Laser Transmission Welding of Semi-Crystalline Thermoplastics—Part I: Optical Characterization of Nylon Based Plastics

Abstract

Optimization of welding for thermoplastic parts strongly depends on the material properties, part design, as well as the welding operating technology conditions. Laser transmission welding requires preferential deposition of energy and subsequent melting of the material in the interfacial zone. This is optimized when the laser beam is transmitted through the transparent part and absorbed by the adjoining part to be welded. Energy deposition can be controlled to some extent by adjusting laser parameters (power, choice of beam focussing optics, sweep rate etc.).

The thermoplastic material properties may have the greater influence and need to be characterized for optimum material selection. Commercial nylon type materials cover a large array of compositions, which may affect the welding process. To guide selection of nylon based plastics for a range of applications we have measured the influence of specific factors such as fiber-glass, mineral filler, impact modifier content, additives, and color versions on the Near InfraRed (NIR) transmission properties.

In a following paper (Part II) ^a ¹ we have related these findings to the mechanical performance of shear and butt joints produced under various laser welding technology conditions (laser beam power, welding speed, laser beam/spot diameter, clamp pressure, plastic color, etc.). Comprehensive results of this evaluation will assist designers and technologists in thermoplastics selection for laser welding applications. The purpose of this report is to increase the understanding of the plastics engineering community regarding the usefulness and possible applicability of laser transmission welding (LTW) technology for nylon made components.

Keywords

Nylon polyamide welding laser near infra-red absorption transmission fiber-glass mineral fillers pigments colors melt layer thickness butt shear

Get full access to this article

View all access options for this article.

References

1. Taylor, N. S. , Klaiber F. and Wermelinger, J.

“Assessment of PP Joints Made by a New Infrared Joining System,”

SPE (Antec’93) Conference Proceedings, Vol. 2, pp. 2647-2656 (1993).

2. Chen Yang S. and Benatar, Avraham , “Infrared Welding of Polypropylene,” SPE (Antec’95) Conference Proceedings, Vol. 1, 1235-1238 (1995).

3. Grimm, R. A. , “Through-Transmission Infrared Welding of Polymers,” SPE (Antec’96) Conference Proceedings, Vol. 1, pp. 1238-1244 (1996).

4. Yeh, Hong Jun and Grimm, Robert A. , “Infrared Welding of Thermoplastics: Characterization of Transmission Behavior of Eleven Thermoplastics,” SPE (Antec’98)Conference Proceedings, Vol. 1, pp.1030-1033 (1998).

5. David A. Grewell , “Applications with Infrared Welding of Thermoplastics,” SPE (Antec’99) Conference Proceedings, Vol. 1, pp. 1411-1415 (1999).

6. Ou, B. S. , Benatar, A. and Albright, C. W. , “Laser Welding of Polyethylene and Polypropylene Plates,” SPE (Antec’92) Conference Proceedings, Vol. 2, pp. 1764-1767 (1992)

7. Jones, Ian , Taylor, Nicki , “Laser Excel in High Speed Plastic Welding,” TWI, Bulletin 6, Reprint 471/6/94 p. 3, November/December (1994).

8. Jones, Ian , “Transmission Laser Welding of Plastics,” TWI, Bulletin 75, 4 p, July/August 1998.

9. Potente, H. , Korte, J. , Becker, F. , “Laser Transmission Welding of Thermoplastics: Analysis of the Heating Phase,” SPE (Antec’98) Conference Proceedings, Vol. 1, pp. 11022-11025 (1998).

10.

10. Potente, H. , Korte, J. , “Laser Butt Welding of Semi-Crystalline Thermoplastics,” SPE (Antec’96) Conference Proceedings, Vol. 1 pp. 1255-1259 (1996).

11.

11. “Lasers Take AIM at Welding Plastics,” Injection Molding, pp.103-106, April (1999).

12.

12. Hedrun Puetz , Dirk Haensch , etc., “Laser Welding Offers Array of Assembly Advantages,” Modern Plastics, pp. 121-123, September (1997).

13.

13. Klein, H. , Haberstroh, E. , “Laser Beam Welding of Plastic Micro Parts,” SPE (Antec’99) Conference Proceedings, Vol. 1, pp. 1406-1410 (1999).

14.

14. Val Kagan , “Good Vibration Join Thermoplastics Fast,” Machine Design, A Penton Publication, pp. 67-74, August (1999).

15.

15. Kagan, V. , etc., “Performance of Vibration Welded Thermoplastic Joints,” US Patent # 5,874,146, February (1999).

16.

16. Carlson, E. , Nelson, K. , “Nylon Under-the-Hood. A History of Innovation,” SAE, Automotive Engineering, pp. 84-89, December (1996).

17.

17. Treusch, H. G. , Putz, H. , Hansch, D. , “Laser Welding of Polymer Parts,” 5-th Plastic Manifold Forum, p. 12 (1998).

18.

18. Natrop, J. , J. Korte, J. , “Machinery Concepts and Welding Applications for Laser Welding,” 5-th Plastic Manifold Forum, p. 16 (1998).

19.

19. Destefani, James D. , “Manifolds Improvements,” Molding Systems, pp. 34-38, August (1999).

20.

20. Potente, H. , Becker, F. , “Laser Welding of Thermoplastic Materials,” 5-th Plastic Manifold Forum, p. 10 (1998).

21.

21. Grimm, Robert. A. and Yeh, Hong Jun

“Infrared Welding of Thermoplastics: Colored Pigments and Carbon Black Levels on Transmission on Infrared Radiation,”

SPE (Antec’98) Conference Proceedings, Vol. 1, pp.1026-1029 (1998).

22.

22. Potente, H. , Becker, F. , “Weld Strength Behavior of Laser Butt Welds,” SPE (Antec’99) Conference Proceedings, Vol. 1 pp. 1402-1405 (1999).

23.

23. “Make it with LASERS: Laser Processing of Polymers, Polymer Composites & Wood,” Seminar on the TechnologyTransfer Program, Technical Presentations. The Welding Institute (TWI), Cambridge, UK (1999).

24.

24. Kagan, V. , Bray, R.G. , Kuhn, W. , and Pinho, G. P. , “Selecting Nylon-Based Plastics for Laser Welding Technology,” SAE 2000 Transactions, J. Matls and Manuf., Vol. 109 pp. 663-679 (2000).