Microstructure and electrical resistivity of carbon/carbon composites prepared by thermal gradient chemical vapor infiltration

Abstract

Carbon/carbon composites were prepared by thermal gradient chemical vapor infiltration with kerosene as precursor. The microstructure and electrical resistivity were examined by polarized light microscopy and low-resistance instrument, respectively. The effects of processing parameters on microstructure as well as the influences of sample density, processing parameters, and needle punch on electrical resistivity of carbon/carbon composites were analyzed. The results show that besides rough laminar, smooth laminar and isotropic pyrocarbon occur at temperatures of 1000°C and 1200°C, respectively. The graphitization degree of composites increases from 16.28% to 63.95% as the heat treatment temperature increases from 2100°C to 2500°C. The electrical resistivity of carbon/carbon composites decreases with increasing heat treatment temperature and sample density but increases as the texture of pyrocarbon varies from rough laminar to smooth laminar. The main mechanism for influencing the electrical resistivity of carbon/carbon composites can be changing carrier concentration, altering grain scattering, or both actions.

Keywords

Carbon/carbon composites chemical vapor infiltration electrical resistivity microstructure pyrocarbon

Get full access to this article

View all access options for this article.

References

Bruneton

Narcy

Oberlin

. Carbon-carbon composites prepared by a rapid densification process І: synthesis and physico-chemical data. Carbon 1997; 35: 1593–1598.

Delhaes

Trinquecoste

Lines

. Chemical vapor infiltration of C/C composites: fast densification processes and matrix characterizations. Carbon 2005; 43: 681–691.

Wang

Qian

Jin

. Microstructure of C/C composites prepared by chemical vapor infiltration method with vaporized kerosene as a precursor. Mater Sci Eng A 2006; 419: 162–167.

Luo

Zhang

. Kinetics of thermal gradient chemical vapor infiltration of large-size carbon/carbon composites with vaporized kerosene. Mater Chem Phys 2009; 113: 616–621.

Luo

Zhang

. Deposition mechanism and microstructure of pyrocarbon prepared by chemical vapor infiltration with kerosene as precursor. Carbon 2009; 47: 1429–1435.

. The production of graphite electrodes. Beijing: Metallurgical Industry Press, 1997, pp. 68–68.

Delhaes

. Chemical vapor deposition and infiltration process of carbon materials. Carbon 2002; 40: 641–657.

Zhang

Huttinger

. Influence of pressure, temperature and surface area/volume ratio on the texture of pyrolytic carbon deposited from methane. Carbon 2003; 41: 749–758.

Blekkan

Myrstad

Olsvik

. Characterization of tars and coke formed during the pyrolysis of methane in a tubular reactor. Carbon 1992; 30: 665–673.

10.

Sherman

Middleman

Jacobs

. Electron transport processes in conductor-filled polymers. Polym Eng Sci 1983; 23: 36–46.

11.

Pierson

Lieberman

. The chemical vapor deposition of carbon on carbon fibers. Carbon 1975; 13: 159–166.

12.

Liang

. New carbon materials. Lanzhou: Institute of Lanzhou Carbon Plant, 1981, p.42.

13.

Zhang

Huang

. Effects of graphitization degree on the electrical conductivity of C/C composites. New Carbon Mater 2001; 16: 45–48.