Damping Performance of Cocured Graphite/Epoxy Composite Laminates with Embedded Damping Materials

Abstract

Cocuring viscoelastic damping materials in composites has been shown to be successful in greatly increasing the damping of composite structures. The damping performance, however, is often not as high in cocured composites as in secondarily bonded composites, where the damping material does not undergo the laminate cure cycle. The reason for the discrepancy in damping between the cocured and secondarily bonded samples was found to be resin penetration into the damping material. Samples with a barrier layer between the damping material and the epoxy resin had a 15.7% to 92.3% higher effective loss factor (depending on the frequency) than cocured FasTape™ 1125 samples without the barrier and at least 168% higher effective loss factor than cocured ISD 112 samples without the barrier. These higher damping values are very close to the values achieved by secondarily bonding. Viscoelastic damping materials typically have maximum recommended temperatures below that of the composite cure cycles. The effect of cure temperature on viscoelastic damping materials was also studied and it was determined that most damping materials are marginally affected by cure cycle temperature.

Keywords

damping in composite materials cocuring viscoelastic materials embedded damping materials

Get full access to this article

View all access options for this article.

References

1. Kosmatka, J. B. and S. L. Liguore . 1993. "Review of Methods to Study Constrained Layer Damping," ASCE Journal of Aerospace Engineering, 6:268-283.

2. Kosmatka, J. B. , A. J. Lapid and O. Mehmed . 1996. "Vibration Reduction in Advanced Composite Turbe Fan Blades Using Embedded Damping Materials," Proceedings of the 1996 SPIE Symposium on Smart Materials and Structures, 2720:13-24.

3. Schultze, J. F. and J. B. Kosmatka . 1989. "Vibration Reduction via Constrained-Layer Damping Techniques," Proceedings of the Damping '89 Conference, KAB1-16.

4. Belknap, F. L. and J. B. Kosmatka . 1991. "Vibration Suppression of Thin-Walled Composite Tubes Using Embedded Viscoelastic Layers," Proceedings of the Damping '91 Conference, HAC1-16.

5. Rotz, C. A. and D. J. Barrett . 1991. "Cocured Damped Layers in Composite Structure," SAMPE Quarterly, pp. 43-47.

6. Harvey, J. A. , J. L. Koury , T. D. Kim and M. L. Drake . 1993. "Integrally Damped Composites—A Study on Fabrication, Dynamics and Statics Effects," SPIE Proceedings on Smart Structures and Materials, Albuquerque, NM, pp. 634-640.

7. Gerst, D. , M. D. Rao and S. He . 1992. "Damping of Cocured Composite Structures Incorporating Viscoleastic Materials," Proceedings of the Damping of Multiphase Inorganic Materials Symposium, Chicago, pp. 85-93.

8. Rao, M. D. and S. He . 1993. "Dynamic Analysis and Design of Laminated Composite Beam with Multiple Damping Layers," AIAA Journal, 31:736-745.

9. Napolitano, K. L. , W. Grippo and J. B. Kosmatka . 1998. "Analysis, Design and Testing of Two Cocured Damped Composite Torsion Shafts," SPIE Proceedings on Smart Structures and Materials, San Diego, CA.

10.

10. Maly, J. J. and C. D. Johnson . 1996. "Cocured Viscoelastic Composites," SPIE Proceedings on Smart Structures and Materials, San Diego, CA, pp. 365-376.