Superhydrophobic and superoleophilic cotton fabric membrane with recycled ZnO for oil–water separation: particle size effect micrometric versus nanometric
Restricted accessResearch articleFirst published online March, 2026
Superhydrophobic and superoleophilic cotton fabric membrane with recycled ZnO for oil–water separation: particle size effect micrometric versus nanometric
This study demonstrates the synthesis of superhydrophobic and hydrophobic cotton fabric membranes, used for separating oil–water emulsions, by a simple immersion method with polydimethylsiloxane (PDMS) and zinc oxide (ZnO) from waste alkaline batteries. Scanning electron microscopy (SEM) analysis confirmed the effectiveness of ZnO/PDMS treatment, which increased the surface roughness and enhanced water contact angles (WCAs). The membranes treated with PDMS (5 g PDMS prepolymer, 0.5 g curing agent, 45 mL isopropyl alcohol) exhibited a WCA of 145 ± 1°, whereas those treated with PDMS and 1 g of ZnO (micro or nano) achieved WCAs of 145 ± 1° and 153 ± 1°, respectively. This difference is attributed to the low surface tension of the PDMS layer on the cotton fabric, combined with the surface roughness topography created by the ZnO micro- and nanostructures. Filtration tests showed that the membranes treated with only PDMS achieved >96% oil filtration and 94% water blockage, whereas ZnO/PDMS membranes maintained similar oil filtration efficiency but achieved 100% water blockage. These results highlight the potential of recycled ZnO in cotton fabric membranes for oil–water separation, with micro-ZnO offering a cost-effective and sustainable solution and nano-ZnO providing superhydrophobic behavior, both contributing to improved membrane performance in wastewater treatment applications.
YinZ, et al.
A superhydrophobic pulp/cellulose nanofiber (CNF) membrane via coating ZnO suspensions for multifunctional applications. Indust Crops Products2022;
187: 115526. doi: 10.1016/j.indcrop.2022.115526.
2.
PadakiM, et al.
Membrane technology enhancement in oil–water separation. A review. Desalination2015;
357: 197–207. doi: 10.1016/j.desal.2014.11.023.
3.
ZhangN, et al.
A review on oil/water emulsion separation membrane material. J Environ Chem Eng2022;
10(2): 107257. doi: 10.1016/j.jece.2022.107257.
4.
GaoXGuoZ.Biomimetic superhydrophobic surfaces with transition metals and their oxides: a review. J Bionic Eng2017;
14(3): 401–439. doi: 10.1016/S1672-6529(16)60408-0.
5.
WangB, et al.
Methodology for robust superhydrophobic fabrics and sponges from in situ growth of transition metal/metal oxide nanocrystals with thiol modification and their applications in oil/water separation. ACS Appl Mater Interf2013;
5(5): 1827–1839. doi: 10.1021/am303176a.
6.
KumarSSaharePDKumarS.Optimization of the CVD parameters for ZnO nanorods growth: its photoluminescence and field emission properties. Mater Res Bull2018;
105: 237–245. doi: 10.1016/j.materresbull.2018.05.002.
7.
LiuYChenWWeiSGaoW.TiO2/ZnO nanocomposite, ZnO/ZnO bi-level nanostructure and ZnO nanorod arrays: microstructure and time-affected wettability change in ambient conditions. RSC Adv2014;
4(58): 30658–30665. doi: 10.1039/C4RA04904G.
8.
RajanS, et al. Synthesis of ZnO nanoparticles by precipitation method: Characterizations and applications in decipherment of latent fingerprints. Mater Today Proc2023. doi: 10.1016/j.matpr.2023.05.680.
9.
XuBCaiZ.Fabrication of a superhydrophobic ZnO nanorod array film on cotton fabrics via a wet chemical route and hydrophobic modification. Appl Surf Sci2008;
254(18): 5899–5904. doi: 10.1016/j.apsusc.2008.03.160.
10.
FaisalMIsmailAAIbrahimAABouzidHAl-SayariSA.Highly efficient photocatalyst based on Ce doped ZnO nanorods: controllable synthesis and enhanced photocatalytic activity. Chem Eng J2013;
229: 225–233. doi: 10.1016/j.cej.2013.06.004.
11.
SalahN, et al.
High-energy ball milling technique for ZnO nanoparticles as antibacterial material. Int J Nanomed2011;
6: 863–869. doi: 10.2147/IJN.S18267.
