The effect of 3D weaving and consolidation on carbon fiber tows,fabrics,and composites

Abstract

This article investigates the damage imparted on load-bearing carbon fibers during the 3D weaving process and the subsequent compaction behavior of 3D woven textile preforms. The 3D multi-layer reinforcements were manufactured on a textile loom with few mechanical modifications to produce preforms with fibers orientated in the warp, weft, and through-the-thickness directions. Tensile tests were conducted on three types of commercially available carbon fibers, 12k HTA, 6k HTS, and 3k HTS in an attempt to quantify the effect of fiber damage induced during the 3D weaving process on the mechanical and physical performance of the fiber tows in the woven composite. The tests were conducted on fiber tows sampled from different locations in the manufacturing process from the bobbin, through the creel and loom mechanism, to the final woven fabric. Mechanical and physical testing were then conducted to quantify the tow geometry, orientation and the effect of compaction during manufacture of two styles of 3D woven composite by vacuum-assisted resin transfer molding (VaRTM).

Keywords

3D weaving carbon fiber fabric

Get full access to this article

View all access options for this article.

References

Atas C. and Liu D. Impact Response of woven composites with small weaving angles. Int J Impact Eng 2008; 35(2): 80.

Mouritz AP , Bannister MK , Falzon PJ and Leong KH Review of applications for advanced three-dimensional fibre textile composites . Composites Part A 1998; 30(12): 1445.

Ding YQ , Yan Y. , McIlhagger R. and Brown D. Comparison of the fatigue behaviour of 2-D and 3-D woven fabric reinforced composites. J Mater Process Technol 1995; 55(3-4): 171.

Quinn JP , McIlhagger R. , McIlhagger AT , Wilson S. , Simpson D. and Wenger W. The influence of binder tow density on the mechanical properties of spatially reinforced composites, Part 1 - Impact resistance. Composites Part A 2007; 38(3): 795.

Rudov-Clark S. , Mouritz AP , Lee L. and Bannister MK Fibre damage in the manufacture of advanced three-dimensional woven composites. Composites Part A 2002; 34(10): 963.

Lee L. , Rudov-Clark S. , Mouritz AP , Bannister MK and Herzberg I. Effect of weaving damage on the tensile properties of three-dimensional woven composites. Compos Struct 2002; 57(1-4): 405.

Lee B. , Leong KH and Herzberg I. Effect of weaving on the tensile properties of carbon fibre tows and woven composites. J Reinf Plast Compos 2001 ; 20(8): 652.

Simacek P. and Karbahari VM Notes on the modelling of perform compaction: I - micromechanics at the fibre bundle level. J Reinf Plast Compos 1996; 15: 86.

Saunders RA , Lekakou C. and Bader MG Compression and microstructure of fibre plain woven cloths in the processing of polymer composites. Composites Part A 1998 ; 29A: 443.

10.

Stewart G. , McIlhagger AT , Quinn JP and King S. An investigation into the effect of compaction on the mechanical performance of a 3D reinforced advanced composite. Polym Polym Compos 2007; 15(7): 535.

11.

Quinn JA and Randall JE Compliance of composite reinforcement materials. I Meche 1990; 3: 105.

12.

Quinn J. , McIlhagger R. and McIlhagger AT A modified system for design and analysis of 3D woven preforms. Composites Part A 2003; 34A: 6503.

13.

BS 2863. Method for determination of crimp of yarn in fabric. London: British Standards Institution, 1984.

14.

ASTM D4018-81. Standard test method for tensile properties of continuous filament carbon and graphite yarns, strands, rovings, and tows. Philadelphia: ASTM, 1981.

15.

ASTM D792-91. Standard test methods for density and specific gravity (relative density) of plastics by displacement. Philadelphia: ASTM , 1991.

16.

CRAG Standard Method 302. Method of test for the tensile strength and modulus of multidirectional fibre reinforced plastics. Philadelphia: ASTM, 1988.