Placeability restricted by in-complete contact between laying roller and mould in an automated fiber placement process

Abstract

In this study, the effect of a roller’s deformability on the placeability restricted by an incomplete contact between a laying roller and mould in an automated fiber placement process was analyzed. The incomplete contact phenomenon was defined theoretically through the differential geometry, and corresponding criteria of placeability were proposed by analyzing the mechanism of interlayer bonding. A finite element model was established to simulate the pressure distribution on the contact zone. The pressure measurement of laying on a curved mould was conducted and the infrared thermographic method was utilized to detect the layup defects. The results of the theoretical analysis showed that the criteria of placeability must satisfy complete contact and pressure’s uniformity simultaneously and be implemented in the condition of laying on a cylinder mould with a fixed angle trajectory. The deformability of the roller with different layup forces relates to its material module and its geometry. The finite element model of pressure distribution was verified by an experiment, and the quantitative relationship between the uniformity of pressure and roller’s module, mould’s radius and tows’ width was acquired by this model. With the increase of module and tows’ width, the uniformity decreases; while with the increase of mould’s radius, the uniformity increases. The thermographic results showed that optimized parameters can guarantee the interlaminar bonding to avoid delamination for laying on the curved mould with a restriction of the incomplete contact.

Keywords

Automated laying technology soft laying roller incomplete contact deformability criteria of placeability uniformity of pressure

Get full access to this article

View all access options for this article.

References

Balakrishnan

John

Pothen

et al.

Natural fibre and polymer matrix composites and their applications in aerospace engineering. Advanced composite materials for aerospace engineering. London: Woodhead Publishing, 2016, pp. 365–383.

Sun

et al . Effect of forming temperature on the quality of hot diaphragm formed C-shaped thermosetting composite laminates J Reinf Plast Comp 2012; 31: 1074–1087.

Hollaway

LC.

The evolution of and the way forward for advanced polymer composites in the civil infrastructure. Constr Build Mater 2003; 17: 365–378.

Chen

Composite technology and large aircraft. Acta Aeronautica Et Astronautica Sinica 2008; 29: 605–610.

Xiong

et al . Mechanical properties of RTM-made composite cross-joints. Chinese J Aeronaut 2009; 22: 211–217.

Thomas

and Nutt

SR.

Temperature dependence of resin flow in a resin film infusion (RFI) process by ultrasound imaging. Appl Compos Mater 2009; 16: 183–196.

Vasiliev

Barynin

and Razin

AF.

Anisogrid composite lattice structures-development and aerospace applications. Compos Struct 2012; 94: 1117–1127.

Chu

Xiao

et al . Modeling and experimental investigation of out-of-plane deformation on mechanical performance of composites manufactured by ATL. J Reinf Plast Comp 2017; 36: 347–359.

Qureshi

Swait

Scaife

et al . In situ consolidation of thermoplastic prepreg tape using automated tape placement technology: potential and possibilities. Compos Part B-Eng 2014; 66: 255–267.

10.

Comer

Ray

Obande

et al . Mechanical characterisation of carbon fibre-PEEK manufactured by laser-assisted automated-tape-placement and autoclave. Compos Part A-Appl S 2015; 69: 10–20.

11.

Rizzolo

and Walczyk

DF.

Ultrasonic consolidation of thermoplastic composite prepreg for automated fiber placement. J Thermoplast Compos 2016; 29: 1480–1497.

12.

Beakou

Cano

Cam

JBL

et al . Modelling slit tape buckling during automated prepreg manufacturing: a local approach. Compos Struct 2011; 93: 2628–2635.

13.

Zhao

Xiao

Huang

et al . Layup quality evaluation of fiber trajectory based on prepreg tow deformability for automated fiber placement. J Reinf Plast Comp 2017; 35: 1576–1585.

14.

Crossley

Schubel

and Warrior

NA.

The experimental determination of prepreg tack and dynamic stiffness. Compos Part A-Appl S 2012; 43: 423–434.

15.

Crossley

Schubel

and Warrior

NA.

Experimental determination and control of prepreg tack for automated manufacture. Plast Rubber Compos 2013; 40: 363–368.

16.

Crossley

Schubel

and Focatiis

DSAD.

Time-temperature equivalence in the tack and dynamic stiffness of polymer prepreg and its application to automated composites manufacturing. Compos Part A-Appl S 2013; 52: 126–133.

17.

Duan

Yan

Chao

et al . Effect of material and shape of compaction roller on the voids and compaction uniformity in fiber placement process. Acta Aeronautica Et Astronautica Sinica 2014; 35: 1173–1180.

18.

Zhang

Sun

Lian

et al . Bonding mechanism of ply during automated tape laying process. Acta Materiae Compositae Sinica 2014; 31: 40–48.

19.

Wang

Research on the prepreg interlaminar tack for automated placement. Nanjing University of Aeronautics and Astronautics, 2015.

20.

Denkena

Schmidt

Völtzer

et al . Thermographic online monitoring system for automated fiber placement processes. Compos Part B-Eng 2016; 97: 239–243.

21.

Chen

Huang

Wang

et al . Typical constitutive models of rubber materials and their ranges of application. Materials Review 2015; 29: 118–120.