Processing of Polypropylene Foams in Melt Compounding Based Rotational Foam Molding

Abstract

This paper is intended to provide an engineering understanding of the technological potentials for processing polypropylene (PP) foams in rotational foam molding. A process proposal, based on the melt compounding material-preparation approach, capable of producing completely foamed, single-layer, single-piece PP products in rotational foam molding, is disclosed in detail. It comprises dispersing a chemical blowing agent (CBA) in the PP matrix using a twin-screw compounder, pelletizing the obtained expandable composition, and then producing foams in an uninterrupted rotational foam molding cycle by using the pre-compounded foamable pellets. Several PP grades were deliberately selected to cover a wide range of melt flow rates (MFR), starting from 5.5 up to 35 dg/min. After the raw materials participating in the study were characterized using thermal analysis instrumentation, different foamable compositions were formulated in order to prepare both 3-fold and 6-fold foamable pellets from each PP grade. The optimal foam processing strategies were identified via a systematic experimental parametric search. Foams with the best cell morphologies were obtained out of the high melt strength PP grades. In addition, the experimental results revealed that the cell morphology of the processed PP foams is not as good as that of respective PE foams. However, the cell morphologies of the PP foams processed by using the melt compounding-based approach demonstrated significant improvements in comparison with those processed by using the dry blending-based approach.

Get full access to this article

View all access options for this article.

References

1. Klempner D. and Frisch K.C. , Handbook of Polymeric Foams and Foam Technology, Hanser Publishers, New York (1991).

2. Frisch K. C. and Saunders J. H. , Plastic Foams (In two parts), Part I, Marcel Dekker, Inc., New York (1972).

3. Landrock A. H. , Handbook of Plastic Foams, Types, Properties, Manufacture and Applications, Noyes Publications, New Jersey (1995).

4. Frisch K. C. and Saunders J. H. , Plastic Foams (In two parts), Part II, Marcel Dekker, Inc., New York (1973).

5. Throne J. L. , Thermoplastic Foams, Sherwood Technologies, Inc., Sherwood Publishers, Ohio (1996).

6. Pop-Iliev R., Processing of Fine-Cell Polypropylene Foams in Compounding-Based Rotational Foam Molding, M.A.Sc. Thesis, University of Toronto (1999).

7. Pop-Iliev R. , Liu G. , Liu F. , Park C. B. , D’Uva S. and Lefas J. A. , SPE ANTEC, Tech. Papers, 45, 1457-1467 (1999).

8. Pop-Iliev R. , Liu G. , Liu F. , Park C. B. , D’Uva S. and Lefas J. A. , SPE RETEC, Preprints of the Rotational Molding Topical Conference, Strongsville, Ohio, pp. 95-104 (1999).

9. Liu G. , Park C.B. , and Lefas J.A. , Polym. Eng. Sci., 38:1997-2009 (1998).

10.

10. Liu F., Processing of Polyethylene and Polypropylene Foams in Rotational Molding, M. A. Sc. Thesis, University of Toronto (1998).

11.

11. Liu S. J. and Tsai C. H. , SPE ANTEC, Technical Papers, pp. 1161-1165 (1998).

12.

12. Equistar Chemical Company , News Releases (1997).

13.

13. Millenium Petrochemicals Inc. , Polypropylene Technical Tips, Cincinnati (1998).

14.

14 Montell Polyolefines , Data Sheets (1998).

15.

15. Uniroyal Chemical , Celogen Selector Guide (1998).

16.

16. Uniroyal Chemical , Celogen Physical Properties Guide (1998).

17.

17. Aldrich Chemical Company , 1998-99 Aldrich Inorganics and Organometalics Catalog/Handbook (1998).

18.

18. Pop-Iliev R. , Liu G. , Liu F. , Park C. B. , D’Uva S. and Lefas J. A. , SPE ANTEC, Technical Papers, 45:1457-1467 (1999).

19.

19. Pop-Iliev R. , Park C. B. , Liu G. and Liu F. , Control of the Melt Strength of Polypropylene in Rotational Foam Molding, SPE ANTEC 2000, submitted (1999).