Catalytic Decomposition of H 2 O 2 over Pure and Li 2 O-Doped Co 3 O 4 Solids

Pure and doped Co₃O₄ samples were prepared by the thermal decomposition at 500–900°C of pure and lithium nitrate-treated basic cobalt carbonate. The amounts of dopant added were varied in the range 0.75–6 mol% Li₂O. The effects of this treatment on the surface and catalytic properties of cobaltic oxide solid were investigated using nitrogen adsorption at −196°C and studies of the decomposition of H₂O₂ at 30–50°C.

The results obtained revealed that Li₂O doping of Co₃O₄ followed by heat treatment at 500°C and 600°C resulted in a progressive increase in the value of the specific surface area, S_BET, to an extent proportional to the amount of dopant present. However, the increase was more pronounced in the case of solid samples calcined at 500°C. This increase in the specific surface areas has been attributed to the fixation of a portion of the dopant ions on the uppermost surface layers of the solid leading to outward growth of the surface lattice. The observed increase in S_BET due to Li₂O doping at 500°C might also result from a narrowing of the pores in the treated solid as a result of the doping process. Lithium oxide doping of cobaltic oxide followed by heat treatment at 700–900°C resulted in a significant decrease in the S_BET, V_p and r̄ values. Pure and doped solids precalcined at 500°C and 600°C exhibited extremely high catalytic activities which were not much affected by doping with Li₂O. On the other hand, doping followed by calcination at 700–900°C brought about a considerable and progressive increase in the catalytic activity of the treated solids. This treatment did not modify the activation energy of the catalysed reaction, i.e. doping of Co₃O₄ solid followed by heating at 700°C and 900°C did not alter the mechanism of the catalytic reaction but increased the concentration of catalytically active constituents taking part in the catalytic process without altering their energetic nature.