Development and Filtration Performance of Polylactic Acid Meltblowns

Abstract

Polylactic acid (PLA) is a biodegradable material that can be used to make meltblowns (MBs, which are fabrics made by the meltblowing method) using direct melt spun. PLA MBs were successfully produced in a 20 cm laboratory meltblown line. The relationships between the processing parameters and the filtration performance of PLA MBs were explored in this study. The key parameters regarding the filtration performance of PLA MBs, including the PLA chip drying process, the melt temperature, the hot air temperature, and the width of the air gap, were thoroughly investigated using scanning electronic microscopy, filtration efficiency, and breathability tests. It was found that the processing parameters were significant to the structure, thus the filtration performance of PLA MBs. PLA turned out to be a favorable material for meltblowing. The preferred spinning temperature was 220°C for optimal web quality. The diameter of PLA MB fibers became larger with the increase of hot air temperature. With the increase of air gap width, the diameter of PLA MB fibers went up, whereas the crimp level went down. This information may be useful for the future development of a commercialized production line of PLA MBs.

Keywords

meltblowns (MBs)polylactic acid (PLA)process parameters performance

Get full access to this article

View all access options for this article.

References

Lu, F. , The Impact of Melt Blown and Spunbond Technologies on the Barrier Properties of SMS Fabrics, Tancon 06, 1-9 (2006).

Auras, R. , Harte, B. , and Selke, S. , An Overview of Polylactides as Packaging Materials, Macromol. Biosci., 4(9), 835-864 (2004).

Schmack, G. , Tandler, B. , Optiz, G. , Vogel, R. , Kornber, H. , Haussler, L. , Voigt, D. , Weinmann, S. , Heinernann, M. , Fritz H. G., High-speed Melt Spinning of Various Grades of Polylactides, J. Appl. Polym. Sci., 91(2), 800-806 ( 2004)

Park, C.H. , Hong, E.Y. , and Kang, Y.K. , Effects of Spinning Speed and Heat Treatment on the Mechanical Properties and Niodegradability of Poly(lactic acid) fibers, J. Appl. Polym. Sci., 103(5), 3099-3104 ( 2007).

Drumright, R.E. , Gruber, P.R. , and Henton, D.E. , Polylactic Acid Technology, Adv. Mater., 12(23), 1841-1846 (2000).

Dugan, J.S. , Novel Properties of PLA Fibers, Int. Non-wovens J., Fall, 29-33 ( 2001).

Kang, H.J. , Kang, D.W. , Chun, S.W. , and Kim, S.H. , Effect of Thermal Degradation on the Crystallization Behavior of Lpolylactic Acid in Melt Processing. Abstracts of papers of Amer. Chem. Soc., 221, 400 (2001).

Zhao, Y. , and Mai, H. , Biodegradable Poly (lactic acid) Non-woven, Tech. Text., 19(4), 31-33 (2001).

Qian, M. , The PLA Resin and Its Application on Non-wovens Production, Tech. Text., 23(9), 30-31 (2005).

10.

Geng, Q. , and Hu, X. , Characteristic of Polylactic Acid Fiber and Fabric Development, Cotton Text . Technol., 32(4), 62-64 ( 2004).

11.

Lunt, J. , PLA for Non-woven Applications, Tech. Text., 24(1), 18-22 (2006).

12.

Lunt, J. , Polylactic Acid Polymers for Fibers and Non-wovens, Int. Fib. J., June, 48-52 (2000).

13.

Dugan, J.S. , Novel Properties of PLA Fibers, Int. Nonwov. J., Fall, 29-33 (2001).

14.

Muller, D.H. , and Krobjilowski , A. , Meltblown Fabrics from Biodegradable Polymers, Int. Nonwov. J., Spring, 11-16 (2001).

15.

Zhou, R. , and Zhao, Y. , Study on Porosity Calculation Method for Non-wovens, Beijing Text. J., 23(3), 17-18 (2002).

16.

Sung Kayser , and Sung Max . , From Corn to Fabric, Text. Asia, 33(12), 6-8 (2002).

17.

http://www.natureworksllc.com/.

18.

Auras, R. , Harte, B. , and Selke S. , An Overview of Polylactides as Packaging Materials, Macromolec. Biosci., 4, 835-864 (2004).

19.

Qu, Y. , and Ke, Q. , The Investigation Progress on Melt-Blown Polylactic Acid Non-wovens, Tech. Text., 21(12), 1-5 ( 2003).

20.

Witzke, D.R. , Ph.D. Thesis, Michigan State University, East Lansing, MI 1997, 389.