Three basic mode-II test methods (ENF, JIS, and ASTM D7905M-14) are assessed using the material system AS4/8552 carbon/epoxy unidirectional composite laminate to understand similarities and differences. The modified JIS method uses a PTFE film coated stainless steel rod instead of the PTFE strip that was proposed in JIS. The ASTM D7905M-14 test method determines FEP film crack front (NPC) and shear precrack front (PC) fracture toughnesses. Alternately, wedge precracked specimens were also tested to assess the shear versus opening mode precracking on mode-II fracture toughness. The analysis and test results revealed that the JIS method is a mixed-mode I-II test and result in lower value of mode-II fracture toughness. The GI loading is about 51 J/m2 for the material tested and GIIc measured by JIS is always less than pure mode-II fracture toughness. The GIIc measured from the ASTM D7905M-14 NPC and the ENF tests are almost identical, but the ASTM test offers a compliance equation that may be beneficial in fatigue crack growth studies. As suggested in ASTM standard, shear precracked specimen is appropriate to measure mode-II fracture toughness.
TayTE. Characterization and analysis of delamination fracture in composites: An overview of developments from 1990 to 2001. Appl Mech Rev2003; 56: 1–32.
2.
DaviesPBlackmanBRKBrunnerAJ. Standard test methods for delamination resistance of composite materials: Current status. Appl Compos Mater1998; 5: 345–364.
3.
O’BrienTK. Interlaminar fracture toughness: The long and winding road to standardization. Compos Part B: Eng1998; 29: 57–62.
4.
DaviesPSimsGDBlackmanBRK. Comparison of test configurations for determination of mode II interlaminar fracture toughness results from international collaborative test programme. Plast Rub Compos Pro1999; 28: 432–437.
5.
Russell AJ and Street KN. Moisture and temperature effects on the mixed-mode delamination fracture of unidirectional graphite/epoxy. In: Johnson WS (ed.) Delamination and debonding of materials, ASTM STP 876. West Conshohocken, PA: American Society for Testing and Materials, 1985, pp. 349–370.
6.
ASTM D5528-13:2013. Standard test method for mode I interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites, West Conshohocken, PA: ASTM, 2013.
7.
JIS-K-786:1993. Testing methods for interlaminar fracture toughness of carbon fibre reinforced plastics.
8.
Kageyama K, Klkuchl M and Yanaglsawa N. Stabilized end notched flexure test: characterization of mode II interlaminar crack growth. In: O Brien TK (ed.) Composite materials fatigue and fracture. ASTM STP 1110, Vol. 3. Philadelphia: American Society for Testing and Materials, 1991.
9.
Martin R and Davidson BD. Mode II fracture toughness evaluation using a four point bend end notched flexure test. In: Proceedings of the 4th international conference on deformation and fracture of composites, 1997, pp. 243–252. Institute of Materials.
10.
Davies P, Blackman BRK and Brunner AJ. Mode II delamination. In: Moore DR, Pavan A and Williams JG (eds) Fracture mechanics testing methods for polymers, adhesives and composites. ESIS Publication 28. Oxford: Elsevier, 2001, pp. 307–334.
11.
Crews JH Jr and Reeder JR. A mixed-mode bending apparatus for delamination testing. NASA TM 100662, August 1988.
12.
ASTM D6671/D6671M-13:2013. Standard test method for mixed Mode I-Mode II interlaminar fracture toughness of unidirectional fiber reinforced polymer matrix composites. West Conshohocken, PA: ASTM.
13.
AvvaVSCrewsJHJrShivakumarKN. Modified mixed-mode bending test apparatus for measuring delamination fracture toughness of laminated composites. J Compos Mater1998; 32: 804–828.
14.
AdeyemiNBShivakumarKNAvvaVS. Delamination fracture toughness of woven-fabric composites under mixed-mode loading. AIAA J1998; 37: 517–520.
15.
ASTM D7905/D7905M-14:2014. Standard test method for determination of the Mode II interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites. West Conshohocken, PA: ASTM.
16.
O’Brien TK, Johnston WM and Toland GJ. Mode II interlaminar fracture toughness and fatigue characterization of a graphite epoxy composite material. NASA/TM–2010-216838, August 2010.
17.
CarlssonLAGillespieJWJrPipesRB. On the analysis and design of the end notched flexure (ENF) specimen for mode II testing. J Compos Mater1986; 20: 594–604.
18.
GillespieJWJrCarlssonLAPipesRB. Finite element analysis of the end notched flexure specimen for measuring mode-II fracture toughness. Compos Sci Technol1986; 27: 177–197.
19.
SalpekarSARajuISO'BrienTK. Strain energy release rate analysis of the end-notched flexure specimen using the finite-element method. J Compos Technol Res1988; 10: 133–139.
20.
BrunnerAJBlackmanBRKDaviesPA. Status report on delamination resistance testing of polymer–matrix composites. Eng Fract Mech2008; 75: 2779–2794.
21.
Davies P. ESIS protocols for interlaminar fracture testing of composites. IFREMER brochure, France, 1993.
22.
PerezCLDavidsonBD. Evaluation of precracking methods for the end-notched flexure test. AIAA J2007; 45: 2603–2611.
23.
AECMA Standard:1995. Carbon fibre reinforced plastics test method for the determination of interlaminar fracture toughness energy mode II-GIIC.
24.
Davies P. Summary of results from the second VAMAS mode II round robin test exercise using the 4ENF specimen. IFREMER Report TMSI/RED/MS 99.82, July 1999.
25.
Martin RH, Elms T and Bowron S. Characterization of mode II delamination using the 4ENF test. In: Proceedings of the 4th European conference on composites testing & standardisation, 1998, pp. 161–70.
26.
DavidsonBDSunX. Effects of friction, geometry, and fixture compliance on the perceived toughness from three-and four-point bend end-notched flexure tests. J Reinf Plast Compos2005; 24: 1611–1628.
27.
Hansen P and Martin R. U.S. Army European Research Office Report - Report no. N68171-98 -M-5177, 1998.
28.
Hanna M and Shivakumar KN. Large deformation and nonlinear contact effects in multiple delaminated laminates subjected to transverse loads. In: Proceedings of 37th AIAA/ASME/ASCE/AHS/ASC structures, structural dynamics, and material conference, Utah, USA, 15–17 April 1996, paper no. AIAA-1996-1421.
29.
Shivakumar K, Panduranga R, Miller S, et al. Assessment of mode II fracture tests for fiber reinforced composite laminates. In: Proceedings of the ASC 29th technical conference, La Jolla, California, USA, 8–10 September 2014.