lin, K.Y. , "Effects of Aging on Compressive Strength of Composites After Impact," AIAA-94-1532-CP, Proc. 35th SDM Conf., American Institute of Aeronautics and Astronautics, 1994, pp. 1683-1690.

3. Harmon, D. , "Durability of Isothermally Aged Polymer Matrix Composites," Proc. ICCM-11, Gold Coast, 1997, pp. V-507N5 16.

4. Shimokawa, T. and Katoh, H. , "Application of the Larson-Miller Equation to Strength Estimation of Light Metallic Materials After Thermal Aging," Proc. 34th Aircraft Symposium, Japan Society for Aeronautical and Space Sciences, 1996, pp. 241-244. (in Japanese)