Char Formation in Polyamides (Nylons 6 and 6.6) and Wool Keratin Phosphorylated by Polyol Phosphoryl Chlorides

Abstract

Polyamides (nylon 6 and 6.6) phosphorylated by spirocyclic pentaerythritol phosphoryl chloride (SPDPC), cyclic 1,3-propanediol phosphoryl chloride (CPPC), and cyclic 2,2- diethyl-1,3-propanediol phosphoryl chloride (CDPPC) can yield phosphorus levels up to 0.7% (w/w). Calculations suggest that only primary amine groups at the end of the molecular chain are the possible phosphorylation sites. The presence of substituted 1,3-propanediol phosphonate moieties significantly increases polyamide char formation above 500°C, and scanning electron microscopy indicates that the residual char has an intumescent structure. SPDPC-phosphorylated wool keratin yields higher phosphorus levels up to 2.06%. For nylons 6 and 6.6, the presence of a methylolated triazine (as the commercial agent Lyofix MLF NEW, Ciba) in the pad-cured treatment can increase the phosphorus level further to significantly enhance char formation. SEM images suggest that the reacted substrates yield char volume expansions in wool of up to 336% compared to the control sample chars.

Get full access to this article

View all access options for this article.

References

Bourbigot, S. , Devaux, E. , and Flambard, X. , Flammability of Polyamide-6/Clay Hybrid Nanocomposite Textiles, Polym. Degrad. Stab. 75(2), 397-402 (2002).

Davies, P.J. , Horrocks, A.R. , and Miraftab , M. , Char Formation in Flame-retarded Wool Fibres, Part 1: Effect of Intumescent on Thermogravimetric Behaviour, Fire Mater. 24, 151-157 (2000).

Morgan, A.B. , Kashiwagi, T. , Harris, R.H. , Campbell, J.R. , and Gilman, J.W. , Flammability Properties of Polymer-clay Nanocomposites: Polyamide-6 and Polypropylene Clay Nanocomposites, in "Fire and Polymers ," G. L. Nelson and C. A. Wilkie , Eds., ACS Symposium Series, 797, American Chemical Society, Washington, D.C., 2001.

Horrocks, A. R., and Zhang, S., U.K. patent application 0018521.5, Flame Retardancy Treatment of Polymeric Material, July 28, 2000, granted August 2003.

Horrocks, A.R. , and Zhang, S. , Enhancing Polymer Char Formation by Reaction with Phosphorylated Polyols, Part 1: Cellulose, Polymer 42, 8025-8033 (2001).

Horrocks, A.R. , and Zhang, S. , Enhancing Polymer Flame Retardancy by Reaction with Phosphorylated Polyols, Part 2: Cellulose Treated with a Phosphonium Salt Urea Condensate (Proban CC®) Flame Retardant, Fire Mater. 26, 173-182 (2002).

Kandola, B.K. , Nanocomposites, in "Fire Retardant Materials," A. R. Horrocks and D. Price , Eds., Woodhead Publishing, Cambridge, U.K., 2001, pp. 204-219.

Moncrieff, R. , in "Man-made Fibres," 6th ed., Newnes-Butterworth, London, 1975 .

Peters, R.H. , and Still, R.H. , in "Applied Fibre Science," vol. 2, F. Happey , Ed., Academic Press, London, 1979, pp. 376-390.

10.

Sasse, K. , in "Houben-Weyl, Methoden der Organischen Chemie," vol 12/1 and 12/2, Georg Thieme Verlag, Stuttgart, Germany, 1965.

11.

Wang, J. , and Zhang, S. Approaches to the Flame Retardancy of Polymers, I: Electron-beam Pre-irradiation and Grafting of Acrylic Monomers on to EVA Copolymers, J. Fire Sci. 15, 68-87 (1997).

12.

Wilkie, C.A. , Suzuki, M. , Dong , X. , Deacon, C. , Chandrasiri, J.A. , and Xue, T.J. , Grafting to Achieve Flame Retardancy, Polym. Degrad. Stab. 54, 117-124 (1996). 13. Zhang, S. , and Horrocks, A.R. , Substantive Intumescence from Phosphorylated 1,3-propandiol Derivatives Substituted onto Cellulose, J. Appl. Polym. Sci. 90, 3165-3172 (2003).