Investigation on Improvement of Flexural Behavior of Low-Density Cellular Concrete through Fiber Reinforcement for Non-Structural Applications

Abstract

During the last decades, cellular lightweight concrete (CLC), or foamed concrete, has been experiencing greater interest in geotechnical, structural, and non-structural applications. The low density and high flowability makes it a favorable construction material in relation to handling, placing, and construction costs. However, the applications of low-density cellular concrete (LDCC), the category of CLC with a unit weight less than 50 pounds per cubic foot (801 kg/m³) and generally without fine aggregates, are limited mostly to backfill applications in geotechnical engineering. The main reason lies in the brittleness of the material and low to zero resistance to flexural loads. Fiber-reinforced LDCC may be a reasonable solution to improve mechanical properties and expand the application range of the material. This study investigated the effects of adding polypropylene and hybrid fibers on physical and mechanical properties of LDCC and the feasibility of expanding LDCC utilization to non-structural applications. Results showed that although there is a slight reduction of flowability and compressive strength, the flexural behavior of LDCC can be significantly improved with the incorporation of fibers. The flexural strength and flexural toughness of LDCC was found to increase from 26.8 pounds per square inch (psi) (0.18 MPa) to 217.5 psi (1.48 MPa), and from 5.67 lb-in. (0.64 kN-mm) to 292 lb-in. (33.0 kN-mm) respectively at a 1.0% addition rate of a fibrillated polypropylene fiber selected in this study, which makes it a feasible material for non-structural applications.

Get full access to this article

View all access options for this article.

References

Guidelines for Cellular Concrete. Strength/Density Chart. https://aerixindustries.com/wp-content/uploads/2019/02/Strength-Density-Charts.pdf. Accessed June 3, 2018.

Mugahed Amran

Y. H.

Farzadnia

Abang Ali

A. A.

Properties and Applications of Foamed Concrete: A Review. Construction and Building Materials, Vol. 101, 2015, pp. 990–1005.

Guide for Cast-in-Place Low-Density Cellular Concrete . ACI 523.1R-06. American Concrete Institute, Farmington Hills, Mich., 2006.

Mugahed Amran

Y. H

Rashid

R. S. M.

Hejazi

Safiee

N. A.

Abang Ali

A. A.

Response of Precast Foamed Concrete Sandwich Panels to Flexural Loading. Journal of Building Engineering, Vol. 7, 2016, pp. 143–158.

Zollo

R. F.

Hays

C. D.

A Habitat of Fiber-Reinforced Concrete. Concrete International, Vol. 16, 1994, pp. 23–26.

Fernando

P. L. N.

Jayasinghe

M. T. R.

Jayasinghe

Structural Feasibility of Expanded Polystyrene (EPS) Based Lightweight Concrete Sandwich Wall Panels. Construction and Building Materials, Vol. 139, 2017, pp. 45–51.

Jayasinghe

Fonseka

W. M. C. D. J.

Abeygunawardhene

Y. M.

Load Bearing Properties of Composite Masonry Constructed with Recycled Building Demolition Waste and Cement Stabilized Rammed Earth. Construction Building Materials, Vol. 102, 2016, pp. 471–477.

Manjummekudiyil

E. M.

Alias

B. P.

Eldhose

B. K.

Rajan

Hussain

Study of GFRG Panel and its Strengthening. International Journal of Civil and Structural Engineering Research, Vol. 2, 2014, pp. 161–165.

Guide for Precast Cellular Concrete Floor, Roof, and Wall Units. ACI 523.2R-96. American Concrete Institute, Farmington Hills, Mich., 1997.

10.

Tikalsky

P. J.

Pospisil

MacDonald

A Method for Assessment of the Freeze-Thaw Resistance of Preformed Foam Cellular Concrete. Cement and Concrete Research, Vol. 34, 2004, pp. 889–893.

11.

Narayanan

Ramamurthy

Structure and Properties of Aerated Concrete: A Review. Cement & Concrete Composites, Vol. 22, 2000, pp. 321–329.

12.

Zollo

R. F.

Hays

C. D.

Engineering Material Properties of a Fiber Reinforced Cellular Concrete. Materials Journal, Vol. 95, 1998, pp. 631–635.