12.
LeónCL, et al.
Synthesis by sol-gel and cytotoxicity of zinc oxide nanoparticles using wasted alkaline batteries. Digest J Nanomater Biostruct2017;
12: 371.
13.
TovarE. Preparacion y caracterizacion de peliculas delgadas de ZnO para su uso en estructuras vidrio/ITO/ZnO/CdS. 2013.
14.
SantiagoAAG, et al.
Development of ZnO/PDMS nanocomposite with photocatalytic/hydrophobic multifunction. Chem Phys Lett2020;
740: 137051. doi: 10.1016/j.cplett.2019.137051.
15.
BarthwalSSinghBBahadur SinghN.Multifunctional and fluorine-free superhydrophobic composite coating based on PDMS modified MWCNTs/ZnO with self-cleaning, oil–water separation, and flame retardant properties. Colloids Surfaces A2020;
597: 124776. doi: 10.1016/j.colsurfa.2020.124776.
16.
ZhangJSeegerS.Polyester materials with superwetting silicone nanofilaments for oil/water separation and selective oil absorption. Adv Funct Mater2011;
21(24): 4699–4704. doi: 10.1002/adfm.201101090.
17.
XuLZhangXShenYDingYWangLShengY.Durable superhydrophobic cotton textiles with ultraviolet-blocking property and photocatalysis based on flower-like copper sulfide. Ind Eng Chem Res2018;
57(19): 6714–6725. doi: 10.1021/acs.iecr.8b00254.
18.
XueC-HLiY-RHouJ-LZhangLMaJ-ZJiaS-T.Self-roughened superhydrophobic coatings for continuous oil–water separation. J Mater Chem A2015;
3(19): 10248–10253. doi: 10.1039/C5TA01014D.
19.
WenH, et al.
Robust super hydrophobic cotton fabrics functionalized with Ag and PDMS for effective antibacterial activity and efficient oil–water separation. J Environ Chem Eng2021;
9(5): 106083. doi: 10.1016/j.jece.2021.106083.
20.
WuZFangKChenWZhaoYXuYZhangC.Durable superhydrophobic and photocatalytic cotton modified by PDMS with TiO2 supported bamboo charcoal nanocomposites. Indust Crops Prod2021;
171: 113896. doi: 10.1016/j.indcrop.2021.113896.
21.
YuLRuanSXuXZouRHuJ.One-dimensional nanomaterial-assembled macroscopic membranes for water treatment. Nano Today2017;
17: 79–95. doi: 10.1016/j.nantod.2017.10.012.
22.
XueC-HJiaS-TChenH-ZWangM.Superhydrophobic cotton fabrics prepared by sol-gel coating of TiO2 and surface hydrophobization. Sci Technol Adv Mater2008;
9(3): 035001. doi: 10.1088/1468-6996/9/3/035001.
23.
LiKZengXLiHLaiXXieH.Facile fabrication of superhydrophobic filtration fabric with honeycomb structures for the separation of water and oil. Mater Lett2014;
120: 255–258. doi: 10.1016/j.matlet.2014.01.105.
24.
FoorginezhadSAsadniaM.Superhydrophobic Al2O3/MMT-PDMS coated fabric for self-cleaning and oil–water separation application. Langmuir2023;
39(50): 18311–18326. doi: 10.1021/acs.langmuir.3c02325.
GaoXWenGGuoZ.Durable superhydrophobic and underwater superoleophobic cotton fabrics growing zinc oxide nanoarrays for application in separation of heavy/light oil and water mixtures as need. Colloids Surfaces A2018;
559: 115–126. doi: 10.1016/j.colsurfa.2018.09.041.
27.
YangPYangJWuZZhangXLiuYLuM.Facile fabrication of superhydrophilic and underwater superoleophobic surfaces on cotton fabrics for effective oil/water separation with excellent anti-contamination ability. Colloids Surfaces A2021;
628: 127290. doi: 10.1016/j.colsurfa.2021.127290.
28.
QianS, et al.
APT-Conjugated PDMS-ZnO/Ag-based multifunctional integrated superhydrophobic biosensor with high SERS activity and photocatalytic sterilization performance. Int J Mol Sci 2024;25(14): 7675. doi: 10.3390/ijms25147675.
29.
ZhangMWangCWangSLiJ.Fabrication of superhydrophobic cotton textiles for oil–water separation based on drop-coating route. Carbohydr Polym2013;
97(1): 59–64. doi: 10.1016/j.carbpol.2012.08.118.
