Ultraviolet resistant cotton fabrics were developed by coating with ZnO and TiO2 nanoparticles. The ZnO nanoparticles applied on cotton yarns were found to withstand the knitting operation. Meanwhile, the TiO 2 nanoparticles applied on the bleached as well as reactive dyed cotton fabrics by the sol-gel and linking agent methods were found to be intact after various cycles of domestic washing. Knitted fabrics containing ZnO nanoparticles showed moderate to high ultraviolet protection factor (UPF) values, whereas 50+ UPF values were measured for the TiO2-coated samples. Further it was found that the rutile phase was better than anatase phase in blocking UV rays. The developed process can be easily adapted to the existing textile machinery, making it industrially viable.
Mills, A., Elliott, N., Parkin, I.P., O’Neill, S.A., and Clark, R.J., Novel TiO2 CVD Films for Semiconductor PhotocatalysisJ. Photochem. Photobio. A. Chem., 151, 171-179 (2002).
2.
Daoud, W.A., and Xin, J.H., Low Temperature Sol-Gel Processed Photocatalytic Titania CoatingJ. Sol-Gel Sci. Tech., 29, 25-29 (2004).
3.
Bozzi, A., Yuranova, T., Guasaquillo, I., Laub, D., and Kiwi, J., Self-cleaning of Modified Cotton Textiles by TiO2 at Low Temperatures Under Daylight IrradiationJ. Photochem. Photobio. A. Chem., 174, 156-164 (2005).
4.
Meilert, K.T. , Laub, D., and Kiwi, J., Photocatalytic Self-cleaning of Modified Cotton Textiles by TiO2 Clusters Attached by Chemical SpacersJ. Mol. Cata. A: Chem., 237, 101-108 (2005).
5.
Marsh, D.H., Riley, D.J., York, D., and Graydon, A., Sorption of Inorganic Nanoparticles in Woven Cellulose Fabrics Particuology , 7, 121-128 (2009).
6.
Becheri, A., Dürr, M., Lo Nostro, P., and Baglioni, P., Synthesis and Characterization of Zinc Oxide Nanoparticles: Application to Textiles as UV-AbsorbersJ. Nanoparticle Res., 10, 679-689 (2008).
7.
Lu, H., Fei, B., Xin, J.H., Wang, R., and Li, L., Fabrication of UV-blocking Nanohybrid Coating via Miniemulsion PolymerizationJ. Colloid Interface Sci., 300, 111-116 ( 2006).
8.
Vigneshwaran, N., Kumar, S., Kathe, A.A., Varadarajan, P.V., and Prasad, V., Functional Finishing of Cotton Fabrics using Zinc Oxide-Soluble StarchNanocomposites Nanotech., 17, 5087-5095 (2006).
9.
Chatelon, J.P. , Terrier, A., and Royer, J.A., Influence of Elaboration Parameters on the Properties of Tin Oxide Films Obtained by the Sol-Gel ProcessJ. Sol-Gel Sci. Tech., 10, 55-65 (1997).
10.
Partlow, D.P. , Gurkovich, S.R., Radford, K.C., and Denes, L.J., Switchable Vanadium Oxide Films by a Sol-Gel ProcessJ. Appl. Phys., 70, 443 (1991).
11.
Ghodsi, F.E. , Tepehan, F.Z., and Tepehan, G.G., T. Optical Properties of Ta2O5 Thin Films Deposited using the Spin Coating Process Sol. Films, 295, 11-15 (1997).
12.
Bach, U., Lupo, D., Comte, P., Moser, J.E., Weissortel, F., Salbeck, J., Spreitzer, H., and Gratzel, M., Solid-state Dye-Sensitized Sesoporous TiO2 Solar Cells with High Photon-to-Electron ConversionEfficiencies Nature, 395, 583-584 ( 1998).
13.
Mahltig, B. , Bottcher, H., Rauch, K., Dieckmann, U., Nitsche, R., and Fritz T., Optimized UV Protecting Coatings by Combination of Organic and Inorganic UV Absorbers T. Sol. Films, 485, 108-114 (2005).
14.
Reinert, G. , Fuso, F., Hilfiker, R., and Schmidt, E., UV-Protecting Properties of Textile Fab-rics and Their Improvement. Text. Chem. Color., 29, 36-43 (1997).
15.
Yang, H., Zhu, S., and Pan, N., Studying the Mechanisms of Titanium Dioxide as Ultraviolet-Blocking Additive for Films and Fabrics by an Improved SchemeJ. App. Polym. Sci., 92, 3201- 3210 (2004).
16.
Ohno, T., Sarukawa, K., Tokieda, K., and Matsumura, M., Morphology of a TiO2 Photocatalyst (Degussa, P-25) Consisting of Anatase and Rutile Crystalline PhasesJ. Catalysis, 203, 82-86 ( 2001).
17.
Campus, F.Bonhote, P.Gratzel, M., Heinen, S., and Walder, L., Electrochromic Devices Based on Surface-Modified Nanocrystalline TiO2 Thin-Film Electrodes Sol. Energ. Mater. Sol. Cell., 56, 281-297 ( 1999).
18.
Dhananjeyan, M., Kiwi, J., and Thampi, K., Photocatalytic Performance of TiO2 and Fe2O3 Immobilized on Derivatized Polymer Films for Mineralisation of PollutantsChem. Commun.1443-1444 (2000).
19.
Dhananjeyan, M., Mielczarski, E., Thampi, K., Buffat, Ph. , Bensimon, M., Kulik, A., et al., Photodynamics and Surface Characterization of TiO2 and Fe2O3 Photocatalysts Immobilized on Modified Polyethylene FilmsJ. Phys. Chem. B.105, 12046- 12055, ( 2001).
20.
Li, Q., Kumar, V., Li, Y., Zhang, H., Marks, T.J., and Chang, R.P.H., Fabrication of ZnO Nanorods and Nanotubes in Aqueous SolutionsChem. Mater., 17, 1001-1006 (2005).
21.
Mao, Z.Shi, Q.Zhang, L., and Cao, H., The Formation and UV-blocking Property of Needle-Shaped ZnO Nanorod on CottonFabric T. Sol. Films, 517, 2681-2686 (2009).
22.
Mo, S.D. , Ching, W.Y., Electronic and Optical Properties of Three Phases of Titanium Dioxide: Rutile, Anatase, and BrookitePhys. Rev. B., 51, 13023-13032 (1995).