Failure Investigation of Graphite/Polyimide Fabric Composites at Room and Elevated Temperatures Using the Biaxial Iosipescu Test

Abstract

The biaxial and modified biaxial Iosipescu shear test methods were applied to determine the shear dominated, biaxial mechanical response of graphite/PMR-15 and graphite/Avimid-R woven fabric composites at room and elevated temperatures. Three different composite architectures were examined: T650-35 warp-aligned, 8-harness satin (8HS) fabric in a PMR-15 matrix, T650-35 warp-aligned, 8HS fabric in an Avimid-R matrix and T650-35 0°/90°, 8HS fabric in an Avimid-R matrix. Several biaxial Iosipescu tests were performed at room temperature under shear, shear-tension, and shear-compression loading conditions to characterize damage and obtain biaxial, shear dominated failure properties. Shear tests were also conducted at elevated temperatures approaching 316 °C to determine the effects of temperature on the shear strengths of the composites investigated. A nonlinear finite element analysis is briefly introduced to evaluate the effects of specimen sliding and geometric nonlinearities on the stress and strain distributions in the biaxial Iosipescu specimens. In addition, the effects of different loading block geometries on the stress distribution in the Iosipescu specimens subjected to biaxial loads were also investigated. Within this investigation, it was found that graphite/Avimid-R was more resistant to biaxial, shear dominated failure at room temperature in comparison to graphite/PMR-15. However, the graphite/PMR-15 composite system exhibited better shear strength properties at elevated temperatures above 232 °C. It was also found that the effect of compression along the notch root axis generated by the loading blocks did not affect the loads at failure.

Get full access to this article

View all access options for this article.

References

1. Meador, M. A. , P. J. Cavano and D. C. Malarik . 1992. "High Temperature Polymer Matrix Composites for Extreme Environments," HITEMP Review 1992, 529-539.

2. Iosipescu, N. 1967. "New Accurate Procedure for Single Shear Testing of Metals," Journal of Materials, 2:537-566.

3. Adams, D. F. and D. E. Walrath . 1982. "Iosipescu Shear Properties of SMC Composite Materials," In Composite Materials: Testing and Design (Sixth Conference), edited by I. M. Daniel , 19-33: ASTM STP 787.

4. Adams, D. F. and D. E. Walrath . 1987. "Current Status of the Iosipescu ShearTest Method," Journal of Composite Materials, 21:494-507.

5. Adams, D. F. and D. E. Walrath . 1987. "Further Developments of the Iosipescu Shear Test Method," Experimental Mechanics, 27:113-119.

6. Slepetz, J. M. , T. F. Zagaeski and R. F. Novello . 1978. Report AMMRC TR 78-30. Watertown, MA: Army Materials and Mechanics Research Center.

7. Walrath, D. E. and D. F. Adams . June 1983. Analysis of the Stress State in an Iosipescu Shear Test Specimen. Report UWME-DR-301-102-1. Laramie, Wyoming: Department of Mechanical Engineering, University of Wyoming.

8. Owens, G. A. and S. E. Schofield . 1988. "Thermal Cycling and Mechanical Property Assessment of Carbon Fibre Fabric Reinforced PMR-15 Polyimide Laminates," Composites Science and Technology, 33:177-190.

9. Grape, J. A. and V. Gupta . 1995. "Failure in Carbon/Polyimide Laminates under Biaxial Compression," Journal of Composite Materials, 29:1850-1872.

10.

10. Mirzadeh, F. and K. L. Reifsnider . 1992. "Micro-deformations in C3000/PMR15 Woven Composite," Journal of Composite Materials, 26:185-205.

11.

11. Naik,N. K. , P.S. Shembekar and M. V. Hosur .1991. "Failure Behavior of Woven Fabric Composites," Journal of Composites Technology & Research, 13:107-116.

12.

12. Ho, H. , M. Y. Tsai , J. Morton and G. L. Farley . March 1994. "In-Plane Shear Testing of Graphite-Woven Fabric Composites," Experimental Mechanics, 45-52.

13.

13. Walsh, T. J. and O. O. Ochoa . 1996. "Analytical and Experimental Mechanics of Woven Fabric Composites," Mechanics of Composite Materials and Structures, 3:133-152.

14.

14. Ifju, P. G. 1995. "Shear Testing of Textile Composite Materials," Journal of Composites Technology & Research, 17:199-204.

15.

15. Ifju, P. G. , P. G. Masters and W. C. Jackson . 1995. "The Use of Moire Interferometry as an Aid to Standard Test-Method Development for Textile Composite Materials," Composites Science and Technology, 53:155-163.

16.

16. Ifju, P. G. 1991. "The Shear Gage: For Reliable Shear Modulus Measurements of Composite Materials," SEM Proceedings Conference, 1-10, Department of Engineering Science and Mechanics.

17.

17. Broughton, W. R. 1989. "Shear Properties of Unidirectional Carbon Fibre Composites," Ph.D. Dissertation, University of Cambridge.

18.

18. Kumosa, M. and D. Hull . 1987. "Mixed-mode Fracture of Composites using the Iosipescu Shear Test," International Journal of Fracture, 35:83-102.

19.

19. Broughton, E. R. , M. Kumosa and D. Hull . 1990."Analysis of the Iosipescu Shear Test as Applied to Unidirectional Carbon-Fiber Reinforced Composites," Composites Science and Technology, 38:299-325.

20.

20. Bansal, A. and M. Kumosa . 1995. "Experimental and Analytical Studies of Failure Modes in Iosipescu Specimens under Biaxial Loadings," Journal of Composite Materials, 29:334-358.

21.

21. Sukumar, N. and M. Kumosa . 1992. "Finite Element Analysis of Mixed Mode Fracture and Failure in Iosipescu Specimens," International Journal of Fracture, 58:177-192.

22.

22. Bansal, A. and M. Kumosa . 1995. "Application of the Biaxial Iosipescu Method to Mixed-Mode Fracture of Unidirectional Composites," International Journal of Fracture, 71:131-150.

23.

23. Ho, H. , J. Morton and G. Farley . "Non-linear Numerical Analysis of the Iosipescu Specimen for Composite Materials," Composites Science and Technology, 50:355-365.

24.

24. Searles, K. , V. Thirumalai , M. V. Balakrishnan and M. Kumosa . 1995-1996. Annual Progress Report. "Biaxial Failure Analysis of Graphite Reinforced Polyimide Composites," Portland, OR and Denver, CO: Department of Materials Science and Engineering, Oregon Graduate Institute of Science and Technology, Center for Advanced Materials and Structures, University of Denver.

25.

25. Kumosa, M. , K. H. Searles and G. Odegard . 1997."Biaxial Failure Analysis of Graphite Reinforced Polyimide Composites," HITEMP Review 1997, Paper 18:1-11.

26.

26. Searles, K. , J. McCarthy and M. Kumosa . 1997: "An Image Analysis Technique for Evaluating Internal Damage in Graphite/Polyimide Fabric Composites," Composites Science and Technology Vol. 58(1998), 1607-1619.

27.

27. Tsai, C. L. and I. M. Daniel . 1991. "Determination of In-Plane and Out-of-Plane Shear Moduli of Composite Materials," Experimental Mechanics, pp. 295-299.

28.

28. Kumosa, M. and Y. Han . "Non-Linear Finite Element Analysis of Iosipescu Specimens," Journal of Composites Science and Technology, in press.

29.

29. Han, Y. Finite Element Analyses of Advanced Composite Structures, MS Thesis, Department of Engineering, University of Denver, November 1997.