The Comparison of Organoclay with Respect to Silica on Properties of Natural Rubber Nanocomposites

Abstract

Effects of organoclay loading (organophilic modified montmorillonite with octadecylamine) in comparison to silica loading on the curing characteristics, tensile properties, thermal stability, and morphology of natural rubber (NR) nanocomposites were studied. Organoclay loading from 2 to 10 phr and silica with 10 and 30 phr loading were used as fillers in this study. The NR/organoclay nanocomposites were compounded using two roll mills and cured at 150°C. The results indicate that the tensile strength and tensile modulus reach maximum at 8 phr of organoclay but elongation at break and thermal stability increase with increasing organoclay loading. Tensile strength, tensile modulus, and elongation at break increase with increasing amount of silica from 10 to 30 phr. Overall results show that organoclay filled NR nanocomposites exhibit shorter processing time and higher tensile properties than silica filled NR nanocomposites. The enhanced properties are due to the homogenous dispersion of individual silicate layers in NR matrix, which is evidenced from the X-ray diffraction (XRD), transmission electron microscopy (TEM), and scanning electron microscopy (SEM) results.

Keywords

organoclay silica natural rubber nanocomposites.

Get full access to this article

View all access options for this article.

References

Varghese, S. and Kocsis, J.K. (2003). Natural Rubber-based Nanocomposites by Latex Compounding with Layered Silicates, Polymer, 44: 4921-4927.

Wang, K. , Liang, S. , Du, R. , Zhang, Q. and Fu, Q. (2004). The Interplay of Thermodynamics and Shear on the Dispersion of Polymer Nanocomposite, Polymer, 45: 7953-7960.

Eckel, D.B. , Balogh, M.P. , Fasulo, P.D. and Rodgers, W.R. (2003). Assessing Organo-clay Dispersion in Polymer Nanocomposites , Journal of Applied Polymer Science, 93: 1110-1117.

Fornes, T.D. , Yoon, P.J. and Paul, D.R. (2003). Polymer Matrix Degradation and Color Formation in Melt Processed Nylon 6/Clay Nanocomposites, Polymer, 44: 7545-7556.

Teh, P.L. , Mohd Ishak, Z.A. , Hashim, A.S. , Kocsis, J.K. and Ishiaku, U.S. (2004). Effects of Epoxidized Natural Rubber as a Compatibilizer in Melt Compounded Natural Rubber-Organoclay Nanocomposites, Eur. Polym. Int., 40: 2513-2521.

Okada, A. and Usuki, A. (1995). The Chemistry of Polymer-clay Hybrids, Mater Sci. Eng., C3: 109-115.

Novak, B.M. (1993). Hybrid Nanocomposite Materials - Between Inorganic Glasses and Organic Polymers, Adv. Mater., 5: 422-433.

Grannelis, E.P. (1996). Polymer Layered Silicate Nanocomposites, Adv. Mater., 8: 29-35.

Vaia, R.A. , Jandet, K.D. , Kramer, E.J. and Grannelis, E.P. (1995). Synthesis of Polypropylene Oligomer- Clay Intercalation Compounds, Macromolecules, 28, 8080-8085.

10.

Kornmam, X. , Lindberg, H. and Berglund, L. (2001). Synthesis of Epoxy-Clay Nanocomposites: Influence of the Nature of the Clay on Structure, Polymer, 42: 1303-1310.

11.

Wang, M. and Pinnavaia, T. (1994). Clay-Polymer Nanocomposites Formed from Acidic Derivatives of Montmorillonite and Epoxy Resin, Chem. Mater. , 6, 468-474.

12.

Messersmith, P. and Giannelis, E. (1994). Synthesis and Characterization of Layered Silicate-Epoxy Nanocomposites, Chem. Mater., 6: 1719-1725.

13.

Usuki, A. , Kawasumi, M. , Kojima, Y. , Fukushima, Y. , Okada, A. , Kurauchi, T. and Kamigaito, O. (1993). Mechanical Properties of Nylon 6 - Clay Hybrid , J. Mater. Res., 8: 1185-1189.

14.

Kojima, Y. , Usuki, A. , Kawasumi, M. , Fukushima, Y. , Okada, A. , Kurauchi, T. and Kamigaito, O. (1993). Synthesis of Nylon 6-Clay Hybrid, J. Mater. Res., 8: 1179-1184.

15.

Bokobza, L. and Rapoport, O. (2002). Reinforcement of Natural Rubber, J. Appl. Polym. Sci., 85: 2301-2316.

16.

Le Baron, P.C. , Wang, Z. and Pinnavaia, T. (1999). Polymer-Layered Silicate Nanocomposites: An Overview, Appl. Clay Sci., 11-29.

17.

Ismail, H. and Chia, H.H. (1998). The Effects of Multifunctional Additive and Epoxidation in Silica Filled Natural Rubber Compounds, Polym. Test., 17(3): 199-210.

18.

Ismail, H. and Chia, H.H. (1998). The Effects of Multifunctional Additive and Vulcanization Systems on Silica Filled Natural Rubber Compounds, Eur. Polym. J., 34: 1857-1863.

19.

Ansarifar, A. , Azhar, A. , Ibrahim, N. , Shiah, S.F. and Lawton, J.M.D. (2005). The Use of a Silanised Silica Filler to Reinforce and Crosslink Natural Rubber, Int. J. of Adhes. and Add., 25: 77-86.

20.

Meissner, B. and Matejka, L. (2000). Description of the Tensile Stress-Strain Behavior of Filler-Reinforced Rubber-Like Networks Using a Langevin-Theory-Based Approach , Polymer, 41: 7749-7760.

21.

Varghese, S. , Kocsis, J.K. and Gatos, K.G. (2003). Melt Compounded Epoxidized Natural Rubber/Layered Silicate Nanocomposites: Structure-Properties Relationships, Polymer, 44: 3977-3983.

22.

Ardhyanata, H. , Ismail, H. , Takeichi, T. and Judawisastra , H. (2006). Preparation and Properties of Ethylene Vinyl Acetate (EVA)/Organoclay/Compatibilizer Nanocomposites, Polym. Plast. Technol. Eng., 45(12): 1285-1293.

23.

Gao, X. , Mao, L. , Zhang, M. and Jin, R. (2006). Polycarbonate/Polypropylene/Fibrillar Silicate Ternary Nanocomposites Via Two-step Blending Process: Degradation and Morphology, Chinese J. Chem. Eng., 14(2): 248-252.

24.

Zanetti, M. , Camino, G. , Thomann, R. and Mulhaupt, R. (2001). Synthesis and Thermal Behaviour of Layered Silicate-EVA Nanocomposites, Polymer , 42(10): 4501-4507.

25.

Zhang, L. , Wang, Y. , Wang, Y. , Shui, Y. and Yu, D. (2000). Morphology and Mechanical Properties of Clay/Styrene-Butadiene Rubber Nanocomposites, J. Appl. Polym. Sci., 78: 1873-1878.