Synthesis of Poly(lactide) Blends by Melt/Solid Polycondensation

Abstract

Different blend compositions of amorphous poly(D,L-lactic acid) (PDLLA) and crystalline poly(L-lactic acid) (PLLA) of various molecular weights are prepared in one step by melt/solid polycondensation in the presence of different concentrations of either SnCl₂·2H₂O/p-toluene sulfonic acid (PTSA) 1 : 1 or Sb₂O₃ as a catalyst. The prepared blends are characterized using differential scanning calorimeter (DSC) and gel permeation chromatography (GPC). The results confirm that using a monomer source in the form of a non-racemic D,L-lactic acid mixture leads to PLA containing both amorphous (DL-based) PLA and crystalline (L-based) PLA. In addition, the polymers prepared in the presence of Sb₂O₃ as a catalyst acquire higher molecular weights (two- or three-fold) with respect to the comparable polymers prepared from a pure L-lactic acid source. The molecular weight measurements of the samples after exposure to degradation medium (phosphate buffer pH 7.4 at 37^°C) prove that the degradation occurs preferentially in the amorphous part.

Keywords

biodegradable poly(lactide)blends polycondensation.

Get full access to this article

View all access options for this article.

References

Quesnel, R. and Hildgen, P. (2005). Synthesis of PLA-b-PEG Multiblock Copolymers for Stealth Drug Carrier Preparation, Molecules, 10: 98—104.

Tsuji, H. and Ikada, Y. (1999). Physical Properties of Polylactides, Current Trends in Polymer Science, 4: 27—46.

Ikada, M. , Jamshidi, K. , Tsuji, H. and Hyon, S. (1987). Stereocomplex Formation Between Enantiomeric Poly(lactides) , Macromolecules, 20: 904—906.

Tsuji, H. and Ikada, M. (1996). Crystallization from the Melt of Poly(lactide)s with Different Optical Purities and their Blends, Macromol. Chem. Phys., 197: 3483—3499.

Sarasua, J.R. , Prud'homme, R.E. , Wisniewski, M. , Le Borgne, A. and Spassky, N. (1998). Crystallization and Melting Behavior of Polylactides, Macromolecules, 31: 3895—3905.

Grizzi, I. , Gareau, H. , Li, S. and Vert, M. (1995). Hydrolytic Degradation of Devices based on Poly(DL-Lactic acid) Size-dependence, Biomaterials, 16(4): 305—311.

Huang, J. , Lisowski, M. , Runt, J. , Hall, E. , Kean, R. , Buehler, N. and Lin, J. (1998). Crystallization and Microstructure of Poly(L-lactide-co-mesolactide) Copolymers, Macromolecules, 31: 2593—2599.

Grijpma, D.W. and Pennings, A.J. (1994). Copolymers of L-lactide, 1. Synthesis, Thermal Properties and Hydrolytic Degradation, Macromol. Chem. Phys., 195: 1633—1647.

Spinu, M. , Jackson, C. , Keating, M.Y. and Gardner, K.H. (1996). Material Design in Poly(Lactic Acid) Systems: Block Copolymers, Star Homo- and Copolymers, and Stereocomplexes, J. M. S . Pure Appl. Chem., A33: 1497—1530.

10.

Kolstad, J.J. (1996). Crystallization Kinetics of Poly(L-lactide-co-mesolactide), J. Appl. Polym. Sci., 62: 1079—1091.

11.

Moon, S.I. , Lee, C.W. , Taniguchi, I. , Miyamoto, M. , Kimura, Y. (2001). Melt/solid Polycondensation of L-lactic acid: An Alternative Route to Poly(L-lactic acid) with High Molecular Weight, Polymer, 42(11): 5059—5062.

12.

Mohammadi-Rovshandeh, J. , Farnia, S.M.F. and Sarbolouki , M.N. (2002). Synthesis and Characterization of ABA Triblock and Novel Multiblock Copolymers from Ethylene Glycol, L-lactide, and ε-caprolactone, J. Appl. Polym. Sci., 83: 2072—2081.

13.

Piao, L.H. , Deng, M.X. , Chen, X.S. , Jiang, L.S. and Jing, X.B. (2003). Ring-opening Polymerization of ε-caprolactone and L-lactide using Organic Amino Calcium Catalyst, Polymer , 44: 2331—2336.