30.
WuJChenJQasimKXiaJLeiWWangB.A hierarchical mesh film with superhydrophobic and superoleophilic properties for oil and water separation. J Chem Technol Biotechnol2012;
87(3): 427–430. doi: 10.1002/jctb.2746.
31.
TianDZhangXWangXZhaiJJiangL.Micro/nanoscale hierarchical structured ZnO mesh film for separation of water and oil. Phys Chem Chem Phys2011;
13(32): 14606–14610. doi: 10.1039/C1CP20671K.
32.
AhmedFUPurkayasthaDD.PVDF@ZnO membrane for its potential application in oil/water separation. Mater Today Proc2022;
68: 177–180. doi: 10.1016/j.matpr.2022.07.236.
33.
NguyenTXQChenS-SPasawanMLeHQChangH-MNguyenNC.Separation of used automobile oil/water mixture by Nylon 6/ZnO nanoparticles electrospun membrane. Separation Purification Technol2022;
298: 121578. doi: 10.1016/j.seppur.2022.121578.
34.
XuDGongMLiSZhuXKongXZ.Fabrication of superhydrophobic/oleophilic membranes by chemical modification of cellulose filter paper and their application trial for oil–water separation. Cellulose2020;
27(11): 6093–6101. doi: 10.1007/s10570-020-03261-z.
35.
ZhouY, et al.
PDMS mesh with reversible super-wettability for oil/water separation. Colloids Surfaces A2022;
641: 128462. doi: 10.1016/j.colsurfa.2022.128462.
36.
van HazendonkJMvan der PuttenJCKeurentjesJTFPrinsA.A simple experimental method for the measurement of the surface tension of cellulosic fibres and its relation with chemical composition. Colloids Surfaces A1993;
81: 251–261. doi: 10.1016/0927-7757(93)80252-A.
37.
WangT, et al.
A compound of ZnO/PDMS with photocatalytic, self-cleaning and antibacterial properties prepared via two-step method. Appl Surf Sci2021;
550: 149286. doi: 10.1016/j.apsusc.2021.149286.
38.
HolderCFSchaakRE.Tutorial on powder X-ray diffraction for characterizing nanoscale materials. ACS Nano2019;
13(7): 7359–7365. doi: 10.1021/acsnano.9b05157.
39.
ZhaoBYueXTianQQiuFZhangT.Controllable fabrication of ZnO nanorods@cellulose membrane with self-cleaning and passive radiative cooling properties for building energy-saving applications. Cellulose2022;
29(3): 1981–1992. doi: 10.1007/s10570-021-04408-2.
40.
UgurŞSSariişikMAktaşAH.The fabrication of nanocomposite thin films with TiO2 nanoparticles by the layer-by-layer deposition method for multifunctional cotton fabrics. Nanotechnology2010;
21(32): 325603. doi: 10.1088/0957-4484/21/32/325603.
41.
KüçükMÖveçoğluML.Fabrication of SiO2–ZnO NP/ZnO NR hybrid coated cotton fabrics: the effect of ZnO NR growth time on structural and UV protection characteristics. Cellulose2020;
27(3): 1773–1793. doi: 10.1007/s10570-019-02891-2.
42.
El-NahhalIMElmanamaAAAmaraNQodihFSSelmaneMChehimiMM.The efficacy of surfactants in stabilizing coating of nano-structured CuO particles onto the surface of cotton fibers and their antimicrobial activity. Mater Chem Phys2018;
215: 221–228. doi: 10.1016/j.matchemphys.2018.05.012.
43.
HamouniSArousOAbdessemedDNezzalGVan der BruggenB.Alcohol and alkane organic extraction using pervaporation process. Macromol Symp2019;
386(1): 1800247. doi: 10.1002/masy.201800247.
Miranda OlmedoNA. Efecto de las nanopartículas en la inyección de agua con baja salinidad como un método novedoso de recuperación mejorada: Alteración de la humectabilidad, 2017. Available at: https://repositorio.unal.edu.co/handle/unal/63464
46.
PakdelEKashiSSharpJWangX.Superhydrophobic, antibacterial, and EMI shielding properties of Ag/PDMS-coated cotton fabrics. Cellulose2024;
31(6): 3921–3946. doi: 10.1007/s10570-024-05819-7.