Application and Evaluation of Micro-Cracking on Cement-Stabilized Bases at Field Projects in Louisiana

Abstract

Cement stabilized soil bases have been used in flexible pavements in Louisiana for years. Soil cement has an excellent load carrying capacity and durability, but is also well-known for developing shrinkage cracks, which can reflect through asphalt concrete surfaces and accelerate the deterioration of asphalt pavements. Micro-cracking is a special reflective cracking mitigation technique used in cement-stabilized base construction. The objectives of the research were to determine the effectiveness and performance of micro-cracking on soil-cement pavements. Micro-cracking was applied on field projects, based on the experience of a previous micro-cracking research project at the Pavement Research Facility of the Louisiana Department of Transportation and Development. Two pavement sites were selected for the field pavement rehabilitation projects, LA 1003 and LA 599, to test the micro-cracking technique. In-situ tests were conducted and pavement performance was monitored for both sites. It was found that an 8.5-in. micro-cracked soil cement pavement showed a similar or better early performance as compared to a non-micro-cracked soil cement pavement with regards to the overall cracking performance. On the other hand, more cracks were found on the micro-cracked test sections than the control sections when micro-cracking was applied on a 12-in. cement treated soil base in Louisiana. Analysis of the structural numbers did not show a significant difference between the control and micro-cracked sections. Further monitoring is recommended for both of the field projects.

Get full access to this article

View all access options for this article.

References

Litzka

Haslehner

Cold In-Place Recycling on Low-Volume Roads in Austria. Proc., 6th International Conference on Low Volume Roads, Minneapolis, Minn., 1995, pp. 189–194.

Thøgersen

Busch

Henrichsen

Mechanistic Design of Semi-Rigid Pavements – An Incremental Approach. Report 138. Mechanistic Design of Semi-Rigid Pavements, Danish Road Directorate, 2004.

George

K. P.

Soil Stabilization Field Trial. Final Report FHWA/MS-DOT-RD-05-133. University of Mississippi, 2001.

George

K. P.

Bajracharya

Gaddam

Precracking Mitigates Shrinkage Cracks in Cemented Materials. Damage and Fracture Mechanics VII, Vol. 37, 2003, pp. 79–90.

Scullion

Precracking of Soil-Cement Bases to Reduce Reflection Cracking: Field Investigation. Transportation Research Record: Journal of the Transportation Research Board, 2002. 1787: 22–30.

Hope

C. A.

Evaluation of Portable Devices for Monitoring Microcracking of Cement-Treated Base Layers. Master thesis. Brigham Young University, 2011.

Miller

H. J.

Guthrie

S. W.

Rebecca

C. A.

Smith

Evaluation of Cement-Stabilized Full-Depth-Recycled Base Materials for Frost and Early Traffic Conditions. Recycled Materials Resource Center, 2012.

Sebesta

Effectiveness of Minimizing Reflective Cracking in Cement-Treated Bases by Microcracking. Texas Transportation Institute, 2004.

George

K. P.

Mechanism of Shrinkage Cracking of Soil-Cement Bases. Highway Research Record, Vol. 442, 1973, pp. 1–10.

10.

Sebesta

Continued Evaluation of Microcracking in Texas. Texas Transportation Institute, 2005.

11.

Sebesta

Microcracking for Reduced Shrinkage in Cement-Treated Base. Project Summary Report 0-4502-S. Texas Transportation Institute, 2006.

12.

Liu

Intaj

Minimizing Shrinkage Cracking in Cement-Stabilized Bases through Micro-Cracking. Project 12-3P. Louisiana Transportation Research Center, 2018 (Submitted).

13.

Standard Practice for Certification of Inertial Profiling Systems . AASHTO Designation: R 56-14. AASHTO, Washington, D.C., 2014.

14.

Standard Test Method for Measuring the Longitudinal Profile of Traveled Surfaces with an Accelerometer Established Inertial Profiling Reference . ASTM Designation: E950/E950M-09. ASTM, West Conshohocken, Pa., 2018.