13.

Jones

M. R.

Zheng

Ozlutas

Stability and Instability of Foamed Concrete. Magazine of Concrete Research, Vol. 68, No. 11, 2015, pp. 1–8.

14.

Kong

Properties of High-Strength Foam Concrete. Master dissertation. National University of Singapore, 2004.

15.

Valore

R. C.

Cellular Concretes Part 2 Physical Properties. Journal Proceedings, Vol. 50, 1954, pp. 817–836.

16.

Falliano

De Domenico

Ricciardi

Gugliandolo

Improving the Flexural Capacity of Extrudable Foamed Concrete with Glass-Fiber Bi-Directional Grid Reinforcement: An Experimental Study. Composite Structures, Vol. 209, 2019, pp. 45–59.

17.

Amirrasouli

Mechanical Properties of Low Density Fibre-Reinforced Cellular Concrete and its Energy Absorption Potential against Air Blast. PhD dissertation. University of Manchester, 2015.

18.

C150 Standard Specification for Portland Cement . ASTM International, West Conshohocken, Pa., 2012.

19.

C869 Standard Specification for Foaming Agents Used in Making Preformed Foam for Cellular Concrete . ASTM International, West Conshohocken, Pa., 2012.

20.

Fiber-Reinforced Cellular Concrete Homes . The Aberdeen Group, publication #J941110, 1994.

21.

Dawood

E. T.

Hamad

A. J.

Toughness Behavior of High-Performance Lightweight Foamed Concrete Reinforced with Hybrid Fibres. Structural Concrete, Vol. 16, 2015, pp. 496–507.

22.

C796 Standard Test Method for Foaming Agents for Use in Producing Cellular Concrete Using Preformed Foam . ASTM International, West Conshohocken, Pa., 2012.

23.

C495 Standard Test Method for Compressive Strength of Lightweight Insulating Concrete . ASTM International, West Conshohocken, Pa., 2012.

24.

C617 Standard Practice for Capping Cylindrical Concrete Specimens . ASTM International, West Conshohocken, Pa., 2012.

25.

C1609 Standard Test Method for Flexural Performance of Fiber-Reinforced Concrete (Using Beam with Third-Point Loading) . ASTM International, West Conshohocken, Pa., 2012.

26.

Cao

Cheng

Cao

Gao

Workability, Strength and Shrinkage of Fiber-Reinforced Expansive Self-Consolidating Concrete. Construction and Building Materials, Vol. 131, 2017, pp. 178–185.

27.

Chen

Liu

Contribution of Hybrid Fibers on the Properties of the High-Strength Lightweight Concrete Having Good Workability. Cement and Concrete Research, Vol. 35, 2005, pp. 913–917.

28.

Niu

Zhang

Huang

Wang

Hong

Zhang

Dynamic Compressive Mechanical Behavior and Modelling of Basalt-Polypropylene Fiber-Reinforced Concrete. Archives of Civil and Mechanical Engineering, Vol. 18, 2018, pp. 914–927.

29.

Libre

N. A.

Shekarchi

Malhoutian

Soroushian

Mechanical Properties of Hybrid Fiber Reinforced Lightweight Aggregate Concrete Made with Natural Pumice. Construction and Building Materials, Vol. 25, 2011, pp. 2458–2464.

30.

Guler

The Effect of Polyamide Fibers on Strength and Toughness Properties of Structural Lightweight Aggregate Concrete. Construction and Building Materials, Vol. 173, 2018, pp. 394–402.

31.

Wang

J. Y.

Chia

K. S.

Liew

J. Y. R.

Zhang

M. H.

Flexural Performance of Fiber-Reinforced Ultra Lightweight Cement Composites with Low Fiber Content. Cement & Concrete Composites, Vol. 43, 2013, pp. 39–47.

32.

Rasheed

M. A.

Prakash

S. S.

Mechanical Behavior of Sustainable Hybrid-Synthetic Fiber Reinforced Cellular Light Weight Concrete for Structural Applications of Masonry. Construction and Building Materials, Vol. 98, 2015, pp. 631–640.