Nanocomposites were prepared by melt mixing in a twin-screw extruder 5% by weight of Cloisite® Na+, 15A or 30B, with an ethylene vinyl acetate/poly(vinyl chloride) (EVA/PVC) blend (90/10% by weight). The dispersion was assessed by X-ray diffraction (XRD), transmission electron microscopy (TEM), oscillatory rheometry, and dynamic mechanical analysis (DMA). XRD and TEM analyses revealed an intercalated morphology and an exfoliated morphology for the composites containing Cloisite 15A and 30B, respectively. Rheometrical and DMA data demonstrated that the presence of PVC in the blend not only improved the interaction with Cloisite 30B but also acted as a mechanical reinforcement.
RivaAZanettiMBragliaM. Thermal degradation and rheological behaviour of EVA/montmorillonite nanocomposites. Polym Deg Stab2002; 77: 299–304.
2.
HeHMaYZhuJ. Organoclays prepared from montmorillonites with different cation exchange capacity and surfactant configuration. App Clay Sci2010; 48: 67–72.
3.
MariniJBrancifortiMCLottiC. Effect of matrix viscosity on the extent of exfoliation in EVA/organoclay nanocomposites. Polym Adv Technol2010; 21: 408–417.
4.
ZhangWChenDZhaoQ. Effects of different kinds of clay and different vinyl acetate content on the morphology and properties of EVA/clay nanocomposites. Polym2003; 44: 7953–7961.
5.
La MantiaFPTzankova DintchevaN. Eva copolymer-based nanocomposites: rheological behavior under shear and isothermal and non-isothermal elongational flow. Polym Test2006; 25: 701–708.
6.
ChaudharyDSPrasadRGuptaRK. Morphological influence on mechanical characterization of ethylene-vinyl acetate copolymer–clay nanocomposites. Polym Eng Sci2005; 45: 889–897.
7.
ZujoVPGuptaRKBhattacharyaSN. Effect of vinyl acetate content and silicate loading on EVA nanocomposites under shear and extensional flow. Rheol Acta2004; 43: 99–108.
8.
PistorVOrnaghiHLJrFerreiraCA. Performance of poly(ethylene-co-vinyl acetate) nanocomposites using distinct clays. J App Polym Sci2011; 125: 462–470.
9.
HernándezRPeñaJJIrustaL. The effect of a miscible and an immiscible polymeric modifier on the mechanical and rheological properties of PVC. Eur Polym J2000; 36: 1011–1025.
10.
RighettiMCCardelliCScalariM. Thermodynamics of mixing of poly(vinyl chloride) and poly(ethylene-co-vinyl acetate). Polym2002; 43: 5035–5042.
11.
KelarakisAGiannleisEPYoonK. Structure–properties relationships in clay nanocomposites based on PVDF/(ethylene–vinyl acetate) copolymer blends. Polym2007; 48: 7567–7572.
RothsTMarthMWeeseJ. A generalized regularization method for nonlinear ill-posed problems enhanced for nonlinear regularization terms. Comp Phys Commun2001; 139: 279–296.
14.
PistorVLizotAFiorioR. Influence of physical interaction between organoclay and poly(ethylene-co-vinyl acetate) matrix and effect of clay content on rheological melt state. Polym2010; 51: 5165–5171.
15.
PistorVChiesaAOrnaghiHLJr. Influence of processing conditions on productivity, thermal and rheological properties of reprocessed low density polyethylene. Int Polym Proc2011; 26: 383–387.
16.
GonzálezOMuñozMESantamaríaA. Rheology and stability of bitumen/EVA blend. Eur Polym J2004; 40: 2365–2372.
17.
HyunYHLimSTChoiH. Rheology of poly(ethylene oxide)/organoclay nanocomposites. Macromolecules2001; 34: 8084–8093.
18.
WilkesCESummersJWDanielsCA. PVC handbook. Munich, Germany: Carl Hanser Verlag, 2005.
19.
YamakiSBPradoEAAtvarsTDZ. Phase transitions and relaxation processes in ethylene-vinyl acetate copolymers probed by fluorescence spectroscopy. Eur Polym J2002; 38: 1811–1826.
20.
MatuanaLM. Rigid PVC (layered silicate) nanocomposites produced through a novel melt-blending approach. J Vinyl Addit Technol2009; 15: 77–86.