Preparation of Unsaturated Polyester Liquid Natural Rubber Reinforced by Montmorillonite

Abstract

The effect of liquid natural rubber (LNR) on the mechanical properties of unsaturated polyester (UP) has been studied in this article. Mechanical tests, such as impact and tensile test, have been conducted on the UP-LNR sample in order to determine the optimum LNR composition. The results showed that the tensile strength and impact energy increased with LNR and optimized at 10 phr. The optimum composition of LNR was used to prepare the composite with montmorillonite (MMT). X-ray diffraction of the composite showed the absence of peak in nanocomposites, which contain treated MMT. Scanning of electron microscopy also clearly showed that the agglomeration of clay occurs in the composite using untreated MMT, but is significantly reduced in size for the composite using treated MMT. On the other hand, the mechanical properties, such as tensile strength, tensile modulus, and impact energy, of the composites with modified MMT were also higher than the composite with unmodified MMT. The optimum composition of modified MMT in the composite was found at 4% filler loading.

Keywords

polyester natural rubber montmorillonite nanocomposite.

Get full access to this article

View all access options for this article.

References

Ramos, V.D. , Costa, H.M. , Soares, V.L.P. and Nascimento, R.S.V. ( 2005). Hybrid Composites of Epoxy Resin Modified with Carboxyl Terminated Butadiene Acrilonitrile Copolymer and Fly Ash Microspheres, Polym . Testing, 24(2): 387-384.

Tripathi, G. and Srivastava, D. (2008). Studies on the Physico-Mechanical and Thermal Characteristics of Blends of DGEBA Epoxy, 3,4 Epoxy Cyclohexylmethyl, 3′,4′-Epoxycylohexane Carboxylate and Carboxyl Terminated Butadiene Co-Acrylonitrile (CTBN), Mater. Sci. & Eng., 496(1-2): 483-493.

Nam, H.K. and Ho, S.K. (2005). Toughening Method and Mechanisms for Thermosets, J. Appl. Polym. Sci., 98(4): 1663-1667.

Pham, S. and Burchill, P.J. ( 1995). Toughening of Vinyl Ester Resins with Modified Polybutadienes , Polym., 36(17): 3279-3285.

Wong, P.Y. , Ahmad, I. and Abdullah, I. ( 2006). Composite of Aramid Fibre-Thermoplastic Natural Rubber: Effect of Processing Parameters and Compatibiliser, Polym. Polym. Compos., 14(7): 651-659.

Byung-Wan, J. , Seung-Kook, P. and Do-Keun , K. (2008). Mechanical Properties of Nano-MMT Reinforced Polymer Composite and Polymer Concrete, Constr. Build. Mater., 22: 14-20.

Dhakal, H.N. , Zhang, Z.Y. and Richardson, M.O.W. ( 2006). Nanoindentation Behaviour of Layered Silicate Reinforced Unsaturated Polyester Nanocomposites, Polym. Test., 25(6): 846-852.

Ibrahim, A. ( 1996). Malaysia Patent, MY-108852-A.

Gryshchuk, O. , Jost, N. and Karger-Kocsis , J. (2002). Toughening of Vinylester-Urethane Hybrid Resins by Functional Liquid Nitrile Rubbers and Hyperbranched Polymers, Polym., 43(17): 4763-4768.

10.

Bucknall, C.B. ( 1977). Toughened Plastics, Applied Science , London.

11.

Newman, S. and Strella, S. ( 1965). Stress - Strain Behavior of Rubber Reinforced Glassy Polymers, J. Appl. Polym. Sci., 9(6): 2297-2310.

12.

Zhang, J. , Jiang, D.D. and Wilkie, C.A. ( 2006). Polyethylene and Polypropylene Nanocomposites Based on A Three Component Oligomerically-modified Clay, Polym. Degrad. Stab., 91(4): 641-648.