Effect of Corona Discharge on the Surface of Wool and Its Application to Printing

Abstract

Corona discharge has been widely used to modify polymer surfaces because it can be operated at an atmospheric pressure in air. In this study, wool fiber and fabric were corona discharged, and afterwards wettability, laundry shrinkage, and frictional coef ficients were determined. An ESCA analysis was done to elucidate the changes of chemical composition on the fiber surface. The corona discharge incorporates oxygen atoms into the fiber and increases wettability and laundry shrink resistance of wool fabrics, but the effects are smaller than those from low temperature O₂ plasma. After the pretreatment with corona discharge, the fabric was printed with color pastes of two acid dyes, and then treated with superheated or high pressure steam. The corona discharge pretreatment, in particular the single pretreatment, improved color depth considerably, which increased in the following order: untreated ≃O₂ plasma treatment < three-fold corona discharge < single corona discharge. From these results it is likely that a small change in hydrophilic properties on the fiber surface plays an important role in improving the color depth of wool fabric in printing.

Get full access to this article

View all access options for this article.

References

Anderson, C.A. , Belin, R.E. , Feldman , H.D. , and Goldsmith , M.T. , Einfluss von Polyamid-Epichlorhydrin auf Vorbehandelte Kammzugwickel bei der Filzfrei-Ausrustung von Wolle, Textileveredlung 5, 846-854 (1970).

Bateup, B.O. , Feldtman, H.D. , and Fleischfresser , B.F. , The Application of Shrink-resist Polymers to Wool Pre-treated in a Corona-Discharge , J. Textile Inst. 72, 34-39 (1981).

Belin, R.E. , Hayes, R.L. , and Mutsaerts, G. , Electrical Discharge Treatment of Wool at Atmospheric Pressure, J. Textile Inst. 74, 191-195 (1983).

Bhalla, G.L. , and Nigam, J.K. , Grafting Methacrylate on DC-Corona and Chemically Pretreated Wool Fabric, Textile Res. J. 75, 585-586 (1986).

Bhalla, G.L. , Nigam, J.K. , and Pillai, P.K.C. , Effect of Corona and Oxidation Pretreatments on Grafting in Wool Fabric, Textile Res. J. 85, 254-255 (1985).

Gregorski, K.S. , and Pavlath, A.E. , Fabric Modification Using the Plasmod, The Effect of Extensive Treatment in Nitrogen and Oxygen Plasmas at Low Pressure , Textile Res. J. 50, 42-46 (1980).

Millard, M.M. , and Pavlath, A.E. , Surface Analysis of Plasma-Polymerized Fluorocarbon Films by X-Ray Photoelectron Spectrometry , J. Macromol. Sci. Chem. A10 (3), 579-597 (1976).

Pavlath, A.E. , and Lee, K.S. , "Plasma Chemistry of Polymer ," Marcel Dekker, Inc., New York , 1976 , pp. 251-262.

Pavlath, A.E. , and Slater, R.F. , Low Temperature Plasma Chemistry, I: Shrinkproofing of Wool, Appl. Polym. Sym., no. 18, 1317-1324 (1971).

10.

Ryu, J. , Wakida, T. , Kawamura, H. , Goto, T. , and Takagishi, T. , Frictional Coefficient of Wool Treated with Low Temperature Plasma , Sen-i Gakkaishi 43, T257-T262 ( 1987).

11.

Ryu, J. , Wakida, T. , Kawamura, H. , Goto, T. , and Takagishi, T. , Dyeing Properties of Wool Treated with Low Temperature Plasma, Chem . Express 2, 377-380 (1987).

12.

Thorsen, W.J. , and Kodani, R.Y. , A Corona Discharge Method of Producing Shrink-Resistant Wool and Mohair, Textile Res. J. 36, 651-661 (1966).

13.

Thorsen, W.J. , A Corona Discharge Method of Producing Shrink-Resistant Wool and Mohair, Part 11: Effect of Temperature, Chlorine Gas, and Moisture , Textile Res. J. 38, 644-650 ( 1968).

14.

Wakida, T. , Kawamura, H. , Song, J. , Goto, T. , and Takagishi, T. , Surface Free Energy of Poly(ethylene Terephthalate) and Nylon 6 Films Treated with Low Temperature Plasma, Sen-i Gakkaishi 43, 384-389 (1987).