Characterization of Curing Stress Effects on Fracture Behavior of FRP Laminated Composites with Embedded Delaminations

Abstract

A detailed study on the effect of curing stresses on interlaminar delamination crack growth behavior in fiber-reinforced polymeric (FRP) composites is presented. At a given applied load or displacement, the strain energy release rate distribution along the delamination front with and without considering the effects of curing stresses are compared. In this analysis, results are presented for elliptical delaminations embedded between plies of different orientations in the laminate. A full three-dimensional coupled-field finite element analysis has been conducted to study the delamination crack growth behavior due to curing stress effects. A superposition procedure along with the modified crack closure integral technique based on the concepts of linear elastic fracture mechanics is employed to evaluate the individual modes of strain energy release rates during delamination propagation. It has been observed that the residual thermal stresses developed during the curing stages in manufacturing of FRP laminated composites significantly affect the onset and growth of delamination. The asymmetric behavior of interlaminar fracture energy along the delamination front is found to depend upon the stacking sequence, neighboring ply orientation, thermoelastic anisotropy, and material heterogeneity at the interface of laminated composites.

Keywords

coupled-field FE analysis curing stress delamination FRP composite LEFM MCCI strain energy release rate

Get full access to this article

View all access options for this article.

References

Hahn, H. T. and Pagano, N. J. (1975). Curing Stresses in Composite Laminates , J. of Composite Materials, 9(1): 91–106 .

Wang, A. S. D. and Crossman, F. W. (1977). Edge Effects on Thermally Induced Stresses in Composite Laminates , J. of Composite Materials, 11(4): 300–312 .

O'Brien, T. K. (1982). Characterisation of Delamination Onset and Growth in a Composite Laminate , Damages in Composite laminates ASTM STP 775, 20, pp. 140–167 .

Johannesson, T. , Sjoblam, P. and Selden, R. (1984). The Detailed Structure of Delaminated Surfaces in Graphite/Epoxy Laminates , J. of Materials Science, 19(4): 1171–1177 .

Kim, K. S. and Hong, C. S. (1986). Delamination Growth in Angle-ply Laminated Composites , J. Composite Materials, 20(5): 423–438 .

Stout, M. G. , Koss, D. A. , Liu, C. and Idasetima, J. (1999). Damage Development in Carbon/Epoxy Laminates Under Quasi-static and Dynamic Loading , Composites Science and Technology, 59(16): 2339–2350 .

Kaczmarek, H. (2003). Lamb Wave Interaction with Impact-induced Damage in Aircraft Composite: Use of the A0 Mode Excited by Air-coupled Transducer , J. of Composite Materials, 37(3): 217–232 .

Chai, H. and Babcock, C. D. (1985). Two Dimensional Modeling of Compressive Failure in Delaminated Laminates , J. Composite Materials, 9(1): 67–98 .

Sun, C. T. and Manoharan, M. G. (1989). Strain Energy Release Rates of an Interfacial Crack Between Two Orthotropic Solids , J. Composite Materials, 23(5): 460–478 .

10.

Liu, K.-S. and Tsai, S. W. (1998). A Progressive Quadratic Failure Criterion of a Laminate , Composites Science and Technology, 58(7): 1033–1041 .

11.

Yin, W. L. (1998). Thermoelastic Postbuckling Response of Strip Delamination Models , Int. J. Solids and Structures, 35(25): 3331–3346 .

12.

Rolfes, R. , Noack, J. and Taeschner, M. (1999). High Performance 3D-analysis of Thermo-mechanically Loaded Composite Structures , Composite Structures, 46(4): 367–379 .

13.

Nairn, J. A. (2000). Energy Release Rate Analysis for Adhesive and Laminate Double Cantilever Beam Specimens Emphasizing the Effect of Residual Stresses , Int. J. Adhesion and Adhesives, 20(1): 59–70 .

14.

Fiedler, B. , Hojo, M. and Ochiai, S. (2002). The Influence of Thermal Residual Stresses on the Transverse Strength of CFRP using FEM , Composites Part A: Applied Science and Manufacturing, 33(10): 1323–1326 .

15.

Aghdam, M. M. and Khojeh, A. (2003). More on the Effects of Thermal Residual and Hydrostatic Stresses On Yielding Behavior of Unidirectional Composites , Composite Structures, 62(3–4): 285–290 .

16.

Dattaguru, B. , Venkatesha , Ramamurthy, T. S. and Buchholz, F. G. (1994). Finite Element Estimates of Strain Energy Release Rate Components at the Tip of an Interface Crack Under Mode I Loading , Engineering Fracture Mechanics, 49(3): 211–228 .

17.

Wang, J. T. and Raju, I. S. (1996). Strain Energy Release Rate Formulae for Skin-stiffener Debond Modeled with Plate Elements , Engineering Fracture Mechanics, 54(2): 211–228 .

18.

Sankar, B. V. and Sonik, V. (1995). Point-wise Energy Release Rate in Delaminated Plates , AIAA J, 33(7): 1312–1318 .

19.

Chakraborty, D. and Pradhan, B. (1998). Critical Strain Energy Release Rate of Broken Ply Composite Laminates , J. of Reinforced Plastics & Composites, 17(6): 498–511 .

20.

Konig, M. , Krueger, R. and Rinderknecht, S. (2000). Finite Element Analysis of Delamination Growth in a Multidirectional Composite ENF Specimen, In: Grant, P. and Rousseau, C. Q. (eds), Composite Materials: Theory and Practice, American Society for Testing and Materials , ASTM STP Vol. 1383, pp. 345–365.

21.

Springer, S. G. and Tsai, S. W. (1967). Thermal Conductivities of Unidirectional Materials , J. of Composite Materials, 1(2): 166–173 .

22.

Williams, J. G. (1988). On the Calculation of Energy Release Rates for Cracked Laminates , Int. J. of Fracture, 36: 101–119 .

23.

Irwin, G. R. (1957). Analysis of Stresses and Strain Near the End of a Crack Traversing a Plate, Trans. ASME , J. of Applied Mechanics, 24, pp. 361–364 .

24.

Rybicki, E. F. and Kanninen, M. F. (1977). A Finite Element Calculation of Stress Intensity Factors by a Modified Crack Closure Integral , Engineering Fracture Mechanics, 9(4): 931–938 .

25.

Wang, S. S. and Choi, I. (1983). The Interface Crack Behavior in Dissimilar Anisotropic Composites Under Mixed-mode Loading , ASME J. of Applied Mechanics, 50: 179–183 .

26.

Rice, J. R. (1988). Elastic Fracture Mechanics Concepts for Interfacial Cracks , ASME J. of Applied Mechanics, 55(11): 98–103 .

27.

Wang, S. S. (1980). An Analysis of Delamination in Angle-ply Fiber-reinforced Composites , ASME J. of Applied Mechanics, 47(2): 64–70 .

28.

Klug, J. , Wu, X. X. and Sun, C. T. (1996). Efficient Modeling of Postbuckling Delamination Growth in Composite Laminates using Plate Elements , AIAA J., 34(1): 178–184 .

29.

Krueger, R. and O'Brien, T. K. (2001). A Shell/3D Modeling Technique for the Analysis of Delaminated Composite Laminates , Composites: Part A, 32(1): 25–44 .

30.

Whitcomb, J. D. (1992). Analysis of a Laminate with Postbuckled Delamination Including Contact Effects , J. of Composite Materials, 26(10): 1523–1325 .

31.

Buchholz, F.-G. , Rikards, R. and Wang, H. (1997). Computational Analysis of Interlaminar Fracture of Laminated Composites , Int. J. of Fracture, 86(1–2): 37–57 .