Effects of Processing Parameters on Mechanical and Thermal Properties of Glass Mat Reinforced Nylon 6 Composites

Abstract

Nylon 6 (PA6)/Glass Mat (GM) composites and pure PA6 were prepared by compression molding technique and the effects of molding temperature, pressure application time and GM content on the final properties of the materials were investigated. At each temperature and pressure application time, the composite with one layer GM had higher tensile strength, tensile modulus but lower% elongation at break than neat PA6. Processing parameters did not significantly influence the tensile behavior of the pure PA6 and PA6/GM composites. The effect of GM content showed that tensile strength and modulus increased but the% elongation at break decreased with increasing GM content. Thermal properties of the neat PA6 and the composites providing sufficient melting point temperature and crystallinity were found to be unaffected with different process temperature, pressure application time and GM content.

Get full access to this article

View all access options for this article.

References

1. Kroschwitz, J.I. (1990). Concise, Encyclopedia of Polymer Science and Engineering, John Wiley & Sons Inc., New York .

2. Darlington, M.W., McGinley, P.L. and Smith, G.R. (1976). Structure and Anisotropy of Stiffness in Glass Fiber Reinforced Thermoplastics , Journal of Material Science, 11: 877–886 .

3. Maekawa, Z., Fujii, T., Ikeda, T. and Yamada, T. (1983). Strength Properties of Glass Fiber Reinforced Thermoplastics , In: Proceedings of 27th Japan Congress on Materials Research, pp. 269–273 .

4. Ericson, M. and Berglund, L. (1992). Deformation and Fracture of Glass-Mat-Reinforced Polypropylene , Composites Science and Technology, 43: 269–281 .

5. Nilsson G., Fernberg S.P., Berglund L.A. (2002). Strain Field Inhomogeneities and Stiffness Changes in GMT Containing Voids , Composites, 33: 75–85 .

6. Wakeman, M.D., Cain, T.A., Rudd, C.D., Brooks R. and Long, A.C. (1999). Compression Molding of Glass and Polypropylene Composites for Optimized Macro-and Micro-mechanical Properties: II. Glassmatreinforced Thermoplastics , Composites Science and Technology, 59: 709–726 .

7. Cantwell, W.J. (1996). The Influence of Stamping Temperature on the Properties of a Glass Mat Thermoplastic Composite , Journal of Composite Materials, 30(11): 1266–1281 .

8. Bernhardsson, J. and Shishoo, R. (2000). Compression Molding of Warp-Knitted PET/GF Based Composites: Influence of Forming Temperature on Consolidation Quality and Impact Properties , Journal of Thermoplastic Composite Materials, 13: 326–341 .

9. Muzzy, J., Norpoth, L. and Varughese, B. (1989). Characterization of Thermoplastic Composites for Processing , SAMPLE Journal, 25: 23–29 .

10.

10. Svensson, N., Shishoo, R. and Gilchrist, M. (1998). Fabrication and Mechanical Response of Commingled GF/PET Composites , Polymer Composites, 19: 360–369 .

11.

11. Wu, S.H., Wang, F.Y., Ma, C.C.M., Chang, W.C., Kuo, C.T., Kuan, H.C. and Chen (2001). Mechanical, Thermal and Morphological Properties of Glass Fiber and Carbon Fiber Reinforced Polyamide-6 and Polyamide-6/Clay Nanocomposites , Materials Letters, 49: 327–333 .

12.

12. Pedroso, A.G., Mei, L.H.I., Agnelli, J.A.M. and Rosa, D.S. (2002). The Influence of the Drying Process Time on the Final Properties of Recycled Glass Fiber Reinforced Polyamide 6 , Polymer Testing, 21: 229–232 .

13.

13. Yilmazer, U. and Cansever, M. (2002). Effects of Processing Conditions on the Fiber Length Distribution and Mechanical Properties of Glass Fiber Reinforced Nylon-6 , Polymer Composites, 23: 61–71 .

14.

14. Annual Book of ASTM Standards. (1993). Standard Test for Method for Tensile Properties of Plastics (Metric), D638M-91, 8-1: pp. 161–173 .

15.

15. Annual Book of ASTM Standards. (1993). Standard Test for Method for Ignition Loss of Cured Reinforced Resins, D2584 – 68, 8-1: pp. 85–86 .

16.

16. Lide, D.R. (1995). Silane Coupling Agents, CRC Handbook of Chemistry and Physics a Ready Reference Book of Chemical and Physical Data, 76th edn., 7636, CRC Press, New York .