The Influence of the Concentration of an ‘n-butyllithium–amine-containing Modifier’ Initiating System on the Copolymerisation of 1,3-butadiene and Styrene

Abstract

The influence of the concentration of an initiating system consisting of n-butyllithium and an amine-containing modifier on the copolymerisation of 1,3-butadiene and styrene in a hexane solvent was studied. The molecular characteristics and the microstructure of specimens of the obtained solution-polymerised styrene butadiene rubber (s-SBR) were determined by gel permeation chromatography on a Breeze liquid chromatograph (Waters) and by IR spectroscopy on a Spectrum GX 100 spectrometer (PerkinElmer) in accordance with ISO 21561/2. It was shown that a reduction in the amount of the initiating system is accompanied with a reduction in the copolymerisation rate and in the monomer conversion, and also with an increase in the average molecular weights of the copolymer. It was established that a reduction in the initiating system concentration in the reaction medium leads to a reduction in the content of 1,2-units in the rubber. A comparative analysis of data for rubber compounds based on the synthesised s-SBR and data for rubber compounds based on standard rubber indicates that their mechanical properties are at the same level. However, the tg δ at 60°C (determined on an RPA 2000 instrument) for rubber compounds based on a trial specimen has a lower value, which will make it possible to produce tyre rubbers providing a lower tyre rolling resistance.

References

Kuperman

F.E.

, New Tyre Rubbers. Solution-polymerised Rubbers with an Increased Content of Vinyl Units: Alternatives to Emulsion-polymerised SBRs. Trans-Polymers and Copolymers of Isoprene and Butadiene. NIIShP, Moscow, 367 pp. (2011).

Monakov

Yu.B.

, and Tolstikov

G.A.

, The Catalytic Polymerisation of 1,3-Dienes. Nauka, Moscow, 211 pp. (1990).

Hsieh

H.L.

, and Quirk

R.P.

, Anionic Polymerisation: Principles and Practical Applications. Marcel Dekker, New York, NY, 727 pp. (1996).

Quirk

R.P.

, Anionic synthesis of chain-end functionalized polymers. Makromol. Chem., (32): 47 (1990).

Patil

A.O.

, Functional Polymers: Modern Synthetic Methods and Novel Structures. American Chemical Society, Washington, DC, 348 pp. (1998).

Vagizov

A.M.

, The copolymerisation of 1,3-butadiene and styrene using n-butyllithium in the presence of an amine-containing modifier in hexane. Zh. Prikl. Khim., 89(1): 95 (2016).

Shvarts

, Anionic Polymerisation. Mir, Moscow, 690 pp. (1971).

Isakova

N.A.

, Monitoring of the Production of Synthetic Rubbers. Khimiya, Leningrad, 240 pp. (1980).

Russian Application 2015128922, from 17.07.2015.

10.

Galimova

E.M.

, The influence of the molecular weights and viscosity of solution-polymerised styrene butadiene rubber on the properties of rubber mixes and vulcanisates filled with a silica filler. Kauch. i Rezina, (3): 4 (2014).

11.

Nikolaev

N.I.

, The polymerisation of isoprene and butadiene using insoluble organolithium compounds. Vys. Soed., 5(6): 811 (1963).

12.

Vinogradova

L.V.

, The nature and reactivity of active centres in the ‘butadiene–n-butyllithium–tetramethylethylenediamine–carbon medium’ system. Vys. Soed., A18(8): 1756 (1976).

13.

Akhmetov

I.G.

, The polymerisation kinetics and molecular characteristics of ‘lithium polybutadiene’: the influence of the concentration of monomer and initiating system. Kauch. i Rezina, (6): 2 (2009).

14.

Hesterwerth

, Classification of polar additives with respect to their influence on the microstructure in anionic polymerization of butadiene with butyllithium by transition energy measurements. J. Appl. Polym. Sci., 73: 1521 (1999).

15.

Kuperman

F.E.

, New Tyre Rubbers. Priority Requirements. Assessment Methods. NIIShP, Moscow, 329 pp. (2005).