Hygrothermal Effects on RT-Cured Glass-Epoxy Composites in Immersion Environments. Part B: Degradation Studies

Abstract

The degradative effects of artificial seawater and distilled water immersion at 333° K on the mechanical properties (ILSS, compression strength) of BID glass/epoxy composite materials has been studied. Experimental results showed that the composite degradation trends were similar in both the media. It was found that the composite specimens exhibited a higher compressive and ILSS retention when immersed in the artificial seawater than when immersed in distilled water. This is attributed to the moisture absorption levels being higher in specimens immersed in distilled water than those immersed in artificial seawater (Part A). Further, it was found that the measured and predicted mechanical strength retention ratios (compression and ILSS) were in fairly good agreement with each other for both the immersion conditions.

Keywords

glass/epoxy composite moisture gain degradation compression ILSS hot wet property

Get full access to this article

View all access options for this article.

References

1. Tsostis, T. K. 1989. “Effects of Moisture on Composite Materials,” Ph.D. dissertation, Texas A&M University.

2. Browning, C. E. 1987. “The Mechanisms of Elevated Temperature Property Losses in High Performance Structural Epoxy Resin Matrix Materials after Exposures to High Humidity Environments,” ICCM-2, p. 1527.

3. Cai, L-W and Y. Weitsman . 1994. “Non-Fickian Moisture Diffusion in Polymeric Composites,” J. of Composite Materials, 28:130.

4. Singh, K. S. , P. N. Singh and R. M. V. G. K. Rao . 1991. J. of Reinforced Plastics and Composites, 10(9):457-462.

5. Menges, G. and H. W. Gitshner . 1980. “Sorption Behaviour of Glass-Fibre Reinforced Composites and the Influence of Diffusing Media on Deformation and Failure Behaviour,” Proceedings of the Third International Conference on Composite Materials, ICCM-3, Paris, p. 597.

6. Schutte, C. , W. McDonough , M. Shioya , M. McAuliffe and M. Greenwood . “The Use of a Single-Fiber Fragmentation Test to Study Environmental Durability of Interfaces/Interphases between DGEBA/mPDA Epoxy and a Glass Fiber: The Effect of Moisture,” in press in Composites.

7. Almeida, J. R. M. 1991. “Effects of Distilled Water and Saline Solution on the Interlaminar Shear Strength of an Aramid/Epoxy Composite,” J. of Composites, Vol. 22, No. 6, p. 448.

8. Sloan, F. E. and R. J. Saymour . 1992. “The Effect of Sea Water Exposure on Mode I Interlaminar Fracture and Crack Growth in Graphite/Epoxy,” J. of Composite Materials, Vol. 26, No. 18, p. 2655.

9. Chamis, C. C. , R. F. Lark and J. H. Sinclair . “An Integrated Theory for Predicting the Hydrothermomechanical Response of Advanced Composite Structural Components,” Lewis Research Center, Cleveland, Ohio. NASA Technical Memorandum 73812.

10.

10. Murthy, P. L. N. and C. C. Chamis .“Simplified Design Procedures for Fiber Composite Structural Components/Joints.” Lewis Research Center, Cleveland, Ohio. NASA Technical Memorandum 103113, N90-24384.