The effect of yttrium on the mechanism of oxidation film formation of the 9Cr reduced activation ferritic/martensitic (9Cr-RAFM) steel was investigated. Four alloys yttrium contents ranging from 0 to 0.065% were melted in a vacuum induction furnace and subjected to continuous isothermal oxidation experiments. The alloys were oxidized in air at 600, 700, 800 and 900 °C for 100 h. Oxidation kinetic curves were obtained and analyzed to study the effect of yttrium on the oxidation resistance of the alloys at high temperatures. The oxide films formed on the alloys were observed and analyzed by X-ray diffractometry, scanning electron microscopy and electron probe X-ray microanalysis. The results indicated that the oxidation weight gain of the samples varied with the yttrium content, with the highest gain observed in the yttrium-free alloy sample, and the least in those containing 0.065% yttrium. Adding yttrium significantly enhanced the high temperature oxidation resistance of 9Cr-RAFM alloy by promoting the formation of a selective Cr2O3 oxide film. The film improved the adhesion of the oxide layer to the base metal, reduced the oxidation rate, and thereby enhanced the high-temperature oxidation resistance of the alloy.
QiuGXZhanDPCaoL,et al.Review on development of reduced activated ferritic/martensitic steel for fusion reactor. J Iron Steel Res Int2022; 29: 1343–1356.
2.
BloomEEConnRWDavisJW, et al.Low activation materials for fusion applications. J Nucl Mater1984; 122: 17–26.
3.
QiuGXZhanDPCaoL, et al.Effect of zirconium on inclusions and mechanical properties of China low activation martensitic steel. J Iron Steel Res Int2021; 28: 1168–1179.
4.
KiranaRRajuSMythiliR, et al.High-Temperature phase stability of 9Cr-W-Ta-V-C based reduced activation ferritic-martensitic (RAFM) steels: effect of W and Ta additions. Steel Res Int2015; 86: 825–840.
5.
EmmerichK. Properties of rapidly solidified FeCrAl ribbons for the use as automotive exhaust gas catalyst substrates. Phys Status Solidi A1993; 135: 381–389.
6.
KlöwerJ. Factors affecting the oxidation behaviour of thin Fe-Cr-Al foils part I: effect of foil dimensions. Mater Corros1998; 49: 758–763.
7.
ZhengZWangSLongJ, et al.Effect of rare earth elements on high temperature oxidation behaviour of austenitic steel. Corros Sci2020; 164: 108359.
8.
PintBA. Experimental observations in support of the dynamic-segregation theory to explain the reactive-element effect. Oxid Met1996; 45: 1–37. doi:https://doi.org/10.1007/BF01046818.
JiaBSXuWJLiJF, et al.Enhancement of thermal stability and high-temperature oxidation resistance of chromium oxide-based films by addition of rare earth element Y. J Mater Sci Technol2024; 188: 105–115.
11.
SilvaRYoungDJMartins JuniorCB, et al.Role of cerium addition in enhancing the oxidation resistance of austenitic Fe-Mn-Si-Cr-Ni shape memory stainless steels at 800 °C: microstructure and oxidation mechanism. Corros Sci2022; 209: 110788.
12.
LiJCaoGWangH, et al.Size effects of Y-enriched intermetallic precipitates in Fe-20Cr-5Al-0.25Y alloy on the spallation resistance of thermally grown α-Al2O3 scales. Corros Sci2020; 174: 108796.
13.
MennickeCHeMYClarkeDR,et al.The role of secondary oxide inclusions (“pegs”) on the spalling resistance of oxide films. Acta Mater2000; 48: 2941–2949.
JedlińskiJGrosseau-PoussardJLKowalskiK, et al.Development of oxide scale at 1,100 °C on Fe20Cr5Al alloy non-implanted and yttrium-implanted. Oxid Met2013; 79: 41–51.
16.
JawańskaMDąbrowaJBikM, et al.Role of the rare-earth elements effect in transforming the oxidation behavior of AlxCoCrFeNi high entropy alloys. Corros Sci2023; 222: 111412.
17.
FountainJGGolightlyFAStottFH,et al.The influence of platinum on the maintenance of α-Al2O3 as a protective scale. Oxid Met1976; 10: 341–345.
18.
PillisMFCorreaOVRamanathanLV. High temperature oxidation behavior of yttrium dioxide coated Fe-20Cr alloy. Mat Res2016; 19: 611–617. doi:https://doi.org/10.1590/1980-5373-MR-2015-0393.
19.
QiuGXWeiXLBaiC, et al.Inclusion and mechanical properties of ODS-RAFM steels with Y, Ti, and Zr fabricated by melting. Nucl Eng Technol2022; 54: 2376–2385.
20.
Sukhjindersingh, GoyalKGoyalR. Performance of Cr3C2-25(Ni-20Cr) and Ni-20Cr coatings on T91 boiler tube steel in simulated boiler environment at 900 °C. Chem Mater Eng2016; 4: 57–64.
21.
WuLYangGXuY. High-temperature oxidation resistance behavior of porous Ni-16Cr-9Al materials. Int J Mater Res2019; 110: 969–978.
22.
QiuGXZhanDPLiCS, et al.Effects of yttrium on microstructure and properties of reduced activation ferritic-martensitic steel. Mater Sci Tech-Lond2018; 34: 2018–2029.
23.
QiuGXZhanDPLiCS, et al.Effects of electroslag remelting process and Y on the inclusions and mechanical properties of the CLAM steel. Nucl Eng Technol2019; 52: 811–818.
24.
LiTF. High-temperature oxidation and thermal corrosion of metals. Beijing: Industrial Equipment and Information Engineering Publishing Center of Chemical Industry Press, 2003, pp.4–171.
BirksNMeierGHPettitFS. Introduction to high-temperature oxidation of metals. Beijing: Higher Education Press, 2010.
27.
LiuDRuiHLiJ, et al.Isothermal oxidation behavior of haynes 230 alloy in air at 1100 °C. Rare Metal Mat Eng2008; 37: 1545–1548.
28.
GoyalKSinghHBhatiaR. Cyclic high temperature corrosion studies of carbon nanotubes-Cr2O3 composite coatings on boiler steel at 900°C in molten salt environment. Anti-Corros Method M2018; 65: 646–657.
29.
WeiserMGaletzMCZschauHE, et al.Influence of Co to Ni ratio in γ′-strengthened model alloys on oxidation resistance and the efficacy of the halogen effect at 900 °C. Corros Sci2019; 156: 84–95.
30.
ZhaoXSZhouCG. Effect of Y2O3 content in the pack on microstructure and hot corrosion resistance of Y-Co-modified aluminide coating. Corros Sci2014; 86: 223–230.
31.
RamanathanLV. Role of rare-earth elements on high temperature oxidation behavior of Fe Cr, Ni Cr and Ni Cr Al alloys. Corros Sci1993; 35: 871–878.