Lead-free (Na,K)(Nb,Ta)O3 (KNNT) piezoelectric single crystal has been successfully grown using the top-seeded solution growth technique. The electromechanical coupling factors are very high (k33 = 0.827, kt = 0.646), and the dielectric loss tangent is as low as 0.004. Acoustic impedance was calculated to be 26.5 MRayl. From the single crystal, a single element transducer was fabricated. The transducer achieved a 57.6% −6 dB bandwidth and 32.3 µm axial resolution at the center frequency of 45.4 MHz, which can identify the cornea of porcine eyeball with high resolution. Comparison between KNNT single crystal and lead-based single crystal was discussed. The results suggest that this single crystal transducer is an excellent candidate to replace lead-containing transducer for high-frequency ultrasonic imaging applications.
TurnbullDHStarkoskiBGHarasiewiczKASempleJLFromLGuptaAKet al. A 40-100 MHz B-scan ultrasound backscatter microscope for skin imaging. Ultrasound Med Biol. 1995;21:79-88.
7.
ColemanDJSilvermanRHChabiARondeauMJShungKKCannataJet al. High-resolution ultrasonic imaging of the posterior segment. Ophthalmology. 2004;111:1344-51.
8.
LiXMaTTianJHanPZhouQShungKK. Micromachined PIN-PMN-PT crystal composite transducer for high-frequency intravascular ultrasound (IVUS) imaging. IEEE Trans Ultrason Ferroelectr Freq Control. 2014;61:1171-8.
9.
ShungKK. High frequency ultrasonic imaging. J Med Ultrasound. 2009;17:25-30.
10.
CannataJMWilliamsJAZhouQRitterTAShungKK. Development of a 35-MHz piezo-composite ultrasound array for medical imaging. IEEE Trans Ultrason Ferroelectr Freq Control. 2006;53:224-36.
11.
ChandranaCTalmanJPanTRoySFleischmanA. Design and analysis of MEMS based PVDF ultrasonic transducers for vascular imaging. Sensors. 2010;10:8740-50.
12.
ZhouQXuXGottliebEJSunLCannataJMAmeriHet al. PMN-PT single crystal, high-frequency ultrasonic needle transducers for pulsed-wave Doppler application. IEEE Trans Ultrason Ferroelectr Freq Control. 2007;54:668-75.
13.
PengJLauSChaoCDaiJChanHLuoHet al. PMN-PT single crystal thick films on silicon substrate for high-frequency micromachined ultrasonic transducers. Appl Phys A Mater Sci Process. 2010;98:233-7.
14.
HollensteinEDavisMDamjanovicDSetterN. Piezoelectric properties of Li- and Ta-modified (K0.5Na0.5)NbO3 ceramics. Appl Phys Lett. 2005;87:182905.
15.
ShroutTRZhangSJ. Lead-free piezoelectric ceramics: alternatives for PZT?J Electroceram. 2007;19:113-26.
16.
XuYYuQLiJ-F. A facile method to fabricate vertically aligned (K,Na)NbO3 lead-free piezoelectric nanorods. J Mater Chem. 2012;22:23221-6.
17.
FisherJGBenc̆anAKosecMVernaySRytzD. Growth of dense single crystals of potassium sodium niobate by a combination of solid-state crystal growth and hot pressing. J Am Ceram Soc. 2008;91:1503-7.
18.
ChenKXuGYangDWangXLiJ. Dielectric and piezoelectric properties of lead-free 0.95(K0.5Na0.5)NbO3 0.05LiNbO3 crystals grown by the Bridgman method. Jpn J Appl Phys. 2007;101:044103.
19.
ZhengLHuoXWangRWangJJiangWCaoW. Large size lead-free (Na,K)(Nb,Ta)O3 piezoelectric single crystal: growth and full tensor properties. CrystEngComm. 2013;15:7718-22.
20.
ZhouQLamKHZhengHQiuWShungKK. Piezoelectric single crystals for ultrasonic transducers in biomedical applications. Prog Mater Sci. 2014;66:87-111.
21.
ChenYJiangXPLuoHSDaiJYChanHL. High-frequency ultrasonic transducer fabricated with lead-free piezoelectric single crystal. IEEE Trans Ultrason Ferroelectr Freq Control. 2010;57(11):2601-4.
22.
DesiletsCSFraserJDKinoGS. The design of efficient broad band piezoelectric transducers. IEEE T Son Ultrason. 1978;25(3):115-25.
23.
LamKHJiHFZhengFRenWZhouQShungKK. Development of lead-free single-element ultrahigh frequency (170–320 MHz) ultrasonic transducers. Ultrasonics. 2013;53:1033-8.