Effect of chemical surface treatment on the mechanical properties of reinforced plasticized poly(lactic acid) biodegradable composites

Abstract

Biodegradable composites were prepared by melt-blending technique using 30 wt% kenaf bast fiber (KBF) to reinforce 70 wt% plasticized poly(lactic acid) (PLA). The KBF was treated with various percentages of sodium hydroxide (NaOH), whereas 5% triacetin was used as plasticizer. The effects of the KBF surface treatments on the tensile, flexural, impact strength, and DMA of the biocomposites were investigated. Tensile, flexural, and impact testing results reveal that 4% of NaOH-treated KBF produced composites with optimum tensile strength (62 MPa), flexural strength (67 MPa), and the impact strength (42 kJ/m²). The removal of the lignin from the fiber during the surface treatment caused the increment in the modulus result. This finding is also supported by the dynamic mechanical analysis. The storage modulus of plasticized PLA/treated KBF is higher than the storage modulus of plasticized PLA/untreated KBF which is attributed to the enhancement of the fiber—matrix adhesion. The loss modulus results showed that the T_g of the plasticized composites was shifting to higher temperature, from 55°C for plasticized PLA/untreated KBF to 65°C for plasticized PLA/treated KBF. The increase in T_g shows that the plasticized PLA has low chain mobility when reinforced with treated KBF, indicating better interaction.

Keywords

kenaf bast fiber NaOH plasticizer triacetin poly(lactic acid)biodegradable

Get full access to this article

View all access options for this article.

References

Huda MS , Dzal LT , Mohanty AK and Misra M. Effect of fiber surface treatments on the properties of laminated biocomposites from poly (lactic acid) (PLA) and kenaf fibers. Compos Sci Technol 2008; 68: 424-432.

Rahman M. and Brasel CS The plasticizermarket: as assessement of traditional plasticizers and research trends to meet new challenges. Prog Polym Sci 2004; 29: 1223-1248.

Mwaikambo L. and Ansell M. Chemical modification of hemp, sisal, jute and kapok fibers by alkalization. J Appl Polym Sci 2002; 84(12): 2222-2234.

Sharifah H. and Ansell M. The effect of alkalization and fibers alignment on the mechanical and thermal properties of kenaf fibers and hepm bast fibers composites: Part 1: polyester resin matrix. Compos Sci Technol 2004; 64: 1219-1230.

Edeerozey M. , Akil HM , Azhar AB and Zainal MI Chemical modification of kenaf fibers. Mater Lett 2007; 61: 2023-2025.

Bisanda E. and Ansell M. Properties of sisal-CNSL composites. J Mater Sci 1992; 27: 1690-1700.

Sreekala M. , Kumaran M. and Thomas S. Oil-palm fibers: morphology, chemical composition, surface modification and mechanical properties. J Appl Polym Sci 1997 ; 66: 821-835.

Geethamma V. , Joseph R. and Thomas S. Short coir fiber reinforced-natural rubber composites: effect of the fiber length, orientation, and alkali treatment . J Appl Polym Sci 1995; 55: 583-594.

Ray JC , Shetty AS and Wang MS Biodegradable plastics: a review. Adv Polym Technol 2006; 10: 23-30.

10.

Espert M. and Drzal LT Sustainable bio-composites from renewable resources: opportunities and challenges in the green materials world. J Polym Environ 2003; 10(1/2): 19-26.

11.

Yang HS , Kim HJ , Park HJ , Lee BJ and Hwang TS Effect of compatibilizing agents on rice husk flour reinforced polypropylene composite. Compos Struct 2007; 77(1): 45-55.

12.

Oksman K. , Skrifvars M. and Selin JF Natural fibers as reinforcement in poly(lactic acid) composites. Compos Sci Technol 2003; 63: 1317-1324.

13.

Drzal LT , Mohanty AK , Mehta G. and Misra M. Low cost biobased composite materials for housing application. J Adv Build Technol 2002; 1: 225-235.

14.

John MJ , Francis B. , Varughese KT and Thomas S. Effect of chemical modification on properties of hybrid fiber bio-composite . Composites Part A 2008; 39: 352-363.

15.

Matthews G. PVC: Production, properties and uses. London: Institute of Metal, 1996.

16.

Foldes E. Study on the effects influencing additive migration in polymer. Die Angew Makromol Chem 1998; 261/262: 2133-2170.

17.

Pothan LA , Oommen Z. and Thomas S. Dynamic mechanical analysis of banana fiber reinforced polyester composites . Compos Sci Technol 2003; 63: 283-293.

18.

Ghazanfari A. , Emami S. , Panigrahi S. and Tabil LG Themal and mechanical properties of blends and composites from HDPE and date pits particles. J Compos Mater 2008; 42: 77-89.

19.

Mohanty AK , Misra M. and Dzal LT Sustainable bio composite from renewable resources: opportunity and challenges in the green material world. J Polym Environ 2004; 10(1/2): 19-26.

20.

Ibarra L. , Macias M. and Palma E. Viscoelastic properties of short carbon fiber thermoplastic (SBS) elastomer composites. J Appl Polym Sci 1995; 57: 831-842.

21.

Dong S. and Gauvin R. Application of dynamic mechanical analysis for the study of the interfacial region in carbon fiber/epoxy composite materials. Polym Compos 1993; 14: 414-420.

22.

Ogata N. , Jimenez G. , Kawai H. and Ogihara TJ Structure and thermal/mechanical properties of poly (l-lactide)-clay blend . J Appl Polym Sci 1997; 12: 584-590.